Embedding copper nanoparticle-anchored conductive nano-blocks in polyelectrolyte

Conductive carbon nanotubes （CNTs） or alternatively polyaniline （PANI） nano-blocks was introduced into aqueous solutions of polyvinyl alcohol （PVA） and copper （II） salt, to assist the reduction of copper （II） ions and the anchoring of the resulting copper nanoparticles onto the conductive blocks. The mixture solutions of nano-blocks, copper （lI） salts and PVA were spin-coated onto the cathode surface, forming swollen cathode films （SCFs）. The copper （II） ions in the film assembled onto the surfaces of the conductive blocks and were then reduced under an appropriate voltage. It is important that the copper nanoparticles grew only on the surfaces of the conductive blocks. PVA which acted as the matrix of the composites played a role in stabilizing the resulting copper nanoparticles. Morphologies of these polymeric composite films were studied by various characterization methods. Moreover, the mechanism of migration of copper （II） ions, the formation of these polymeric composites, and the overall procedure were investigated in detail.     

贮存条件对纤维素/大豆蛋白膜结构与性能的影响

通过流延成膜法制备一系列纤维素/大豆分离蛋白复合膜材料,分别以10%醋酸溶液、5%醋酸和5%乙醇的混合溶液、75%乙醇溶液等3种水溶液及蒸馏水为贮存体系,通过力学性能测试、扫描电镜观察、紫外测试等方法研究了不同贮存条件对纤维素/大豆分离蛋白复合膜结构与性能的影响.结果表明,10%醋酸水溶液贮存纤维素/大豆分离蛋白复合膜30d能够较好地维持其力学性能和微观结构,可作为该复合膜较为适合的贮存体系.     

Passively Q-Switched EDFL Using a Multi-Walled Carbon Nanotube Polymer Composite Based on a Saturable Absorber

A stable passive Q-switched erbium-doped fiber laser （EDFL） operating at 1563.5 nm is demonstrated by using a multi-walled carbon nanotube （MWCNT） polymer composite film based saturable absorber for the first time. The composite is prepared by mixing the MWCNTs homogeneous solution into a dilute PEO polymer solution before it is left to dry at room temperature to produce thin film. Then the film is sandwiched between two FC/PC fiber connectors and is integrated into the laser cavity for Q-switching pulse generation. The EDFL generates a stable pulse train with repetition rates ranging from 4.5 kHz to 20.0 kHz by varying the 1480 nm pump power from 35 mW to 53 mW. At the 53 mW pump power, the pulse width and pulse energy are 8.8 μs and 15.3 nJ, respectively.     

DMFCs用磺化聚醚醚酮/功能化二氧化硅复合质子交换膜

在磺化度(DS)为55.1%的磺化聚醚醚酮(SPEEK)中掺杂功能化二氧化硅(吸湿性SiO2溶胶及带有磺酸基团的二氧化硅(SiOx-S)粒子)制备SPEEK/SiO2和SPEEK/SiOx-S复合质子交换膜.SiO2和SiOx-S的掺杂能有效提高复合膜的抗溶胀、阻醇性能及高温低湿情况下的电导率.纯SPEEK膜在80℃溶胀为52.6%,而SiO2和SiOx-S掺杂量为15%的复合膜在此温度下分别仅有26.2%和27.3%的溶胀.在室温至80℃范围内,SPEEK/SiO2(20 wt%)和SPEEK/SiOx-S(20 wt%)复合膜的甲醇透过系数比Nafion115膜小近2个数量级.在120℃、相对湿度(RH)为40%情况下,SPEEK纯膜的电导率仅为2.6×10-4S.cm-1,SPEEK/SiO2(20 wt%)复合膜约为2.0×10-3S.cm-1,而SPEEK/SiOx-S(20 wt%)复合膜高达1.0×10-2S.cm-1,与Nafion115相当.SPEEK/SiO2(20 wt%)和SPEEK/SiOx-S(20 wt%)2种复合膜的尺寸稳定性较高,膜电极无催化剂与膜分离现象,其DMFCs单电池性能好于SPEEK膜.     

含氨基聚芳醚酮/磺化聚芳醚酮砜中高温质子交换复合膜的制备与性能研究

以自制的高磺化度磺化聚芳醚酮砜(SPAEKS)和含有氨基的聚芳醚酮(Am-PAEK)为原料,通过共溶剂涂膜法制备了不同重量比例的Am-PAEK/SPAEKS复合膜.通过高温(160℃)处理使氨基和磺酸基团在复合膜内形成交联,制得交联型复合膜.复合膜的热性能、尺寸稳定性、阻醇性能有所提高,而且交联型复合膜中的Am-PAEK/SPAEKS-C-3质子传导率在120℃时达到了0.0892 S/cm,高于在相同测试条件下SPAEKS膜的0.0654 S/cm和Nafion膜的0.062 S/cm,而其甲醇渗透系数在25℃时达到0.14×10-6cm2/s,低于SPAEKS膜的0.85×10-6cm2/s和Nafion膜的2×10-6cm2/s.实验结果表明,Am-PAEK/SPAEKS交联型复合膜有望在中高温质子交换膜燃料电池中得到应用.     

聚硅氧烷/液晶复合膜的制备及其血液相容性研究

以含氢硅油和乙烯基硅油为基质,在氯铂酸催化下与胆甾醇油烯基碳酸酯液晶共混交联成一定强度的聚硅氧烷／液晶复合膜。借助偏光显微撞观察了不同液日含量在材料表面的状态,通过动态凝血实验、血小板粘附与变形实验、溶血实验等研究材料表面形态与血液相容性的关系。结果表明,含液晶２０％、３０％的液晶膜具有优良的抗凝血性能。     

具有界面交联结构藻酸钠复合膜的制备与性能

报道了一种具有界面交联结构的新型藻酸钠复合膜及其对醇水和其它有机物水体系的渗透汽化分离性能.该膜的活性层为藻酸钠,支撑层为氨化聚丙烯腈(PAN)多孔膜,在这两层之间存在着界面交联结构.研究了PAN多孔膜的水解时间、进行氨基化的二元胺种类及浓度对复合膜分离性能的影响,用己二胺进行氨基化所得到的复合膜的分离性能明显优于用乙二胺的结果.扫描电镜照片显示水解及氨基化改变了PAN超滤膜的孔结构,这也是影响新型复合膜性能的一个重要原因.     

磷酸掺杂的聚苯并咪唑复合膜在高温质子交换膜燃料电池中的应用

磷酸掺杂的聚苯并咪唑复合膜在高温质子交换膜燃料电池中的应用     

电铸自支撑金刚石-镍复合膜的制备

用电铸方法,采用低应力电镀液,制备出了自支撑金刚石-镍复合膜.电镀液PH值3.8-4.2,温度40～60℃,阳极与阴极间距100～150mm.用扫描电镜(SEM)和X射线衍射(XRD)方法检测了复合膜的表面形貌、晶体显微结构和复合膜中金刚石颗粒的分布情况.结果表明:阴极电流密度对自支撑金刚石-镍复合膜的品质影响很大,当阴极电流密度从1.3 A/dm2增加到3.3 A/dm2时,复合膜的显微应变从0.36;减小到0.28;;随着阴极电流密度的增加,复合膜中金刚石颗粒的含量增加.     

孔梯度陶瓷纤维复合膜管的制备及特性

陶瓷过滤管具有孔隙率高、耐腐蚀、耐高温、机械强度高、便于清洗、使用寿命长等优点,是高温烟尘处理用的高效过滤元件.本文研制了一种具有梯度孔结构堇青石陶瓷纤维复合膜过滤元件,该过滤元件是由多孔支撑体、过渡层和分离膜层组成.其中支撑体、过渡层和分离层的气孔率分别为35～40;、50～60;和60～70;.文中主要分析了孔梯度陶瓷纤维复合膜管的材料结构和抗热震性能,同时对复合膜管进行含尘气体过滤的冷态模拟试验.对于烟气中粒径大于或等于0.1μm的颗粒,复合膜管的截留率达到99.8;以上.