A novel tridentate nitrogen donor as ligand in copper catalyzed ATRP of methyl methacrylate

A tridentate ligand, BPIEP: 2,6‐bis[1‐(2,6‐diisopropyl phenylimino) ethyl] pyridine, having central pyridine unit and two peripheral imine coordination sites was effectively employed in controlled/“living” radical polymerization of MMA at 90°C in toluene as solvent, Cu^IBr as catalyst, and ethyl‐2‐bromoisobutyrate (EBiB) as initiator resulting in well‐defined polymers with polydispersities M_w/M_n ≤ 1.23. The rate of polymerization follows first‐order kinetics, k_app = 3.4 × 10^?5 s^?1, indicating the presence of low radical concentration ([P*] ≤ 10^?8) throughout the reaction. The polymerization rate attains a maximum at a ligand‐to‐metal ratio of 2:1 in toluene at 90°C. The solvent concentration (v/v, with respect to monomer) has a significant effect on the polymerization kinetics. The polymerization is faster in polar solvents like, diphenylether, and anisole, as compared to toluene. Increasing the monomer concentration in toluene resulted in a better control of polymerization. The molecular weights (M_n,SEC) increased linearly with conversion and were found to be higher than predicted molecular (M_n,Cal). However, the polydispersity remained narrow, i.e., ≤1.23. The initiator efficiency at lower monomer concentration approaches a value of 0.7 in 110 min as compared to 0.5 in 330 min at higher monomer concentration. The aging of the copper salt complexed with BPIEP had a beneficial effect and resulted in polymers with narrow polydispersitities and higher conversion. PMMA obtained at room temperature in toluene (33%, v/v) gave PDI of 1.22 (M_n = 8500) in 48 h whereas, at 50°C the PDI is 1.18 (M_n = 10,300), which is achieved in 23 h. The plot of lnk_app versus 1/T gave an apparent activation energy of polymerization as (ΔE^≠_app) 58.29 KJ/mol and enthalpy of equilibrium (ΔH⁰_eq) to 28.8 KJ/mol. Reverse ATRP of MMA was successfully performed using AIBN in bulk as well as solution. The controlled nature of the polymerization reaction was established through kinetic studies and chain extension experiments. © 2005 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 43: 4996–5008, 2005     

A model study for the steady state error of numerical approximations of inviscid flow equations on Cartesian grid

The widely used locally adaptive Cartesian grid methods involve a series of abruptly refined interfaces. In this paper we consider the influence of the refined interfaces on the steady state errors for second‐order three‐point difference approximations of flow equations. Since the various characteristic components of the Euler equations should behave similarly on such grids with regard to refinement‐induced errors, it is sufficient enough to conduct the analysis on a scalar model problem. The error we consider is a global error, different to local truncation error, and reflects the interaction between multiple interfaces. The steady state error will be compared to the errors on smooth refinement grids and on uniform grids. The conclusion seems to support the numerical findings of Yamaleev and Carpenter (J. Comput. Phys. 2002; 181: 280–316) that refinement does not necessarily reduce the numerical error. Copyright © 2005 John Wiley & Sons, Ltd.     

Synthesis and characterization of a polyfluorene containing carbazole and oxadiazole dipolar pendent groups and its application to electroluminescent devices

We have synthesized a blue‐light‐emitting polyfluorene (PF) derivative ( PF‐CBZ‐OXD ) that presents bulky hole‐transporting carbazole and electron‐transporting oxadiazole pendent groups functionalized at the C‐9 positions of alternating fluorene units. The results from photoluminescence and electrochemical measurements indicate that both the side chains and the PF main chain retain their own electronic characteristics in the copolymer. An electroluminescent device incorporating this polymer as the emitting layer was turned on at 4.5 V; it exhibited a stable blue emission with a maximum external quantum efficiency of 1.1%. Moreover, we doped PF‐CBZ‐OXD and its analogue PF‐TPA‐OXD with a red‐light‐emitting iridium phosphor for use as components of phosphorescent red‐light emitters to investigate the effect of the host's HOMO energy level on the degree of charge trapping and on the electrophosphorescent efficiency. We found that spectral overlap and individual energy level matching between the host and guest were both crucial features affecting the performance of the electroluminescence devices. Atomic force microscopy measurements indicated that the dipolar nature of PF‐CBZ‐OXD , in contrast to the general nonpolarity of polydialkylfluorenes, provided a stabilizing environment that allowed homogeneous dispersion of the polar iridium triplet dopant. © 2007 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 45: 2925–2937, 2007     

Numerical approximation of generalized Newtonian fluids using Powell–Sabin–Heindl elements: I. theoretical estimates

In this paper we consider the numerical approximation of steady and unsteady generalized Newtonian fluid flows using divergence free finite elements generated by the Powell–Sabin–Heindl elements. We derive a priori and a posteriori finite element error estimates and prove convergence of the method of successive approximations for the steady flow case. A priori error estimates of unsteady flows are also considered. These results provide a theoretical foundation and supporting numerical studies are to be provided in Part II. Copyright © 2003 John Wiley & Sons, Ltd.     

Sulfobetaine‐containing diblock and triblock copolymers via reversible addition‐fragmentation chain transfer polymerization in aqueous media

A novel bifunctional acrylamido‐based reversible addition–fragmentation chain transfer (RAFT) chain‐transfer agent (CTA), N,N′‐ethylenebis[2‐(thiobenzoylthio)propionamide] (CTA2), has been synthesized and used for the controlled free‐radical polymerization of N,N‐dimethylacrylamide (DMA). A comparative study of CTA2 and the monofunctional CTA N,N‐dimethyl‐s‐thiobenzoylthiopropionamide (CTA1) has been conducted. Polymerizations mediated by CTA1 result in poly(N,N‐dimethylacrylamide) (PDMA) homopolymers with unimodal molecular weight distributions, whereas CTA2 yields unimodal, bimodal, and trimodal distributions according to the extent of conversion. The multimodal nature of the PDMAs has been attributed to termination events and/or chains initiated by primary radicals. The RAFT polymerization of DMA with CTA2 also results in a prolonged induction period that may be attributed to the higher local concentration of dithioester functionalities early in the polymerization. A series of ω‐ and α,ω‐dithioester‐capped PDMAs have been prepared in organic media and subsequently employed as macro‐CTAs for the synthesis of diblock and triblock copolymers in aqueous media with the zwitterionic monomer 3‐[2‐(N‐methylacrylamido)‐ethyldimethylammonio] propane sulfonate (MAEDAPS). Additionally, an ω‐dithioester‐capped MAEDAPS homopolymer has been used as a macro‐CTA for the block polymerization of DMA. To our knowledge, this is the first example of a near‐monodisperse, sulfobetaine‐containing block copolymer prepared entirely in aqueous media. The diblock and triblock copolymers form aggregates in pure water that can be dissociated by the addition of salt, as determined by ¹H NMR spectroscopy and dynamic light scattering. In pure water, highly uniform, micellelike aggregates with hydrodynamic diameters of 71–93 nm are formed. © 2003 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 41: 1262–1281, 2003     

A remark on divisibility of definable groups

We show that if G is a definably compact, definably connected definable group defined in an arbitrary o‐minimal structure, then G is divisible. Furthermore, if G is defined in an o‐minimal expansion of a field, k ∈ ? and p_k : G → G is the definable map given by p_k (x ) = x^k for all x ∈ G , then we have |(p_k )^–1(x )| ≥ k^r for all x ∈ G , where r > 0 is the maximal dimension of abelian definable subgroups of G . (© 2005 WILEY‐VCH Verlag GmbH & Co. KGaA, Weinheim)     

Synthesis and refractive‐index control of fluoropolymers by the polyaddition of bis(epoxide)s and triazine di(aryl ether)s

The polyaddition of fluorine‐containing bis(epoxide)s and fluorine‐containing triazine di(aryl ether)s were examined to give the corresponding fluorine‐containing poly(cyanurate)s. It was observed that the synthesized fluoropolymers had good thermal stabilities and good film‐forming properties. The glass transition temperatures (T_g's) and refractive‐indices (n_D's) of synthesized polymers were determined by differential scanning calorimetry and ellipsometry, respectively, and it was found that the values of T_g's and n_D's were supported by their fluorine containing ratios and skeletons. © 2007 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 45: 4421–4429, 2007     

Ultrasonic spectroscopic evaluation of the ring‐opening metathesis polymerization of dicyclopentadiene

An in situ ultrasonic spectroscopy technique was used to study the ring‐opening metathesis polymerization of dicyclopentadiene catalyzed by bis(tricyclohexylphosphine)benzylidene ruthenium dichloride. A reaction cell employing a flexible poly(ethylene terephthalate) window for pulse echo ultrasonic spectroscopy was used to monitor the polymerization. The changes in the density, wave speed, acoustic modulus, and attenuation were all simultaneously monitored. In comparison with Fourier transform infrared (FTIR) spectroscopy data, the changes in the density, velocity, and modulus only accurately measured the rate constant for the metathesis of the cyclopentyl unsaturation. The ultrasonic values were within 6% of the values determined by FTIR. The activation energy for metathesis of the cyclopentyl unsaturation was 84 kJ mol^?1, following first‐order kinetics. Rate constants for the polymerization of the norbornyl unsaturation could not be determined by ultrasound. The gel point, vitrification, and qualitative information about the reaction rate could be determined from the change in the attenuation. © 2003 Wiley Periodicals, Inc. J Polym Sci Part B: Polym Phys 41: 1323–1333, 2003     

Mechanisms of n‐butanol formation in butyl acrylate latexes

The mechanisms involved in the formation of n‐butanol during the synthesis of butyl acrylate containing latices were investigated. The experimental results showed that neither the hydrolysis of butyl acrylate nor of the ester bond in the butyl acrylate segments of the polymer played a major role in the formation of n‐butanol, which was mainly generated from the polymer backbone, by transfer reactions to polymer chain followed by cyclization. © 2007 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 45: 5838–5846, 2007     

Magnetic poly(N‐isopropylacrylamide) microspheres by dispersion and inverse emulsion polymerization

The aim of this study was to develop novel thermally responsive polymer microspheres with magnetic properties. Dispersion and inverse emulsion copolymerization of N‐isopropylacrylamide (NIPAAm) and N,N′‐methylenebisacrylamide (MBAAm) was investigated in the presence of γ‐Fe₂O₃ nanoparticles. The resulting microspheres were characterized in terms of morphology, size, polydispersity, iron content, and temperature‐dependent swelling using optical microscopy, transmission electron microscopy, scanning electron microscopy, QELS, and AAS. The effects of several variables, such as the concentration of γ‐Fe₂O₃, MBAAm crosslinking agent, Span 80 surfactant, 2,2′‐azobis(2‐methyloctanenitrile) (AMON) initiator, and polymerization temperature on the properties of the microspheres were studied. Swelling and thermoresponsive behavior of the microspheres containing γ‐Fe₂O₃ nanoparticles were also investigated. The microspheres contained about 8 wt % of iron. The presence of magnetic nanoparticles and their concentration changes did not have any significant effect on the temperature sensitivity of the composites. The particles gradually shrink into an increasingly collapsed state when the temperature is raised to 40 °C since the increase in temperature weakens the hydration and PNIPAAm chains gradually become more hydrophobic, which leads to the collapse of the particles. © 2007 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 45: 5884–5898, 2007