A model for crack formation during active solid pyrolysis of a char-forming solid: crack patterns; surface area generation; volatile mass efflux

A model is developed for the formation and propagation of cracks in a material sample that is heated at its top surface, pyrolyses, and then thermally degrades to form char. In this work the sample is heated uniformly over its entire top surface by a hypothetical flame (a heat source). The pyrolysis mechanism is described by a one-step overall reaction that is dependent nonlinearly on the temperature (Arrhenius form). Stresses develop in response to the thermal degradation of the material by means of a shrinkage strain caused by local mass loss during pyrolysis. When the principal stress exceeds a prescribed threshold value, the material forms a local crack. Cracks are found to generally originate at the surface in response to heating, but occasionally they form in the bulk, away from ever-changing material boundaries. The resulting cracks evolve and form patterns whose characteristics are described. Quantities examined in detail are: the crack spacing in the pyrolysis zone; the crack length evolution; the formation and nature of crack loops which are defined as individual cracks that have joined to form loops that are disconnected from the remaining material; the formation of enhanced pyrolysis area; and the impact of all of the former quantities on mass flux. It is determined that the mass flux from the sample can be greatly enhanced over its nominal (non-cracking) counterpart. The mass efflux profile qualitatively resembles those observed in Cone Calorimeter tests.     

Preparation and properties of the biodegradable graded blend of poly(L‐lactic acid) and poly(ethylene oxide)

We prepared biodegradable poly(ethylene oxide) (PEO)/poly(L ‐lactic acid) (PLLA) graded blends by the dissolution–diffusion process, and discussed the biodegradability and tensile strength of the graded blends by comparing isotropic blend and PLLA only. All the graded blends were degraded more largely than the PLLA only and isotropic blend (PEO: 37.5 wt %), which had the same content as the total content of those graded blends. The graded blend having most excellent wide compositional gradient was degraded most largely with the enzyme. Thus, graded structure of the blends promoted their biodegradabilities large. It was considered that the dissolution of PEO with water increased the surface area attacked by the enzyme, while PEO caught PLLA oligomers to promote the biodegradation of PLLA. Then, the biodegradabilities of the graded blends were suppressed by the increasing crystallinity of PLLA. Furthermore, the strengths of all the graded blends were larger than those of the isotropic blend. © 2007 Wiley Periodicals, Inc. J Polym Sci Part B: Polym Phys 45: 2972–2981, 2007     

Temporary attachment of carbohydrates to cyclopeptide templates: a new strategy for single-bead analysis of multivalent neoglycopeptides

Employing a cleavable carbohydrate–peptide linker, a new strategy for single-bead analysis of multivalent cyclic neoglycopeptides based on Edman degradation is described. Edman degradation of glycopeptides is hampered by the acid lability of the glycosidic bond and potential incompatibilities of phenylthiohydantoin (PTH) derivatives of glycosylated amino acids with PTH derivatives of the proteinogenic amino acids. To overcome this problem, carbohydrates are detached from the cyclopeptide templates before single-bead analysis, allowing for micro sequencing under routine conditions. With this strategy, application of multivalent cyclic neoglycopeptides in split-mix libraries with a subsequent screening process becomes possible for the first time.     

Novel,biodegradable, functional poly(ester‐carbonate)s by copolymerization of trans‐4‐hydroxy‐L‐proline with cyclic carbonate bearing a pendent carboxylic group

Water‐soluble poly(ester‐carbonate) having pendent amino and carboxylic groups on the main‐chain carbon is reported for the first time. This article describes the melt ring‐opening/condensation reaction of trans‐4‐hydroxy‐N‐benzyloxycarbonyl‐L ‐proline (N‐CBz‐Hpr) with 5‐methyl‐5‐benzyloxycarbonyl‐1,3‐dioxan‐2‐one (MBC) at a wide range of molar fractions. The influence of reaction conditions such as catalyst concentration, polymerization time, and temperature on the number average molecular weight (M_n) and molecular weight distribution (M_w/M_n) of the copolymers was investigated. The polymerizations were carried out in bulk at 110 °C with 3 wt % stannous octoate as a catalyst for 16 h. The poly(ester‐carbonate)s obtained were characterized by Fourier transform infrared spectroscopy, ¹H NMR, differential scanning calorimetry, and gel permeation chromatography. The copolymers synthesized exhibited moderate molecular weights (M_n = 6000–14,700 g mol^?1) with reasonable molecular weight distributions (M_w/M_n = 1.11–2.23). The values of the glass‐transition temperature (T_g) of the copolymers depended on the molar fractions of cyclic carbonate. When the MBC content decreased from 76 to 12 mol %, the T_g increased from 16 to 48 °C. The relationship between the poly(N‐CBz‐Hpr‐co‐MBC) T_g and the compositions was in approximation with the Fox equation. In vitro degradation of these poly(N‐CBz‐Hpr‐co‐MBC)s was evaluated from weight‐loss measurements and the change of M_n and M_w/M_n. Debenzylation of 3 by catalytic hydrogenation led to the corresponding linear poly(ester‐carbonate), 4 , with pendent amino and carboxylic groups. © 2004 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 42: 2303–2312, 2004     

Studies of photooxidative degradation of poly(vinyl chloride)/poly(ethylene oxide) blends

The photooxidative degradation of blends (in a full range of compositions) of amorphous poly(vinyl chloride) (PVC) with semicrystalline poly(ethylene oxide) (PEO) in the form of thin films is investigated using absorption spectroscopy (UV–visible and Fourier transform infrared) and atomic force microscopy (AFM). The amount of insoluble gel formed as a result of photocrosslinking is estimated gravimetrically. It is found that the PVC/PEO blendsí susceptibility to photooxidative degradation differs from that pure of the components and depends on the blend composition and morphology. Photoreactions such as degradation and oxidation are accelerated whereas dehydrochlorination is retarded in blends. The photocrosslinking efficiency in PVC/PEO blends is higher than in PVC; moreover, PEO is also involved in this process. AFM images showing the lamellar structure of semicrystalline PEO in the blend lead to the conclusion that the presence of PVC does not disturb the crystallization process of PEO. The changes induced by UV irradiation allow the observation of more of the distinct PEO crystallites. This is probably caused by recrystallization of short, more mobile chains in degraded PEO or by partial removal of the less stable amorphous phase from the film surface. These results confirm previous information on the miscibility of PVC with PEO. The mechanism of the interactions between the components and the blend photodegradation are discussed. © 2004 Wiley Periodicals, Inc. J Polym Sci Part B: Polym Phys 42: 585–602, 2004     

Physical properties of glycosaminoglycan hydrogels

The chemical composition of glycosaminoglycan (GAG) hydrogels was found to have a profound effect on the physical properties of gels. Hyaluronan (HA) and chondroitin sulfate (CS) were each modified with adipic dihydrazide (ADH) with carbodiimide chemistry. The resulting polymer was crosslinked with various concentrations of poly(ethylene glycol) dialdehyde (PEG‐diald) to produce a series of hydrogels. The physical properties of these GAG hydrogels varied in a concentration‐dependent fashion. Maximal crosslinking was observed at a theoretical crosslinking of 50% for the HA‐ADH‐PEG‐diald hydrogels and 75% for the CS‐ADH‐PEG‐diald hydrogels. Adding PEG‐diald beyond the optimum for crosslinking prolonged the in vitro enzymatic degradation time of the hydrogels. The swelling of the crosslinked GAG hydrogels was correlated with the amount of PEG‐diald used rather than with the crosslinking density. © 2004 Wiley Periodicals, Inc. J Polym Sci Part B: Polym Phys 42: 4344–4356, 2004     

Differential scanning calorimetry and thermogravimetric analysis investigation of the thermal properties and degradation of some radiation‐grafted films and membranes

The influence of irradiation and grafting on the crystallinity of three base polymers has been investigated with differential scanning calorimetry. Grafting has the largest effect on the base polymer crystallinity and results in a reduction of the crystallinity. The thermal degradation of the base polymers and grafted films has been investigated with thermogravimetric analysis. The extent of the fluorination of the base polymer, the irradiation method, and the graft level all influence the thermal degradation and its activation energy. It is proposed that the variation of the chain lengths of the grafted polystyrene chains is actually a primary underlying factor responsible for the influence of these various parameters on the degradation process. The first results of a comparative thermal analysis of some fuel‐cell membranes are also presented, and the promise and shortcomings of this method are discussed. © 2004 Wiley Periodicals, Inc. J Polym Sci Part B: Polym Phys 42: 2612–2624, 2004     

硬盘磁头-碟界面润滑剂失效机理及添加剂X-1P的性能研究

采用热重分析 (TGA)、傅立叶红外光分析 (FTIR)和磁头起飞降落 (CSS)等试验方法 ,研究了硬盘磁头 碟界面润滑层PFPE的失效机理以及添加剂X 1P在磁头 碟界面润滑剂中的作用 .研究结果表明 ,高温条件下磁头材料Al2 O3 会诱导磁头 碟界面润滑剂PFPE发生歧化降解 ,造成磁头 碟界面润滑层失效 ;添加剂X 1P因其特殊的分子结构和化学性能 ,可作为一种有效稳定剂添加到磁头 碟润滑剂PFPE中 ,减弱磁头材料Al2 O3 作为催化反应中心的催化反应活性 ,减缓磁头 碟界面润滑剂PFPE的高温歧化降解 ,改善磁头 碟界面的CSS性能