SiO₂ monoliths with double-pore structure were synthesized with tetraethyl orthosilicate, polyethylene glycol, starch, ethanol and ammonia as the main raw materials via a sol-gel route. The effect of different content of starch of the samples was studied on the mesopore structure, macropore appearance, hydrothermal stability and enzyme activity to immobilize gluczyme. The results indicate that porous blocks with mesopores of 10～12 nm and macropores of 10～30 μm can be formed by the removal of polyethylene glycol and starch after heating at 600 ℃. The minimal density of the obtained samples was 0.34 g·cm^-3 and the maximal porosity was 76%. After being immersed in water at 80 ℃ for 7 d, the density, porosity and shape of N₂ adsorption-desorption curves of the samples were almost unchanged, showing that the sample has a good hydrothermal stability. The initial enzyme activity of sample P2KD30 was 11 190 U, and definite enzyme activity could be maintained after five cycles.     

明胶/PEG制备多孔块状SiO2载体及葡萄糖淀粉酶的固定

本文通过溶胶-凝胶法，以正硅酸乙酯、聚乙二醇和明胶为主要原料，制得了孔径约为20 nm的生物酶载体用多孔SiO₂块状材料，并着重研究了热处理温度对多孔SiO₂载体的结构和酶活力的影响。明胶的加入能有效地防止SiO₂表面羟基在烧结过程中的失活现象，提高了多孔材料的吸附能力。制备过程中未加入明胶样品(G0)的酶吸附量和初始酶活力回收率的最高值分别为90 mg·g^-1和11%；加入质量分数为15%明胶的样品(G15)的酶吸附量和初始酶活力回收率分别提高到115 mg·g^-1和38%以上。经过5次重复使用后，G15载酶块体所显示的酶活力还高于G0载酶块体的初始酶活力。600 ℃热处理后所制得的G15样品表现出较好的综合性能，此类多孔块体材料便于酶的回收、保存和再利用。     

稀土离子掺杂硼铝酸盐玻璃的发光性能

用高温熔融法制备了Eu2+单掺和Dy3+-Eu3+、Tb3+-Eu3+共掺的硼铝酸盐玻璃,研究了其激发和发射光谱性能.结果表明:Eu2+单掺的玻璃在蓝光区域能够产生有效激发,并且发射峰呈现黄绿色发光,随着B2O3含量的增加,玻璃的配位场强度降低,Eu2+的发射峰发生蓝移.Dy3+-Eu3+共掺玻璃中Dy3+在451 nm处呈现最强激发峰,在其激发下Dy3+向Eu3+产生能量传递,并发出蓝、黄和红光.Tb3+-Eu3+共掺玻璃在482 nm蓝光的激发下,Tb3+向Eu3+产生能量转移,并发出绿、黄和红发光.这些发射带与蓝光发光二极管(LED)复合可产生白光.     

共沉淀条件对纳米级Sb/SnO2粒度和电性能的影响

导电粉;共沉淀温度;pH值;微粉末特性;共沉淀条件对纳米级Sb/SnO2粒度和电性能的影响     

二氧化硅-聚苯胺(SiO2-PANI)杂化透明导电薄膜的制备和表征

本文采用溶胶-凝胶法,以3-巯丙基三甲氧基硅烷(MPTMS)和聚苯胺为主要原料,制备得到有机-无机杂化透明导电薄膜。着重研究制备过程中醋酸、间甲酚和聚苯胺含量对薄膜结构、导电性和可见光透过率的影响。通过红外光谱可知,采用溶胶-凝胶法可制得结构稳定的杂化导电材料。醋酸作为水解缩聚反应的反应剂和催化剂,当其与3-巯丙基三甲氧基硅烷的物质的量比为0.4时,MPTMS的水解缩聚速率和聚苯胺掺杂入无机前驱体的掺杂速率达到平衡。此外,透明杂化导电薄膜的方块电阻随间甲酚和聚苯胺含量的增加而降低,当间甲酚和3-巯丙基三甲氧基硅烷的物质的量比为5,聚苯胺和二氧化硅的质量比为3/7时,薄膜的方块电阻为3.23 kΩ/□,可见光透过率为80%。     

纳米级掺锑SnO2微粉的制备和性能

以SnCl4·5H2O和SbCl3为原料,采用共沉淀法制得纳米级的SnO2微粉.用DSC-TG、XRD、TEM和UV等方法观测了微粉末,比较系统地研究了掺Sb浓度对粉末颗粒度和电阻的影响规律,探讨了纳米级掺锑SnO2微粉的显色机理.     

碱土金属离子对硼铝酸盐玻璃发光性能的影响

以等离子显示板(PDP)用蓝色荧光粉BaMgAl(10)O(17):s E(2)(BAM)为基础,加入B3,及不同的碱土金属离子Mg2+,Sr2+,Ba2+,采用高温熔融法制备了硼铝酸盐透明发光玻璃.光谱分析表明不同碱土金属离子硼铝酸盐透明玻璃在紫外和紫蓝光区域均可有效激发,于蓝光处产生强光发射.发射峰按照加入Mg2+...     

制备条件对Sb/SnO2超细粉水分散性的影响

制备条件对Sb/SnO2超细粉水分散性的影响     

热处理对多孔SiO2块材结构和性能的影响

以正硅酸乙酯、聚乙二醇和乙醇等为主要原料,采用溶胶-凝胶法制备了固定化酶用的块状多孔SiO2,着重研究了不同热处理温度下材料的红外光谱、孔径分布和水热稳定性.结果表明:600℃热处理后可有效去除残余有机物,形成无定形硅氧网络结构,并得到细孔比表面积为392m2/g、孔容积为0.93 cm3/g、平均孔径为17 nm的圆柱状多孔SiO2;但经800℃以上热处理后多孔材料的体积密度显著增加、开口气孔率和比表面积急剧减小.600℃热处理的多孔材料在80℃热水中浸泡72 h后,氧化硅溶出率小于2%,细孔比表面积减少小于7%,显示出较好的水热稳定性.     

助熔剂法合成Gd2O2S:Tb荧光粉

采用共沉淀法制备前驱体,再加入助熔剂煅烧合成Gd2O2S:Tb荧光粉,并对制备的荧光粉样品的晶体结构及发光性能进行了系统研究.结果表明:助熔剂的选择对Gd2O2S:Tb荧光粉合成影响显著;当Li2CO3与Li3PO4添加量的摩尔比为2:1时发光亮度最大,且颗粒分布较均匀;当助熔剂的质量分数为0.35时发光性能最好.