预处理条件对Zn/Al-CLM的丙烷芳构化性能的影响

在脉冲微反装置上考察了不同的预处理条件对Zn/Al-CLM催化剂的丙烷芳构化反应的影响。结果表明，丙烷在Zn/Al-CLM催化剂上具有一定的的反应活性和芳烃选择性，而且芳构化主要转化为苯；载体Al-CLM的焙烧温度、金属锌负载量、活化温度等对Zn/Al-CLM催化剂的丙烷芳构化性能具有重要影响。载体经500℃预焙烧制备的Zn/Al-CLM催化剂具有最好的柱结构保留度，从而表现出最佳的芳构化性能；随着锌含量的增加，Zn/Al-CLM催化剂的酸量增大，从而使丙烷转化率增大，而选择性则是锌含量质量分数为5．8％时具有极大值；400℃活化处理可使Zn与Al-CLM之间具有适中的相互作用，从而使得Zn/Al-CLM具有较高的芳烃收率。     

Chemical synthesis and firefly luciferase produced dehydroluciferyl-coenzyme A

Dehydroluciferyl-coenzyme A (L-CoA) was chemically synthesized and characterized by MS, UV-vis spectrometry and RP-HPLC. The identity of the chemically synthesized compound with the one that was produced by firefly luciferase was confirmed. Moreover, the reversibility of the enzymatic conversion of dehydroluciferin ? dehydroluciferyl-adenylate ? L-CoA was also confirmed. The chemical synthesis of L-CoA, described here, may help the clarification of the activator effect of CoA on luciferase bioluminescent assays, in which the enzyme catalyzed formation of L-CoA and the consequent destruction of L-AMP is one of the possible explanations for that effect.     

微波合成铝掺杂钻酸锂材料及性能研究

以LiOH·H2O，Al2O3和Co3O4为原料，微波加热合成Li离子电池正极材料LiAlxCo（1-x）O2．通过XRD测试表征了不同Al加入量时合成产物的晶体结构，确定当x≤0．4时，产物为单一相层状结构．计算了不同x时LiAlxCo（1-x）O2的晶胞参数，随着x的增大，a值减小，c值增大．对合成LiAlxCo（1-x）O2样品进行DSC—TGA测试，结果表明，当x不同时，合成样品的热稳定性不同．SEM测试表明，合成晶体粒度较均匀，粒径在5μm左右．电化学测试表明，LiAl0.2Co0.8O2的电化学性能最好，首次循环放电容量为127mAh／g，多次循环容量损失率小于LiCoO2．     

Shot noise sets the limit of quantification in electrochemical measurements

Detection of single molecules, particles, and rapid redox events is a challenge of electrochemical investigations and requires either an amplification strategy or significant averaging for the electrochemical current to exceed the noise level. We consider the minimum number of electrons required to reach the limit of quantification in these electrochemical measurements. A survey of the literature indicates that the state-of-the-art limit in current detection for different types of measurements (e.g. voltammetry, single-molecule redox cycling, ion channel recordings of single molecules, metal nanoparticle collision, and phase nucleation) is independent of the nature of the measurement and increases linearly with reciprocal response time, Δt^?1, over ～5 orders of magnitude (from ～10 to ～10⁶ s^?1). We demonstrate that the practical limit of quantification requires cumulative measurement of ～2100 electrons during Δt and is determined by statistics of counting electrons, that is, the shot noise in the current.     

V_2O_5/C催化氧化乙二醛制备乙醛酸

利用等体积浸渍法制备了V2O5/C催化剂,并应用于乙二醛的液相氧化反应,采用XRD、TEM手段对催化剂进行了物化性质表征.结果表明,V2O5/C对乙二醛的氧化表现出较高的催化活性和乙醛酸选择性,反应10h,乙二醛的转化率达29.2%,乙醛酸得率13.6%.与贵金属Pd-Bi/C催化剂相比,V2O5/C催化剂的稳定性和重复使用效果都比较好.     

生物体系中电子转移机理的研究Ⅱ: 分子间电子转移及 电子供、受体间不同基 团的影响

利用自编程序MOPAC-ET中AM1方法,及KT(Koopman'sTheorem)法,研究了二苯负离子体系的分子间电子转移现象,计算了其电子供、受体在不同距离下的V~A~B及它们之间的相关性,另外,还对两苯环间不同介入基团对电子转移的影响做了初步研究,发现不同的介入基团存在着较大的差异。     

The effect of annealing on the subsequent cold crystallization of amorphous poly(ethylene terephthalate)

Amorphous poly(ethylene terephthalate) was annealed at temperatures around the glass transition temperature and then heated up in differential scanning calorimeter at 20 °C min⁻¹. It was found that the annealing favored the subsequent cold crystallization and this effect became stronger with increasing annealing temperature. The experimental results were explained by considering the structural change during the annealing.     

Nation-Teflon bimembrane-supported palladium catalysts for Suzuki coupling reactions

Nation-Teflon bimembrane was used as an efficient support for the preparation and application of heterogeneous palladium catalysts.The supported palladium catalysts exhibit high activity and stability in the Suzuki cross-coupling of aryl bromides with arylboronic acids to afford the corresponding biaryls in good to excellent yields,and can be readily recovered and reused several times without significant loss of activity.     

N-TiO2/ZnO复合纳米管阵列的掺杂机理及其光催化活性

以ZnO纳米柱阵列为模板, 采用溶胶-凝胶法制备出TiO2/ZnO和N掺杂TiO2/ZnO的复合纳米管阵列. 扫描电镜(SEM)、X射线光电子能谱(XPS)和紫外-可见漫反射吸收光谱(UV-Vis)的结果表明: 两种阵列的纳米管均为六角形结构, 直径约为100 nm, 壁厚约为20 nm; 在N-TiO2/ZnO复合纳米管阵列中, 掺入的N离子主要是以N-Ox、N-C和N-N的形式化学吸附在纳米管表面, 仅有少量的N离子以取代式掺杂的方式占据TiO2晶格O的位置; 表面N物种形成的表面态能级和取代式掺杂导致带隙的窄化, 增强了纳米管阵列的光吸收效率, 促进了光生载流子的分离. 光催化实验结果表明, N离子的掺杂有利于N-TiO2/ZnO复合纳米管阵列光催化活性的提高.     

高比表面积窄孔分布氧化铝的制备研究 Ⅰ.沉淀条件的影响

 以硫酸铝液为原料，以氨水、氢氧化钠和铝酸钠为碱沉淀剂，采用pH摆动法制备了高比表面积、大孔径、窄孔分布、大孔体积氧化铝，考察了沉淀剂、沉淀温度及沉淀时酸侧pH值对氧化铝物性的影响，并对pH摆动法与等pH沉淀法的结果进行了比较．结果表明，通过改变制备参数可以获得高比表面积、大孔体积的氧化铝，当沉淀温度为70℃，pH摆动3或4次时，氧化铝的孔体积可高达1．0ml／g，比表面积仍大于300m2／g．用pH摆动法制得的样品比用等pH沉淀法制得的样品容易酸溶，对挤压成型有利．不同样品在酸溶液中的分散性表明，用氨水沉淀剂可获得相对较小的沉淀粒子．改变沉淀时酸侧的pH值，可导致沉淀粒子的结构发生变化．