Zn(BTZ)2白色有机电致发光材料的合成及其器件制备

以PCl₃为脱水剂,将邻氨基硫酚与水杨酸脱水环化合成出2-(2-羟基苯基)苯并噻唑,并进一步将所得产物与乙酸锌反应合成出2-(2-羟基苯基)苯并噻唑螯合锌(Zn(BTZ)₂)材料。以该配合物作为发光层制备出结构为ITO/PVK:TPD/Zn(BTZ)₂/Al近白色电致发光器件,其色坐标位于白场之内(x=0.242,y=0.359),在驱动电压为16V时,亮度达3200cdm²,对应的量子效率为0.32%。进一步在Zn(BTZ)₂中掺入橙红色染料Rubrene,制成ITO/PVK:TPD/Zn(BTZ)₂:Rubrene/Al结构器件,实现了纯白色发光(色坐标值:x=0.324,y=0.343),非常接近于白色等能点,且量子效率达0.47%。最后对上述器件的发光和电学性能进行了深入的研究和探讨。     

Second-order Nonlinear Optical Properties of a Series of Azulene Derivatives

The first hyperpolarizabilities of a series of novel azulenic-barbituric acid chromophores have been studied by using 12 excitation wavelengths, ranging from 900 to 1907 nm. The dispersion relation of the first hyperpolarizabilities of chromophores holds the same tendency as the experimental results. In addition, the static first hyperpolarizability β0 of molecules was calculated by means of the Sum-Over-States (SOS) expression and the two-level formula respectively. The results show that these molecules possess large static first hyperpolarizabilities and the, β0 value increases as the donor or acceptor strength enhances; the distorted degree of molecules has also an important influence on the β0 value.     

Novel Chiral Ferrocenyl Aziridino Alcohol Catalysts Promoting Asymmetric Addition of Diethylzinc to Aldehydes

Optically active aziridino alcohols containing ferrocenyl groups were prepared from commercially available L-threonine in excellent yields and used as catalysts to promote the asymmetric addition of diethylzinc to aryaldehydes to afford 1-arylpropanol in up to 84% enantiomeric excesses with moderate to good yields.     

铬（Ⅵ）—DBC—HNO3催化动力学光度法测定痕量铬（Ⅵ）

在硝酸介质中，痕量铬(Ⅵ)能灵敏的催化氧化DBC褪色。研究了反应的最佳条件，建立了测定痕量铬(Ⅵ)的新方法。检出限可达10^-9g／ml，测定范围为0．12--0．7μgCrC(Ⅵ)／10ml，方法简便、灵敏、快速、准确。用于测定水中的痕量铬(Ⅵ)，获得了满意的结果。     

支气管灌洗液中铜锌含量及铜／锌比值的观察

用原子吸收光谱法检测了肺癌患者灌洗液中铜、锌含量及铜／锌比值。结果表明：中央型肺癌组与肺部良性疾病组比较均有极显著差异；与周围型比较，铜、铜／锌具有显著性差异；而周围型肺癌组与良性组比较，除铜／锌比值有显著性差异，Ｃｕ、Ｚｎ均无统计学意义差异。     

乌洛托品法测定钢铁热浸镀锌量

钢铁热浸镀锌量的测定在GB及世界各国标准里均采用三氯化锑法。因其产生SbH_3有毒气体而被甲醛或乌洛托品代替锑剂。ZBH11001-88采用甲醛,GB/T13825-92及ISO1460-1992(E)均采用乌洛托品。本文对乌洛托品方法进行试验并与三氯化锑法、ZBH11001-88法加以研究比较。 1 试验部分 1.1 主要试剂 乌洛托品(六次甲基四胺,分析纯,含甲醛97％以上) 乌洛托品盐酸退镀溶液,称取乌洛托品3.5g溶于盐酸(1+1)1L中。 1.2 测定步骤 将热浸镀锌钢铁试样制备成可测面积的样品,以无水乙醇及乙醚清除表面油污,烘干冷至室温于万分之一天平上称准至毫克。置于盛有乌洛托品退镀溶液的器皿中,保持样品每平方厘米表面上有10ml以上的     

Effects of Substrate Temperature on Helium Content and Microstructure of Nanocrystalline Titanium Films

Helium-charged nanocrystalline titanium films have been deposited by HeAr magnetron co-sputtering. The effects of substrate temperature on the helium content and microstructure of the nanocrystalline titanium films have been studied. The results indicate that helium atoms with a high concentration are evenly incorporated in the deposited titanium films. When the substrate temperature increases from 60℃ to 350℃ while the other deposition＇parameters are fixed, the helium content decreases gradually from 38.6 at.% to 9.2at.%, which proves that nanocrystalline Ti films have a great helium storage capacity. The 20 angle of the Bragg peak of （002） crystal planes of the He-charged Ti film shifts to a lower angle and that of （100） crystal plane is unchanged as compared with that of the pure Ti film, which indicates that the lattice parameter c increases and a keeps at the primitive value. The grain refining and helium damage result in the diffraction peak broadening.     

Si衬底上ZnSe外延膜的低压MOCVD生长

以硒化氢（H2Se）和二甲基锌为源材料，生长温度是300℃时，用低压金属有机化学气相沉积（LP－MOCVD）系统在Si(111)衬底上外延生长了ZnSe薄膜。通过X射线衍射（XRD）、扫描电子显微镜的能量色散（EDS）以及光致发光（PL）实验验证ZnSe外延膜的质量，在X射线衍射谱中只有一个强的ZnSe(111)面衍射峰，这说明外延膜是（111）取向的单晶薄膜，在能量色散谱中除了Si,Zn和Se原子外，没有观测到其他原子，说明ZnSe外延膜中杂质含量较少。ZnSe外延膜中Zn/Se原子比接近1，有较好的化学配比。在ZnSe外延膜的77K光致发光谱中没有观测到与深中心发射相关的发光峰，表明ZnSe外延膜的晶格缺陷密度较小。77K时的近带边发射峰447nm在室温时移至465nm附近。     

ICP-AES测定饮用水源中的Cu、Mn、Pb、Cd、Zn

用ICP－AES法同时测定饮用水源中的Cu、Mn、Pb、Cd、Zn等重金属元素，具有基体效应小、测量范围宽等优点。检出限为0．2－4．0μg/L，回收率为91．5％－103．9％，相对标准偏差为0．29％－1．5％，测定密码样与实际样品，结果令人满意。