Observation of β-Relaxation in Sub-Tg Isothermally Annealed Al-Based Metallic Glasses

Al85Ni5 Y8Ca2 and Al88Ni5 Y6Co2Fe2 metallic glasses are fabricated by melt spinning. A kink or a small exothermic peak is observed for both the samples isothermally annealed at sub-glass transition temperatures. Temperature modulated differential scanning calorimetry （TMDSC） data disapprove amorphous phase separation. The activation energies derived from Kissinger plots of the exothermic process on DSC curve around glass transition temperature are consistent with those of β-relaxation of metallic glasses.     

退火对表面纳米化纯钛热稳定性的影响

采用表面机械研磨技术实现纯钛材料表面纳米化,并研究了纳米化处理后的材料表层组织结构,详细分析了样品表层纳米晶组织在不同温度、不同时间退火后的热稳定性.结果表明:纯钛TA2经过表面机械研磨处理后可以在表面形成等轴且取向随机的纳米晶层,晶粒尺寸约为12nm.对表面纳米化样品退火后发现,表层纳米晶组织在773 K以下温度退火后具有良好的热稳定性,晶粒尺寸没有明显增大;在773 K温度退火150min后晶粒尺寸稍有增大,而在773 K温度退火240min后晶粒尺寸明显增大,且横截面显微硬度也比表面纳米化后未退火样品显著下降,良好的热稳定性消失.     

强磁场对半无限Al/Cu固液扩散偶凝固组织的影响

采用半无限Al/Cu扩散偶法,对磁场下Al-Cu合金凝固组织进行研究.结果表明:由于沿扩散方向Cu原子分数逐渐减小,凝固时,沿凝固方向依次生成α-Al胞/枝状晶等组织、Al-Al2Cu共晶组织和Al2Cu过共晶组织;在不同磁感应强度下(0～12 T),各组织发生了明显变化,胞状晶消失,枝晶粗化并发生偏转;共晶组织层间距与磁感应强度呈非线性关系,组织被扭曲;过共晶组织界面形貌变平整;Cu原子扩散距离缩短.利用XRD对α-Al枝晶区进行衍射分析,发现磁场下α-Al(100)晶面峰值强度变弱,(111)晶面变强.理论分析认为,强磁场对熔体流动的抑制作用和磁场下晶体的磁各向异性是导致上述现象的主要原因...     

块状铁基α″-Fe_(16)N_2磁性材料的制备

采用气固反应法制备出α″-Fe16N2相含量较高的块状铁基磁性材料,对材料的结构和磁性能进行了研究.采用X射线衍射、横截面显微组织观察及振动磁强计作为主要检测手段,检测不同处理方法所获得的样品中α″-Fe16N2相的含量、相变情况及磁性能.测试结果表明,气固反应渗氮及退火、淬火、回火这一过程中会获得α″-Fe16N2相较高的铁基磁性材料.当回火温度为150℃、时间为4.5 h时,试样中α″-Fe16N2相的质量分数最大,达到50.57%,其饱和磁极化强度高达223.6 A·m2/kg,明显优于α-Fe(N)相和γ'-Fe4N相.     

氮化铁材料的金刚石可切削性实验研究

为解决单晶金刚石切削黑色金属时产生严重磨损这一制造领域难题,对工件表面改性方法进行了深入研究,并探索了新的金刚石可切削材料.对有限厚度的纯铁进行了气体渗氮,并用X射线衍射分析法对渗层进行了物相表征.渗氮纯铁的金刚石可切削性实验结果表明,以氮化铁为主要成分的化合物是一种适于镜面加工的潜在材料(Ra10,nm);在此研究基础之上,提出了整体单相可控氮化铁粉末冶金钢这一新型模具材料,初步切削实验证明其具有较好的金刚石可切削性,后刀面磨损VB值仅为1.16,μm.