Fe掺杂对BiTaO_4陶瓷样品介电和铁电特性的影响

为探究Fe掺杂对BiTaO4陶瓷样品介电特性和铁电特性的影响,采用传统固相烧结法制备了Bi Ta1-xFexO4-x(x=0,0.01,0.03)陶瓷样品,利用X线衍射仪和扫描电子显微镜对样品的晶体结构和表面形貌进行分析,利用精密阻抗分析仪和铁电分析仪对样品的介电性能和铁电性能进行检测.结果表明:Fe掺杂没有明显改变样品的晶体结构;随着Fe掺杂量的增加,样品的介电常数表现出较好的稳定性,介电损耗略有减小,且基本保持在tanδ=0.05以下,其漏电流先增大后减小,且掺杂样品均可得到比较完整的电滞回线.     

关于检查井沉降与解决措施的研究

基于我国检查井施工中出现的不均匀沉降及相关施工问题的实际情况,针对导致上述问题出现的各方面原因进行分析,就优化设计、规范开挖及回填施工、强化检查井的砌筑等方面提出了相应解决措施.以期为我国市政管线建设中的检查井设计及施工提供借鉴.     

Feasibility study on buoyancy–weight ratios of a submerged floating tunnel prototype subjected to hydrodynamic loads

The research progress of a novel traffic solution,a submerged floating tunnel(SFT),is reviewed in terms of a study approach and loading scenario.Among existing publications,the buoyancy-weight ratio(BWR) is usually predefined.However,BWR is a critical structural parameter that tremendously affects the dynamic behaviour of not only the tunnel tube itself but also the cable system.In the context of a SFT prototype(SFTP) project in Qiandao Lake(Zhejiang Province,China),the importance of BWR is illustrated by finite element analysis and subsequently,an optimized BWR is proposed within a reasonable range in the present study.In the numerical model,structural damping is identified to be of importance.Rayleigh damping and the corresponding Rayleigh coefficients are attained through a sensitivity study,which shows that the adopted damping ratios are fairly suitable for SFTP.Lastly,the human sense of security is considered by quantifying the comfort index,which helps further optimize BWR in the SFTP structural parameter design.     

Polypyrrole Shell@3D‐Ni Metal Core Structured Electrodes for High‐Performance Supercapacitors

Three‐dimensional (3D) nanometal films serving as current collectors have attracted much interest recently owing to their promising application in high‐performance supercapacitors. In the process of the electrochemical reaction, the 3D structure can provide a short diffusion path for fast ion transport, and the highly conductive nanometal may serve as a backbone for facile electron transfer. In this work, a novel polypyrrole (PPy) shell@3D‐Ni‐core composite is developed to enhance the electrochemical performance of conventional PPy. With the introduction of a Ni metal core, the as‐prepared material exhibits a high specific capacitance (726 F g^?1 at a charge/discharge rate of 1 A g^?1), good rate capability (a decay of 33 % in C_sp with charge/discharge rates increasing from 1 to 20 A g^?1), and high cycle stability (only a small decrease of 4.2 % in C_sp after 1000 cycles at a scan rate of 100 mV s^?1). Furthermore, an aqueous symmetric supercapacitor device is fabricated by using the as‐prepared composite as electrodes; the device demonstrates a high energy density (≈21.2 Wh kg^?1) and superior long‐term cycle ability (only 4.4 % and 18.6 % loss in C_sp after 2000 and 5000 cycles, respectively).     

Bimetallic Covalent Organic Frameworks for Constructing Multifunctional Electrocatalyst

Covalent organic frameworks (COFs) are a new class of crystalline porous polymers comprised mainly of carbon atoms, and are versatile for the integration of heteroatoms such as B, O, and N into the skeletons. The designable structure and abundant composition render COFs useful as precursors for heteroatom-doped porous carbons for energy storage and conversion. Herein, we describe a multifunctional electrochemical catalyst obtained through pyrolysis of a bimetallic COF. The catalyst possesses hierarchical pores and abundant iron and cobalt nanoparticles embedded with standing carbon layers. By integrating these features, the catalyst exhibits excellent electrochemical catalytic activity in the oxygen reduction reaction (ORR), with a 50 mV positive half-wave potential, a higher limited diffusion current density, and a much smaller Tafel slope than a Pt-C catalyst. Moreover, the catalyst displays superior electrochemical performance toward the hydrogen evolution reaction (HER), with overpotentials of −0.26 V and −0.33 V in acidic and alkaline aqueous solution, respectively, at a current density of 10 mA cm⁻². The overpotential in the catalysis of the oxygen evolution reaction (OER) was 1.59 V at the same current density.