Dependence of Performance of Organic Light-emitting Devices on Sheet Resistance of Indium-tin-oxide Anodes

IntroductionIndium-tin-oxide(ITO) has been widely used asthe anode material in organic light-emitting devices(OLEDs) because of its high transmittance in the visi-ble region and low electrical resistivity. In the pastyears, many investigations focused on …     

煅烧温度对TiO2/SiO2混合氧化物表面酸量的影响

采用共沉淀法制备了高钛含量的复合氧化物TiO2／SiO2．用BET、XRD、FT-IR和正胺吸附等分析手段，研究了煅烧温度对TiO2／SiO2表面酸量的影响．研究发现，随着煅烧温度的升高，TiO2／SiO2表面羟基密度、比表面积逐渐减少，TiO2晶粒尺寸变大，造成TiO2／SiO2表面酸量降低．当煅烧温度达到600℃到800℃之间，表面酸量基本不再改变．     

TiSiW12O40/TiO2催化合成己酸异戊酯

报道了以固载杂多酸盐TiSiW12O40/TiO4为多相催化剂，通过己酸和异戊醇反应合成了己酸异戊酯，探讨了TiSiW12O40/TiO4对酯化反应的催化活性，较系统地研究了醇酸摩尔比，催化剂用量，反应时间诸因素对收率的影响，实验表明：TiSiW12O40/TiO4是合成己酸异戊酯的良好催化剂，在n(醇）：n(酸）＝1．6：1，催化剂用量为反应物总质量的1．5％，反应时间45min，使用环己烷为带水剂的适宜条件下，己酸异戊酯的收率可达91．9％。     

A Novel Plasticizer for the Preparation of Thermoplastic Starch

TPS was a biodegradable material based on starch. Starch was an inexpensive and natural renewable polysaccharide, which was widely investigated as the substitute of petroleum-derived plastics. Native starch commonly existed in granule structure with about…     

偶氮胂-DBS用于光度法测定牛血清白蛋白

在室温下,于pH 2.5的Britton-Robinson缓冲溶液中及非离子表面活性剂OP存在下,牛血清白蛋白(BSA)与偶氮胂-DBS的复合物的最大吸收在514 nm波长处,但显色复合物与试剂空白吸光度之差在370 nm处最大,选择在370 nm处测定,反应迅速完成。非离子表面活性剂OP可提高反应灵敏度及复合物稳定性。乙醇可提高体系灵敏度。BSA的质量范围在0~60.0 mg.L-1范围内符合比耳定律,方法表观摩尔吸光率3ε70 nm=8.58×105L.mol-1.cm-1。方法用于测定血清样品中蛋白质的总量,5次测定值的RSD为0.60%,回收率为98.0%。     

固相氯化法合成氯化聚乙烯的红外光谱研究

本文研究在不同条件固相氯化聚乙烯(CPE)的红外光谱,探讨了一步和两步氯化合成的CPE的结构差别,着重讨论了两步氯化的CPE结构特点。从观察表征结晶结构和—(CH_2)_n—链段氯分布的特征频率变化表明,低温固相氯化主要发生在无定形区,并且在CPE中形成高氯化和低氯化链段(或未氯化)的嵌段结构。在两步固相氯化时,晶区受到较大程度的破坏,氯化作用已不局限在无定形区,其结晶结构的破坏主要同第二步氯化程度有关,即使CPE氯含量相同,若前后两步氯化程度不同,结构有很大差异。     

FREQUENCY DEPENDENCE OF THE DIELECTRIC RELAXATION OF 1,2-POLYBUTADIENES

The dielectric loss factor and permittivity of a series of 1, 2-polybutadienes with different contents of 1, 2-units and different contents of syndiotactie 1, 2-units were determined over a frequency range from 30Hz to 100KHz at different temperatures. The WLF equation was evaluated for various samples with T_θat 100KHz as a reference temperature and the master curves of various samples have been constructed, which are in accordance with those calculated by Havriliak-Negami equation. The frequency dependence of the dielectric relaxation of 1, 2-polybutadienes was investigated over a frequency range from 10~0 Hz to 10~(12) ZHz in terms of the experimental data and the master curves.     

一种新的磷酸根离子敏感电极研究

一种新的磷酸根离子敏感电极研究肖丹，俞汝勤，李军，袁孔铨（湖南大学化学化工系，长沙，４１００８２）关键词磷酸根，离子选择电极，磷酸二氢根磷酸根离子浓度的测定在化学化工、环境保护、生命科学和临床医学等领域有着重要的意义。对磷酸根离子敏感电极的研究和探索...     

ZrxTixAl1-2xO2的制备及其在三效催化剂上的应用

Zr_0.5Ti_0.5O₂(ZT) and Zr_0.25Ti_0.25Al_0.5O₂(ZTA) mixed oxides were prepared by co-precipitation method and characterized by low temperature adsorption-desorption， XRD and NH₃-TPD. The activity of Pt/Zr_0.5Ti_0.5O₂ and Pt/ Zr_0.5Ti_0.5Al_0.5O₂ catalysts was evaluated using the simulated gases. The results show that ZTA samples exhibit higher specific surface area， larger pore volume and proper surface acidic amount and acidity in comparison with ZT. The results of the catalytic test indicate that Pt/ZT and Pt/ZTA catalysts exhibit excellent low-temperature catalytic activity and lower light-off temperatures of hydrocarbon， carbon monoxide and nitrogen oxides， especially better conversion for nitrogen oxides (NO_x). The addition of Al₂O₃ into ZT enhanced the anti-aging property of Pt/ ZTA catalysts due to the excellent textural， structural， surface acidity and thermal stability.     

新型蒈酸基双酰肼化合物的合成及其生物活性

先将3-蒈烯分子中的碳碳双键氧化开环制得蒈酮酸，再将羰基还原成亚甲基得到蒈酸，酰氯化后与系列酰肼发生N-酰化反应合成了14个新型蒈酸基双酰肼化合物(5a～5n)，其结构经UV-Vis、¹H NMR、¹³C NMR、 FT-IR和MS(ESI)表征，并测试了目标化合物的抑菌和除草活性。结果显示：在用药量为50 μg·mL^-1时，目标化合物对花生褐斑病菌、小麦赤霉病菌、黄瓜枯萎病菌、苹果轮纹病菌、番茄早疫病菌、玉米小斑病菌、西瓜炭疽病菌以及水稻纹枯病菌等8种植物病原菌具有一定的抑制活性，其中化合物蒈酸基α-噻吩甲酰肼5f（R=α-thiophene）对苹果轮纹病菌的抑制率达85.0%，优于阳性对照百菌清。在用药量为100 μg·mL^-1时，化合物蒈酸基3′,4′-二甲氧基苯甲酰肼5j(R=3′,4′-OMe-Ph)、蒈酸基-m-甲氧基苯甲酰肼5d(R=m-OMe-Ph)、蒈酸基-m-甲基苯甲酰肼5b(R=m-Me-Ph)和蒈酸基苯甲酰肼5a(R=Ph)对油菜胚根生长的抑制率分别为88.5%、 86.1%、 85.1%和82.6%（均为A级活性水平），优于阳性对照丙炔氟草胺。