MgFe2O4-Fe2O3纳米粉体的软化学合成及电磁学特性

Nano-MgFe₂O₄-Fe₂O₃ magnetic powders were synthesized by citrate gel under microwave irradiation. The structure，particle size distribution，electromagnetic characteristics of nano-MgFe₂O₄-Fe₂O₃ were characterized by using TG-DTA, X-ray, electronic microscope, nano-size measurement and electromagnetism measurement apparatus。The results show that the product is a mixture of MgFe₂O₄ and Fe₂O₃ with average size of 44 nm, tanδ for the product is 0.265 and 0.610 at frequency of 1.0 GHz and 1.8 GHz respectively.     

Single crystal tin nano-rod arrays electrodeposited by a soft template

Single crystal tin nano-rod arrays were fabricated by the electrodeposition method when amphiphilic triblock copolymer P123 was used as a soft template at a concentration much lower than that for forming a liquid crystalline phase.     

Highly visible-light luminescence properties of the carboxyl-functionalized short and ultrashort MWNTs

Luminescence of the short multiwalled carbon nanotubes (MWNTs) conjugated with carboxylic acid groups has been studied. The results show that the carboxyl-functionalized short MWNTs could emit luminescence and the emission peak appears at 500 nm with a corresponding optimal excitation wavelength centering at 310 nm. When the short MWNTs are filtered through 0.15 μm polytetrafluoroethylene (PTFE) membrane, the ultrashort MWNTs are obtained from the filtrate. An interesting feature for the ultrashort MWNTs is that the emission intensity is strengthened and the peak is slightly blue shifted to 460 nm. This result indicates that the luminescence properties of MWNTs are strongly affected by the tube length. After chemical oxidization cutting, defects and carboxylic acid groups at the tube end and/or sidewall can be produced; the more shorten of MWNTs, the better dispersion and carboxylic passivation of the nanotubes, and the more intense luminescence emissions. The broad emissions are logically attributed to the trapping of excitation energy by defect sites in the carboxyl-functionalized nanotube structure.     

Aerobic oxidation assisted by ligand-free palladium catalysts

Aerobic oxidation of electron-rich benzylic and phenyl allylic alcohols was achieved with high yields with only 0.1 mol.% of Pd(OAc)2 catalyst in the absence of any ligand. This procedure was expected to be valuable for realistic industrial-scale applications from both economic as well as environmental points of view.     

稀土在鼠肝中的物种分布

采用 ICP-MS、微量蛋白层析分离技术 ,研究了长时间、低剂量混合稀土及短时间、高剂量硝酸镧分别对大鼠及小鼠作用后 ,稀土在鼠肝中的代谢累积及其物种分布 .结果表明 ,鼠肝中各稀土含量随给药剂量的增加而增大 ,其累积速度大小顺序为 La>Ce>Nd>Pr;经柱层析分离未得到与稀土特异结合的鼠肝蛋白 ;稀土可与多种鼠肝蛋白 (包括多种重要的酶 )结合 ,在一定条件下 ,稀土与其结合蛋白可发生解离     

Alkylation of benzene with 1-hexene in acidic ionic liquid systems: Et3NHCl-FeCl3and Et3NHCl-AlCl3ionic liquids

Summary The alkylation of benzene with 1-hexene has been investigated in different triethylamine hydrochloride-ferric chloride (Et₃NHCl-FeCl₃) and triethylamine hydrochloride-aluminium chloride (Et₃NHCl-AlCl₃) ionic liquids. Both high catalyst activity and monoalkylation selectivity were observed for these two type of ionic liquids. Systems prepared by modification with HCl in Et₃NHCl-FeCl₃ionic liquids prove to be very suitable solvents and catalysts for the reaction. When employing Et₃NHCl-AlCl₃ionic liquids as catalysts, the reaction takes place in biphasic mode with facile catalyst separation and catalyst recycling.     

偶合反应化学发光法测定痕量银的研究

本文报道了Ａｇ（Ⅰ）催化ｏ－ｐｈｅｎ和Ｋ４Ｆｅ（ＣＮ）６的配位体取代反应与Ｌｕｍｉｎｏｌ－Ｃｕ（ＣＮ）２－４的化学发光反应偶合测定痕量银的方法．方法的线性浓度范围为１×１０－１１～１×１０－７ｇ／ｍＬＡｇ，检出限为４×１０－１２ｇ／ｍＬＡｇ，用于水样分析，结果较为满意     

Concise Synthesis and Antimicrobial Activities of New Substituted 5‐Isoxazolpenicillins

The synthesis of a series of new 5‐isoxazolpenicillins is described, which were obtained by coupling substituted isoxazoles with 6‐APA. Concise large‐scale synthesis of 3,5‐disubstituted isoxazoles by 1,3‐dipolar cycloaddition using copper(I) as catalyst was also investigated. Representative compounds were assayed for antimicrobial activities, showing satisfactory antimicrobial activities against Gram‐negative bacteria.     

微波辐射下4-(4-羟基-3-甲氧基)苯基-3,3,6,6-四甲基-1,8-二氧代1,2,3,4,5,6,7,8,9,10-十氢吖啶的合成和晶体结构

标题化合物C24H29NO4?1/2C2H5OH稨2O)由香兰素、5,5-二甲基-1,3-环己二酮、醋酸铵在微波辐射下干反应并经95%乙醇重结晶而得C24H29NO4穀2(C2H5OH稨2O)晶体。结构通过单晶X-射线衍射法确定,其晶体属单斜晶系,空间群P21/n, a = 9.810(2), b = 14.516(3), c = 17.008(3) ? b = 101.03(2), V = 2377.2(8) ?, Z = 4, Mr = 427.52, Dc = 1.195 g/cm3 , m(MoKa) = 0.082 mm-1, F(000) = 920。晶体结构用直接法解出,经全矩阵最小二乘法对原子参数进行修正,最终的偏离因子为R = 0.0406, wR = 0.0892。X-射线衍射分析结果表明,吡啶环和与之稠合的2个六员环均为信封式构象。