层状钙钛矿La1.3Sr1.7Mn2-xCuxO7的磁性及电特性

通过固相反应烧结法成功制备了层状钙钛矿La1.3Sr1.7Mn2-xCuxO7多晶,主要研究了其磁电特性.结果表明,样品为Sr3Ti2O7型钙钛矿结构.随着温度的降低,其磁性经历了一个很复杂的转变过程.当x=0时,在T*=231 K出现二维短程铁磁有序,在Tc=114 K出现三维长程铁磁有序,在TN=56 K出现倾斜的反铁磁转变.当x=0.05时,Cu替代使得T*,Tc和TN减小.其电特性表明,La1.3Sr1.7Mn2-xCuxO7多晶呈现出双峰现象,这是由于钙钛矿结构锰氧化物共生现象造成的.虽然5%Cu替代,降低了金属一绝缘体转变温度,但是却增强了磁电阻效应.     

Green and red up-conversion emissions and thermometric application of Er^3＋-doped silicate glass

The green and red up-conversion emissions centred at about 534, 549 and 663 nm of wavelength, corresponding respectively to the ^2H11/2 → ^4I15/2, ^4S3/2 → ^4I15/2 and ^4F9/2 → ^4I15/2 transitions of Er^3＋ ions, have been observed for the Er^3＋-doped silicate glass excited by a 978 nm semiconductor laser beam. Excitation power dependent behaviour of the up-conversion emission intensity indicates that a two-photon absorption up-conversion process is responsible for the green and red up-conversion emissions. The temperature dependence of the green up-conversion emissions is also studied in a temperature range of 296-673 K, which shows that Er^3＋-doped silicate glass can be used as a sensor in high-temperature measurement.     

通过超宽139La固体核磁共振波谱研究层状La(OH)2NO3

层状稀土氢氧化物是一类新型的稀土功能材料,本文采用固体核磁共振（SSNMR）方法研究了同时具备离子交换能力和非线性光学特性的层状La（OH）₂NO₃化合物,探讨了通过四极核CPMG（QCPMG）脉冲序列和变频谱图采集获取超宽¹³⁹La SSNMR谱图的方法,并描述了适用于此类实验的滤波方程和谱图重建方法.重建谱图同时包含四极核中心跃迁和卫星跃迁信息,本文使用QUEST软件对超宽¹³⁹La NMR谱图进行了模拟,获取的四极耦合常数C_Q和非对称因子η_Q均与CASTEP密度泛函理论计算值高度吻合.SSNMR实验结果证实层状La（OH）₂NO₃化合物属于非中心对称结构（P2₁）,解决了对其结构长期以来存在的争论.     

含水玻璃夹层状硅酸盐的合成与XRD表征

120℃时膨润土、高岭土分别用水玻璃固化，固化物晶形仍以蒙脱石、高岭石结构为主，且蒙脱石可包含更多的水玻璃成分，其固化机理为水玻璃加强了这些硅酸盐的层间作用力，讨论了新型夹层物质形成的可能。     

基于PdSe2/GaAs异质结的高灵敏近红外光伏型探测器的制备和图像传感的应用

本文制备了一种基于PdSe₂/GaAs异质结的高灵敏近红外光电探测器,该探测器是通过将多层PdSe₂薄膜转移到平面GaAs上制成的. 所制备的PdSe₂/GaAs异质结器件在808 nm光照下表现出明显的光伏特性,这表明近红外光电探测器可以用作自驱动器件. 进一步的器件分析表明,这种杂化异质结在零偏电压和808 nm光照下具有1.16×10⁵的高开关比. 光电探测器的响应度和比探测度分别约为171.34 mA/W和2.36×10¹¹ Jones. 而且,该器件显示出优异的稳定性和可靠的重复性. 在空气中2个月后,近红外光电探测器的光电特性几乎没有下降,这归因于PdSe₂的良好稳定性. 最后,基于PdSe₂/GaAs的异质结器件还可以用作近红外光传感器.     

基于层状模型的功能梯度板中兰姆波传播研究

功能梯度板中的兰姆波的传播在实际工程中有着非常广泛的应用。采用层状模型研究了兰姆波在材料特性沿厚度方向连续变化的功能梯度板中的传播特性。通过数值计算获得了层状板中兰姆波的色散关系,并与已有结果进行了比较,获得了材料属性沿厚度方向呈指数变化和多项式变化时功能梯度板中兰姆波的波速和位移解。当材料属性连续变化时,兰姆波各阶模态的波速与位移都将发生变化。相比于兰姆波的高阶模态,低阶模态的波速变化更加明显。本文的研究可为功能梯度板的设计提供参考。     

Spectroscopic properties of thulium ions in bismuth silicate glass

A new type of bismuth silicate glass (Bi2O3-SiO2-ZnO-Al2O3-La2O3) doped with Tm2O3 is prepared by melt-quenching method. The thermal stability of the glass is examined by differential scanning calorimetry. No crystallization peak is found. Using the absorption and emission spectra, the absorption and emission cross-sections are calculated. Their maximum data are 2.9×10-21cm2 at 1663 nm and 4.7×10-21cm2 at 1826 nm, respectively. Using the Judd-Ofelt theory, the radiation transition probabilities and radiative lifetimes are obtained. The extended overlap integral method is applied to analyze energy transfer process among the Tm3+ ions. The transfer constants of cross-relaxation and energy migration among the Tm3+ ions at the 3H4 level are 7.60×10-40 and 14.98×10-40 cm6 /s, respectively. The critical transfer radius for cross-relaxation is 0.99 nm. The cross relaxation process is easy to realize and is favorable for obtaining ～2-μm laser.     

偏铝酸锂/环化聚丙烯腈共包覆改性高镍层状正极材料的制备

构建表面无机-有机复合包覆层,用于改善高镍层状(NCM811)正极材料结构和界面不稳定问题。复合包覆层由纳米偏铝酸锂(LiAlO₂,LAO)和环化聚丙烯腈(cPAN)构成。该复合包覆层中LAO是一种典型的锂离子导体,可提供Li⁺迁移通道;PAN环化后,可产生离域的π键,形成具有电子导电性的cPAN。材料表面复合包覆层的结构及成分研究表明,该复合包覆层均匀分布在 NCM811 材料表面。半电池测试结果表明,在 2.7~4.3 V(vs Li/Li⁺)电压范围内,在 180 mA·g^-1电流密度下,改性后的NCM811材料循环150周后容量保持率为84.8%。而同样条件下,原始NCM811材料容量保持率为65.5%。该复合包覆层可有效提升NCM811结构和界面稳定性,减少电解液分解,降低界面阻抗。     

层状复合氧化物La4BaCu5-xMxO13+λ的制备、表征及对CO还原NO的活性

 采用柠檬酸爆炸法合成了系列层状钙钛矿型复合氧化物La4BaCu5-xMxO13+λ(M=Mn, Co; x=0~5)催化剂. 用TPD, TPR和化学分析法对催化剂进行了表征,考察了催化剂在CO还原NO中的催化活性.结果表明,掺杂Mn, Co后催化剂中的活性氧含量及氧化还原性质发生了变化. 掺杂少量Mn, Co可使催化剂在CO还原NO中的催化活性明显提高,且掺杂Co的样品比掺杂Mn的样品活性提高更明显.这是由于Cu-Mn与Cu-Co之间的协同作用不同导致的结果.     

Eu2+/Sm3+掺杂硅酸盐玻璃发光特性研究

制备了一种新型的Eu2+/Sm3+共掺硅酸盐玻璃,研究了Eu2+/Sm3+共掺硅酸盐玻璃的热稳定性能和发光特性。研究发现,在近紫外光360 nm激发下,在室温下同时观察到明显的蓝绿光(475 nm)、黄光(562 nm)、橙光(599 nm)和红光(644 nm和706 nm)发光。其中蓝绿光(475 nm)是由于Eu2+的4f65d1→4f7辐射跃迁,黄光(562 nm)是由于Sm3+的4G5/2→6H5/2辐射跃迁,橙光(599 nm)是由于Sm3+的4G5/2→6H7/2辐射跃迁,红光(644 nm和706 nm)是由于Sm3+的4G5/2→6H9/2和4G5/2→6H11/2辐射跃迁。随着Sm3+离子浓度的增加,Eu2+/Sm3+共掺硅酸盐玻璃的色度从蓝绿光区域逐渐向白光区域移动。当Eu2+,Sm3+掺杂摩尔分数分别为0.05%和1.0%时,硅酸盐玻璃的色坐标为(0.312,0.307),接近纯白色点的色坐标(0.333,0.333)。研究结果表明,Eu2+/Sm3+掺杂硅酸盐玻璃是一种潜在的白光LED基质材料。