以2-巯基苯并咪唑为保护剂,聚乙烯吡咯烷酮为稳定剂,水合肼为还原剂,“一锅法”合成2-巯基苯并咪唑保护的,高稳定性、强荧光、大斯托克斯位移的铜纳米团簇(Cu NCs),并用于检测水样中的银离子含量。采用透射电子显微镜(TEM)和X射线光电子能谱(XPS)对铜纳米团簇的结构进行表征,通过荧光光谱和紫外可见光谱对其光学性能进行研究。研究表明:该铜纳米团簇的最大激发和发射波长分别为340和558 nm,在日光灯和紫外灯下分别为无色和橙色。Cu NCs具有较高的分散性,尺寸大小为2~3 nm。在最佳反应条件下,铜纳米团簇可以选择性地被银离子猝灭,且灵敏度高,线性范围为1~40μmol/L,检测限为0.5μmol/L。该方法用于检测实际水样(自来水、湖水)中银离子的浓度,结果令人满意,表明在环境监测中有非常高的应用价值。     

增容剂对聚丙烯/粘土纳米复合材料热分解动力学的影响

采用三单体固相接枝聚丙烯作为增容剂制备了聚丙烯粘土纳米复合材料.通过XRD和TEM表征了其纳米结构.利用动态TGA方法研究了聚丙烯和纳米复合材料的热稳定性.分别采用Flynn Wall Ozawa和Kissinger法研究了聚丙烯及其纳米复合材料的热分解动力学.结果都表明,蒙脱土的加入明显提高了聚丙烯的起始热分解温度,纳米复合材料热失重10%时的温度比聚丙烯提高40K左右;纳米复合材料的热分解温度区间明显比聚丙烯的窄;纳米复合材料热分解表观活化能明显增大,与聚丙烯相比提高50%以上.     

Allylation of Aromatic Aldehyde under Microwave Irradiation

Allylation of carbonyl compounds is one of the most interesting processes for the preparation of homoallylic alcohols. Over the past few decades, many reagents have been developed for such reactions[1～3]. In this paper, we first report allylic zinc reagent 1, which can be prepared from zinc dust and allyl bromide conveniently in THF, and reacted with aromatic aldehyde to give homo-allylic alcohols under microwave irradiation.     

有机溶剂性质及其水含量对酶催化合成含D－氨基酸残基的二肽衍生物的影响

有机溶剂性质及其水含量对酶催化合成保护的寡肽及其衍生物有显著影响。系 统地研究了有机溶剂性质及在不同有机溶剂中水含量对α－胰凝乳蛋白酶催化合成 含D－氨基酸残基的二肽衍生物产率的影响。用α－胰凝乳蛋白酶、枯草杆菌蛋白 酶和嗜热杆菌蛋白酶在有机溶剂中催化合成了一系列保护的二肽及其衍生物，并研 究了水含量对反应产率的影响，得到了十分有意义的结果。     

微孔[Me4N]2HgGe4S10的溶剂热合成与表征

用溶剂热方法合成了[Me₄N]₂HgGe₄S₁₀, 通过单晶X射线衍射, IR, DSC-TG手段对其进行了表征. 结果表明, 标题化合物属四方晶系, I-4空间群, 晶胞参数a＝0.92687(8) nm, c＝1.43739(12) nm, V＝1.23484(18) nm³, Z＝2, Mo Kα λ＝0.071073 nm, R₁＝0.0570, wR₂＝0.1374, 空旷骨架结构由超四面体Ge₄S₁₀与HgS₄四面体共用顶点连接而成, 有机模板离子在一维孔道中. 该化合物具有一定的热稳定性, 在320 ℃发生分解形成GeS₂.     

洋葱状富勒烯的提纯研究

以石墨粉为碳源, Al为催化剂, 采用真空热处理法制备了平均粒径为15～35 nm的洋葱状富勒烯(OLFs).并用CS₂分离和空气氧化法对得到的OLFs初产品进行了提纯处理.高分辨透射电镜(HRTEM)、X射线衍射(XRD)、热重分析(TGA)对提纯前后样品的分析表明, CS₂分离处理可有效去除初产品中裸露的金属催化剂微粒,然后在空气中610 ℃焙烧200 min,可基本去除无定型碳,并大量去除了石墨状碎片等碳杂质, OLFs的纯度在50％(体积分数)以上.     

Rapid Synthesis of Lead Oxide Nanorods by One-step Solid-state Chemical Reaction at Room Temperature

A simple and facile method was reported to synthesize lead oxide nanorods. Nanorods of lead oxide were obtained directly from grinding solid metal salt and sodium hydroxide in agate mortar with the assistance of a suitable nonionic surfactant in only one step, which is different from the result of hydroxide in solution. The product has been characterized by XRD, TEM and SEM. The formation mechanism of rod-like morphology is discussed and the surfactant plays an important soft-template role in modifying the interface of solid-state reaction and according process of rod-formation.     

链状[NH3CH2CH2NH3]AgAsS4的溶剂热合成及表征

利用溶剂热方法合成了链状[NH3CH2CH2NH3]AgAsS4,通过单晶X射线衍射技术对其进行了晶体结构分析,该化合物晶体属单斜晶系,空间群C2/c,晶胞参数a=1.35805(8)nm,b=0.65331(3)nm,c=2.27711(9)nm,β=106.42(3)°,Z=8.化合物具有有趣的梯子状双链结构,该阴离子链由AsS4与AgS3共用顶点交替连接而成,有机阳离子在阴离子链之间存在较强的N—H…S氢键.DSC和Tg分析结果表明化合物在200℃以下是稳定的.     

(EnH2)2Ge2S6的合成与结构表征

用溶剂热方法制备了(EnH2)2Ge2S6单晶.单晶X射线衍射分析结果表明,(EnH2)2Ge2S6属单斜晶系,P2(1)/n空间群,晶胞参数a=0.67125(5)nm,b=1.12290(4)nm,c=1.07518(4)nm,β=92.288(2)°,Z=2.利用DSC及TG分析研究了其热稳定性,结果表明,该化合物在200℃以下能够稳定存在.     

氧化锌薄膜的电化学沉积和表征

以透明导电玻璃(TCO)为衬底，用硝酸锌水溶液作为电解液，研究了阴极还原沉积ZnO薄膜的反应机理和电化学行为. 通过改变工艺条件来控制ZnO的生长速率， 得到了粒径为10～15 nm的纳米ZnO薄膜. XRD分析显示纳米ZnO薄膜纯度高， 呈纤锌矿结构. 光学测试结果表明，在可见光区其透光度高达90%，禁带宽度为3.37 eV.