PET/SiO2 nanocomposites prepared by cryomilling

The mixed powders of poly(ethylene terephthalate) (PET) and SiO₂ has been subjected to cryomilling. The evolution of microstructure with time was characterized using scanning electron microscope, transmission electron microscope, field emission scanning electron microscope, and laser diffraction particle size analyzer. It was shown that, upon cryomilling for 10 h, SiO₂ nano particles were well deconglomerated into single particles (～30 nm) that get homogeneously dispersed in PET matrix. The resulted PET/SiO₂ primary particles were flake‐shaped with a size of 400 nm. These primary composite particles agglomerated to form secondary composite particles with an average size about 7.6 μm. A three‐stage model was purposed for the formation mechanism of the nanocomposite structures induced by cryomilling. Our evidences suggest that cryomilling is a capable and promising technique for the production of polymer/inorganic nanocomposites. © 2006 Wiley Periodicals, Inc. J Polym Sci Part B: Polym Phys 44: 1161–1167, 2006     

Quasi-static deformation and final fracture behaviour of aluminium alloy 5083: influence of cryomilling

The commercial aluminium alloy 5083 was processed via cryomilling to produce nanocrystalline (NC) powders with an average grain size of ～25–50?nm. The powders were subsequently degassed at 723 K (450°C), pre-heated and immediately quasi-isostatic (QI)-forged to produce a thermally stable bulk ultrafine grain (UFG) material having average grain size values ranging from 190 to 350?nm, depending on the processing conditions used. In this paper, the tensile properties and fracture behaviour of the bulk UFG material are presented and compared with the tensile properties of its conventionally processed counterpart. The specific influence of preheat temperature on strength and ductility of the alloy is briefly discussed. Three different pre-heat temperatures of 523, 623 and 723?K (250, 350 and 450°C) were chosen and used with the primary objective of controlling grain growth during forging. The influence of preheat temperature on tensile deformation and final fracture behaviour is highlighted. The macroscopic fracture modes of the bulk nanostructured material (BNM) prepared following three pre-heat temperatures are investigated. The microscopic mechanisms controlling tensile deformation and final fracture behaviour are discussed with regards to the intrinsic microstructural effects in the UFG alloy, nature of loading, and the kinetics and mechanisms of deformation.     

低温球磨制备5083超细铝合金及性能研究

本文采用低温球磨的方法制备了5083纳米晶铝合金,并用XRD、SEM和DSC等检测手段对样品粉末的微观结构、组织的变化过程和热稳定性进行了研究。结果表明:随着球磨的进行,球磨混合料中Mg相逐渐减少并逐渐固溶于Al中形成合金,粉末颗粒尺寸不断减小;球磨时间和球磨转速是影响合金结构和性能的主要因素,采用低温高速球磨能使合金纳米晶粒更加均匀,有利于Mg固溶于Al中;能谱分析和DSC分析表明,低温液氮球磨过程中形成的氧化物和氮氧化物颗粒对晶粒的钉扎一定程度的提高了5083铝合金的热稳定性。     

Electromagnetic nanocomposites prepared by cryomilling of polyaniline and Fe nanoparticles

The polyaniline (PANI)/iron nanocomposites have been prepared by high‐energy ball milling under cryogenic temperatures, namely cryomilling, of PANI with Fe nanoparticles. It takes 5 h to refine the Fe into an average grain size of 20 nm and to get homogeneously dispersed in PANI matrix. The obtained PANI/Fe nanocomposites have a maximum conductivity of 0.78 S cm^?1 after 2‐h cryomilling, whereas its coercivity increases monotonously with time in the range of experiment up to 10 h. It is found that the sizes of Fe particles have obvious effects on both electrical and magnetic properties. When compared with micrometer Fe particles as raw materials, Fe nanoparticles result in somewhat lower conductivity but a much higher coercivity exceeding 400 Oe. © 2008 Wiley Periodicals, Inc. J Polym Sci Part B: Polym Phys 46: 1571–1576, 2008     

Catalytic activity of novel thermoplastic/cellulose-Au nanocomposites prepared by cryomilling

Due to environmental concerns, increasing attention has been focused on the application and preparation of biobased polymers and their blends. In this study, cellulose, the most spread biopolymer on Earth, was used in the preparation of novel cotton/polypropylene-Au and cotton/polyethylene-Au nanocomposites via a green mechanochemical approach. First, mechanoradicals were generated by ball milling of the cotton and thermoplastics under cryo conditions, and then, these radicals were used in the reduction of Au ions to Au nanoparticles (Au NPs). Nanocomposites were characterized by scanning electron microscopy (SEM), X-ray diffraction (XRD), and X-ray photoelectron spectroscopy (XPS). The application of mechanochemistry in obtaining the cotton/thermoplastic blends allowed homogenous and fine blending of the samples and in addition, excluded the usage of toxic solvents. Since Au NPs exhibit a wide range of applications, e.g., in catalysis, cotton/thermoplastic-Au nanocomposites were used to catalyze the reduction reaction of 4-nitrophenol to
4-aminophenol, followed by UV-Vis spectroscopy. Finally, the hydrophobicity of the nanocomposites was alternated by tuning the blend composition. In the prepared nanocomposites, cotton and thermoplastics acted as very good supporting matrices for the Au NPs and provided satisfactory access to the NPs.     

Consolidation of cryomilled Al–Si using spark plasma sintering

Cryomilled eutectic aluminum–12% silicon powder was sintered using spark plasma sintering (SPS) to create bulk compacts. The cryomilling serves to break up and disperse the eutectic phase in the powder to create a well-distributed Si phase throughout the matrix and to modify the morphology of the Si phase from plate-like to spherical, whilst refining the aluminium grain size to the nanometric level. The effects of different sintering times and temperatures using SPS on the densification of the powder, the aluminium grain size evolution, the growth of the Si phase and the morphology change of the Si phase were investigated. The compacts were analysed using X-ray diffraction, scanning electron microscopy and optical microscopy. The initial stages of densification appear to be highly dependent on the yield strength of the powder. An estimate of the temperature gradient seen in the powder bed was made and calculated to be near 200?°C at the highest point. The Al and Si phase growth was investigated and it was observed that the Si coarsening rate is increased due to the increased volume of grain boundaries. As the Si coarsens, any pinning effect on the Al grains is lost, resulting in a highly unstable microstructure that coarsens rapidly.     

Polyaniline/iron nanocomposites prepared by cryomilling

The polyaniline/iron nanocomposites with both conducting and magnetic properties have been prepared by cryomilling (high‐energy ball milling under cryogenic temperature), in which the average size of iron grains attains 20 nm. Enhanced coercivity of 206 Oe and decreased conductivity of 0.1 S cm^?1 at room temperature have been obtained for the nanocomposites containing 10% volume fraction of iron in polyaniline after cryomilling for 20 h. The high value of the coercivity could be considered due to the presence of a fraction of single‐domain particles in the nanocomposites. The low value of the conductivity could be considered due to the dedoping of conducting polyaniline with the cryomilling time. © 2006 Wiley Periodicals, Inc. J Polym Sci Part B: Polym Phys 44: 3157–3164, 2006     

Thermal behaviors of poly(ethylene terephthalate)/SiO2 nanocomposites prepared by cryomilling

The thermal behaviors of poly (ethylene terephthalate) (PET)/SiO₂ nanocomposites prepared by cryomilling were studied, by comparing with the cryomilled PET and the raw PET. Cryomilling induced amorphization of crystalline PET matrix and the decrease of PET molecular weight. Cryomilled PET/SiO₂ nanocomposites have two abnormal phenomena in the DSC 1st heating thermogram due to the stored energy induced by cryomilling. During DSC cooling process, the dispersed nanometer SiO₂ particles play a role of nucleating agent in PET matrix, and the hot crystallization ability of PET/SiO₂ nanocomposites improves a lot. Besides, the heat stability of cryomilled PET/SiO₂ nanocomposites improves more much during reheating. © 2006 Wiley Periodicals, Inc. J Polym Sci Part B: Polym Phys 44: 1351–1356, 2006