纳米氧化钛-乙二醇溶胶溶液的研究

选用了钛酸丁酯、硬脂酸和乙二醇作为表面活性剂，采用表面化学修饰和表面物理修饰2种方法修饰纳米氧化钛，然后分散在乙二醇溶剂中形成溶胶溶液．并通过红外光谱仪、紫外分光计、原子力显微镜，分析了表面化学修饰后的纳米氧化钛表面化学结构的变化，观测了纳米氧化钛溶胶在乙二醇溶剂中稳定性．试验结果表明表面活性剂与纳米氧化钛的表面的不饱和键之间形成了新的化学结构，粒子表面可能接枝上有机长链，提高了纳米粒子在溶剂中的相容性．表面化学修饰后的纳米氧化钛与乙二醇溶剂形成了较稳定的溶胶体系，而且纳米溶胶粒径较小．表面活性剂添加量与纳米粒子添加量控制在(1～1．2)：1时，可以获得纳米溶胶粒径较小，同时溶胶稳定性较好的纳米氧化钛-乙二醇溶胶体系．     

Atomic-scale simulation of nano-grains:structure and diffusion properties

Nanograins are characterized by a typical grain size from lto 100 nm.Mclecular dynamics aimubations have been carried out for the nanograin sphere with the diameters from 1.45 to 10.12 nm.We study the influence of grain size on structure and diffusion properties of the nanograins.The results reveal that as the grain size is reduced,the fraction of grain surface increases significantly,and the surface width is approximately constant；the diffusicn coefficlent is increased sharply,and the relation of the diffusion coefficient and the grain size is close to exponential relation below 10nm.     

纳米Zr-V-O粉末的XRD及TG-DSC研究

利用机械合金化制备纳米Zr-V粉末，对制备过程的材料进行物相分析和热分析试验。初始粉末Zr（150μm）和V（150μm）元素粉末（纯度99．15％）按原子比1：2或1：1进行混合后在氩气气氛中放入SimoloyerCMol—2球磨仓中，按几种不同的试验条件进行球磨。同时在997K和1047K下热处理40min和1h，并对热处理前后的粉末进行了物相和TG-DSC实验分析。     

Raman properties embeddedof GaSb nanoparticlesin SiO2 films

The Raman shifts of nanocrystalline GaSb excited by an Ar^ ion laser at wavelengths 514.5, 496.5, 488.0, 476.5,and 457.9nm are studied by an SPEX-1403 laser Raman spectrometer respectively, and they are explained by phonon confinement, tensile stress, resonant Raman scattering and quantum size effects. The Stokes and anti-Stokes Raman spectra of GaSb nanocrystals strongly support the Raman feature of GaSb nanocrystals. The calculated optical spectra compare well with experimental data on Raman scattering GaSb nanocrystals.     

袁家骝和他的科学贡献

1 生平 美籍华人、世界著名高能物理学家袁家骝先生,于2003年2月11日下午在北京协和医院逝世,享年91岁[1].     

双维位置灵敏CsI(Tl)探测器

描述了一种双维位置灵敏CsI(Tl)探测器.用3组分α源测量该探测器得到的位置分辨为0.81mm(FWHM),对于69MeV/u ³⁶Ar能量分辨为0.9％(FWHM).在RIBLL的ΔE-E粒子鉴别望远镜中常常作为E探测器.由于CsI(Tl)晶体对不同的粒子的能损-光输出的非线性,需要针对不同离子对CsI探测器作能量-光输出校正曲线.     

有限温度下的K介子凝聚

我们把Brown等讨论在零温时K介子凝聚的工作推广到有限温度.结果表明温度对于原子核的临界密度影响不大,新物质相有可能在重离子反应中形成.     

Spectral property and its shape transition on ^72-84Kr isotopes in microscopic core plus two-quasiparticle approach

By using a microscopic sdIBM-2 2q.p, approach, the levels of the ground-band, 7-band and partial two-quasi-particle bands for ^72-84Kr isotopes are calculated. The data obtained are in good agreement with the recent experimental results, and successfully reproduce the nuclear shape phase transition of ^72-S4Kr isotopes at zero temperature.The ground-state band is described successfully up to J^π=18^ and Ex=10.0MeV. Based on this model, the aligned requisite minimum energy has been deduced. The theoretical calculations indicate that no distinct change of nuclear states is caused by the abruptly broken pair of a boson, and predict that the first backbending of Kr isotopes may be the result of aligning of two quasi-neutrons in orbit g9/2, which galus the new experimental support of the measurements of g factors in the ^78-86Kr isotopes.     

一种有机电致发光共聚物的制备和性能

采用Suzuki方法合成了9，9-二辛基芴与萘并硒二唑的两种无规共聚物并研究了其紫外光谱、光致发光和电致发光性能。两种聚合物的电致发光波长为650～666nm，均为发饱和红光的LED材料，其电致发光外量子效率最高达到了1．05％。随着共聚物中萘并硒二唑含量的增加，共聚物的光致发光和电致发光的发射波长均有少量红移。证明了根据共轭高聚物链内能量转移原理，在聚芴链中引入不同含量的窄带隙杂环单元可实现对聚芴发光颜色的调节。     

Nano-tribological study on a super-hydrophobic film formed on rough aluminium substrates

A novel super-hydrophobic stearic acid (STA) film with a water contact angle of 166^o was prepared by chemical adsorption on aluminum wafer coated with polyethyleneimine (PEI) film. The micro-tribological behavior of the super-hydrophobic STA monolayer was compared with that of the polished and PEI-coated Al surfaces. The effect of relative humidity on the adhesion and friction was investigated as well. It was found that the STA monolayer showed decreased friction, while the adhesive force was greatly decreased by increasing the surface roughness of the Al wafer to reduce the contact area between the atomic force microscope (AFM) tip and the sample surface to be tested. Thus the friction and adhesion of the Al wafer was effectively decreased by generating the STA monolayer, which indicated that it could be feasible and rational to prepare a surface with good adhesion resistance and lubricity by properly controlling the surface morphology and the chemical composition. Both the adhesion and friction decreased as the relative humidity was lowered from 65% to 10%, though the decrease extent became insignificant for the STA monolayer. The project supported by the National Natural Science Foundation of China (50375151, 50323007, 10225209) and the Chinese Academy of Sciences (KJCX-SW-L2)