Preparation of rhodium–phyllosilicate catalysts without leaching in liquid-phase 1-hexene hydrogenation

Rhodium catalysts have been prepared on palygorskite and montmorillonite (clay) supports by reduction with hydrogen (1 atmosphere) at room temperature of a cationic organometallic rhodium compound anchored to the support. The activity of these catalysts for the hydrogenation of liquid-phase 1-hexene remains constant with increase of prehydrogenation time and with re-use for several runs. No rhodium leaching is observed.     

A novel tridentate nitrogen donor as ligand in copper catalyzed ATRP of methyl methacrylate

A tridentate ligand, BPIEP: 2,6‐bis[1‐(2,6‐diisopropyl phenylimino) ethyl] pyridine, having central pyridine unit and two peripheral imine coordination sites was effectively employed in controlled/“living” radical polymerization of MMA at 90°C in toluene as solvent, Cu^IBr as catalyst, and ethyl‐2‐bromoisobutyrate (EBiB) as initiator resulting in well‐defined polymers with polydispersities M_w/M_n ≤ 1.23. The rate of polymerization follows first‐order kinetics, k_app = 3.4 × 10^?5 s^?1, indicating the presence of low radical concentration ([P*] ≤ 10^?8) throughout the reaction. The polymerization rate attains a maximum at a ligand‐to‐metal ratio of 2:1 in toluene at 90°C. The solvent concentration (v/v, with respect to monomer) has a significant effect on the polymerization kinetics. The polymerization is faster in polar solvents like, diphenylether, and anisole, as compared to toluene. Increasing the monomer concentration in toluene resulted in a better control of polymerization. The molecular weights (M_n,SEC) increased linearly with conversion and were found to be higher than predicted molecular (M_n,Cal). However, the polydispersity remained narrow, i.e., ≤1.23. The initiator efficiency at lower monomer concentration approaches a value of 0.7 in 110 min as compared to 0.5 in 330 min at higher monomer concentration. The aging of the copper salt complexed with BPIEP had a beneficial effect and resulted in polymers with narrow polydispersitities and higher conversion. PMMA obtained at room temperature in toluene (33%, v/v) gave PDI of 1.22 (M_n = 8500) in 48 h whereas, at 50°C the PDI is 1.18 (M_n = 10,300), which is achieved in 23 h. The plot of lnk_app versus 1/T gave an apparent activation energy of polymerization as (ΔE^≠_app) 58.29 KJ/mol and enthalpy of equilibrium (ΔH⁰_eq) to 28.8 KJ/mol. Reverse ATRP of MMA was successfully performed using AIBN in bulk as well as solution. The controlled nature of the polymerization reaction was established through kinetic studies and chain extension experiments. © 2005 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 43: 4996–5008, 2005     

Förster energy transfer from poly(arylene–ethynylene)s to an erbium–porphyrin complex

We study the infrared emission at 1.54 μm of an organolanthanide complex, Er(III)-tetraphenylporphyrin [Er(TPP)acac], both as a result of direct optical excitation and via energy transfer from host π-conjugate polymers of type poly(arylene–ethynylene) [PAE]. In the first case, the emission of the neat complex is characterized in inert transparent materials and a value of the quantum yield at 1.54 μm φ_IR=4×10⁻⁴ is measured. Then, fluorescence resonance transfer is investigated in blends of Er(TPP)acac with PAEs by monitoring the quenching of the polymer fluorescence along with the enhancement of both the visible emission of the ligand and the near-infrared band of Er³⁺. These different procedures allow a detailed analysis of the transfer efficiency within a specific implementation of the Förster model for polymeric donors. The experimental values of the critical radius R₀, ranging from 1.3 to 2.5 nm for the different blends, are in good agreement with theory for a wide interval of the physical and spectroscopic parameters. This suggests that other mechanisms for excitation transfer do not play a significant role in these materials.     

Estimation of growth rate in unidirectionally solidified multicrystalline silicon by the growth-induced striation method

Multicrystalline silicon was grown by unidirectional solidification method using the accelerated crucible rotation technique. The application of the accelerated crucible rotation technique in unidirectional solidification method induced growth striations across the axial direction of the grown crystal. This striation pattern was observed from carbon concentration distribution, obtained by using Fourier transform infrared spectroscopy. The generated striation pattern was found to be weak and discontinuous. Some striations were absent, probably due to back melting, caused during each crucible rotation. From the growth striations and applied time period in crucible rotation, the growth rate was estimated by using Fourier transformation analysis.     

1H and 13C NMR spectroscopic study of oxidation of D,L‐cystine and 3,3′‐dithiobis(propionic acid) with hydrogen peroxide in aqueous solution

The oxidation of symmetrical disulfides [D ,L ‐cystine ( 1 ) and 3,3′‐dithiobis(propionic acid) ( 2 )] with hydrogen peroxide in D₂O–NaOH solution (pH 10–11) was studied by NMR spectroscopy. Assignments of the proton and carbon NMR signals of starting materials ( 1 and 2 ) and products of oxidation are based on conventional 1D NMR methods (DEPT, selective spin decoupling). Formation of C—S bond cleavage products or, in case of 2 , partially oxidized intermediates was not detected. The accelerating effect of Cu²⁺ cations, but not Fe³⁺ cations, on the oxidation rate of 1 in basic medium was demonstrated. Copyright © 2002 John Wiley & Sons, Ltd.     

Two‐stage copolycondensation of preformed oligomers with bisphenols by tosyl chloride/dimethylformamide/pyridine from distributions of resulting oligomers determined by a combination of gel permeation chromatography and NMR

A two‐stage co‐oligomerization of the oligomers initially formed from an equimolar mixture of isophthalic acid (IPA) and terephthalic acid (TPA) and 2,2‐bis(4‐hydroxyphenyl)propane (BPA, 50 mol %) with bisphenols (BPs, 20 mol %) was carried out using a tosyl chloride/dimethylformamide/pyridine condensing agent. The distributions of the resulting oligomers (n_x‐mers), which were quenched with methanol, were determined by a combination of gel permeation chromatography (GPC) and NMR. These distributions (presented by molar percentage) were conveniently calculated with the equation n_x (mol %) = n_x (% mol by GPC) × n₀ (mol % by NMR)/n₀ (% mol by GPC), where n_x (% mol) = n_x (wt % by GPC)/its molecular weight. The results showed the distributions of the preformed IPA/TPA‐BPA oligomers to be in fairly good accord with those obtained directly from GPC and to be supported by the NMR results. The calculation was applied to the co‐oligomers prepared up to a reaction of 0.7, at which there was an increase in the number of higher oligomers indivisible by GPC and the distributions could no longer be determined by molar percentage. The calculated distributions are discussed in relation to the results of copolycondensation. The sequence distributions in the resulting co‐oligomers, which were also examined by NMR, are compared with those in the copolymers. © 2003 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 42: 44–51, 2004     

Shear banding in strained semicrystalline polyamide 6 films as revealed by atomic force microscopy: Role of the amorphous phase

Atomic force microscopy (AFM) has been used to visualize the plastic deformation mechanisms that are responsible for the yielding of semicrystalline polymers of low degree of crystallinity (<50%). Indeed, AFM, if operated in suitable conditions, is able to image both the amorphous and the crystalline phases. Polyamide 6 films have been drawn at temperatures T < 160 °C. Postmortem AFM observations show that, at yield, shear bands nucleate and propagate in the amorphous phase. They cross the crystalline lamellae and run over the whole surface of the sample. By crossing the lamellae, they form nanoblocks of uniform size. Neither the size of the nanoblocks nor the angle between the tensile axis and the shear bands can be explained in terms of crystal plasticity. © 2004 Wiley Periodicals, Inc. J Polym Sci Part B: Polym Phys 42: 687–701, 2004     

Mutual influence of the morphology and capillary rheological properties in nylon/glass‐fiber/liquid‐crystalline‐polymer blends

Nylon‐6/glass‐fiber (GF)/liquid‐crystalline‐polymer (LCP) ternary blends with different viscosity ratios were prepared with three kinds of nylon‐6 with different viscosities as matrices. The rheological behaviors of these blends were characterized with capillary rheometry. The morphology was observed with scanning electron microscopy and polarizing optical microscopy. This study showed that although LCP did not fibrillate in binary nylon‐6/LCP blends, LCP fibrillated to a large aspect ratio in some ternary blends after GF was added. The addition of 5 wt % LCP significantly reduced the melt viscosity of nylon‐6/GF blends to such an extent that some nylon‐6/GF/LCP blends had quite low viscosities, not only lower than those of neat resins and nylon‐6/GF blends but also lower than those of corresponding nylon‐6/LCP blends. The mutual influence of the morphology and rheological properties was examined. The great reduction of the melt viscosity was considered the result of LCP fibrillation. © 2004 Wiley Periodicals, Inc. J Polym Sci Part B: Polym Phys 42: 1619–1627, 2004     

Pressure and temperature dependence of the gas‐transport properties of dense poly[2,6‐toluene‐2,2‐bis(3,4‐dicarboxylphenyl)hexafluoropropane diimide] membranes

The gas‐transport properties of poly[2,6‐toluene‐2,2‐bis(3,4‐dicarboxylphenyl)hexafluoropropane diimide] (6FDA‐2,6‐DAT) have been investigated. The sorption behavior of dense 6FDA‐2,6‐DAT membranes is well described by the dual‐mode sorption model and has certain relationships with the critical temperatures of the penetrants. The solubility coefficient decreases with an increase in either the pressure or temperature. The temperature dependence of the diffusivity coefficient increases with an increase in the penetrant size, as the order of the activation energy for the diffusion jump is CH₄ > N₂ > O₂ > CO₂. Also, the average diffusion coefficient increases with increasing pressure for all the gases tested. As a combined contribution from sorption and diffusion, permeability decreases with increases in the pressure and the kinetic diameter of the penetrant molecules. Even up to 32.7 atm, no plasticization phenomenon can be observed on flat dense 6FDA‐2,6‐DAT membranes from their permeability–pressure curves. However, just as for other gases, the absolute value of the heat of sorption of CO₂ decreases with increasing pressure at a low‐pressure range, but the trend changes when the feed pressure is greater than 10 atm. This implies that CO₂‐induced plasticization may occur and reduce the positive enthalpy required to create a site into which a penetrant can be sorbed. Therefore, a better diagnosis of the inherent threshold pressure for the plasticization of a glassy polymer membrane may involve examining the absolute value of the heat of sorption as a function of pressure and identifying the turning point at which the gradient of the absolute value of the heat of sorption against pressure turns from a negative value to a positive one. © 2003 Wiley Periodicals, Inc. J Polym Sci Part B: Polym Phys 42: 354–364, 2004