ZrxTixAl1-2xO2的制备及其在三效催化剂上的应用

Zr_0.5Ti_0.5O₂(ZT) and Zr_0.25Ti_0.25Al_0.5O₂(ZTA) mixed oxides were prepared by co-precipitation method and characterized by low temperature adsorption-desorption， XRD and NH₃-TPD. The activity of Pt/Zr_0.5Ti_0.5O₂ and Pt/ Zr_0.5Ti_0.5Al_0.5O₂ catalysts was evaluated using the simulated gases. The results show that ZTA samples exhibit higher specific surface area， larger pore volume and proper surface acidic amount and acidity in comparison with ZT. The results of the catalytic test indicate that Pt/ZT and Pt/ZTA catalysts exhibit excellent low-temperature catalytic activity and lower light-off temperatures of hydrocarbon， carbon monoxide and nitrogen oxides， especially better conversion for nitrogen oxides (NO_x). The addition of Al₂O₃ into ZT enhanced the anti-aging property of Pt/ ZTA catalysts due to the excellent textural， structural， surface acidity and thermal stability.     

新型蒈酸基双酰肼化合物的合成及其生物活性

先将3-蒈烯分子中的碳碳双键氧化开环制得蒈酮酸，再将羰基还原成亚甲基得到蒈酸，酰氯化后与系列酰肼发生N-酰化反应合成了14个新型蒈酸基双酰肼化合物(5a～5n)，其结构经UV-Vis、¹H NMR、¹³C NMR、 FT-IR和MS(ESI)表征，并测试了目标化合物的抑菌和除草活性。结果显示：在用药量为50 μg·mL^-1时，目标化合物对花生褐斑病菌、小麦赤霉病菌、黄瓜枯萎病菌、苹果轮纹病菌、番茄早疫病菌、玉米小斑病菌、西瓜炭疽病菌以及水稻纹枯病菌等8种植物病原菌具有一定的抑制活性，其中化合物蒈酸基α-噻吩甲酰肼5f（R=α-thiophene）对苹果轮纹病菌的抑制率达85.0%，优于阳性对照百菌清。在用药量为100 μg·mL^-1时，化合物蒈酸基3′,4′-二甲氧基苯甲酰肼5j(R=3′,4′-OMe-Ph)、蒈酸基-m-甲氧基苯甲酰肼5d(R=m-OMe-Ph)、蒈酸基-m-甲基苯甲酰肼5b(R=m-Me-Ph)和蒈酸基苯甲酰肼5a(R=Ph)对油菜胚根生长的抑制率分别为88.5%、 86.1%、 85.1%和82.6%（均为A级活性水平），优于阳性对照丙炔氟草胺。     

1-苯基-3-甲基-4-(6-氢-4-甲基氨基-5-硫杂-2,3-吡嗪)-吡唑啉酮的合成与晶体结构

通过1-苯基-3-甲基-4-氯乙酰基-吡唑啉酮-5 (PMCP) 和4-甲基氨基硫脲 (MTSC) 缩合, 形成了一种新的双杂环化合物 (PMCP-MTSC)。利用元素分析与单晶X-射线衍射进行了表征。 该化合物(C14H15N5OS)属单斜晶系, P21 空间群, 晶体学参数为 a = 7.634(1), b = 11.639(2), c = 8.150(2) ? ?= 98.13(1), V = 716.9(2) ?, Z = 2, Dc = 1.396 g/cm3, (MoKa) = 0.232 mm-1, F(000) = 316, Mr = 301.37。结构由直接法解出,共收集3114个衍射点,其中I > 2(I)的独立衍射点有2453个,用全矩阵最小二乘法修正,最终偏离因子:R = 0.0294, wR = 0.0738。结构分析表明: 该化合物以酮式存在,分子间通过氢键作用(N(5)H…O)连接起来并形成一维链状结构。     

全氟烷基磺酸酯C-O键断裂的同面SN2反应

用密度泛函理论研究了CF3SO3CF2CF3 F^-的碳氧键断裂反应的机理。首先，用DFT方法优化了反应物、中间体、过渡态、产物的平衡构型，分析了碳氧键断裂反应的势能面变化，发现在SN2反应机理中，除了S-O断裂SN2反应外，引起C-O键断裂的同面进攻也是一个可能的反应途径。理论计算表明，最终反应的产物是受热力学控制的，S-O键的断裂绝对地优于C-O的断裂。因此，C-O断裂的同面机理虽然是可能的，但却难以被实验观察到，本文还讨论了端基-CF3在同面SN2反应中的邻位效应，以及基组对这个效应的影响。     

PREPARATION OF MICROGEL-EPOXY RESIN TWO-PHASE POLYMERS BY IN SITU POLYMERIZATION~*

Microgel-epoxy resin two-phase polymers were prepared by in situ copolymerization of ethylenic monomers with unsaturated polyesters. The choice of monomers and the effect of monomer concentration on microgel particle size were discussed. Agglomeration of particles played a significant role in the early stage of polymerization. The microgel dispersion in epoxy resin was stable after the finish of polymerization. Upon curing the particles remained well dispersed.     

Dawson结构钼钒磷杂多化合物对苯酚过氧化氢羟化作用的研究

Ｄａｗｓｏｎ结构钼钒磷杂多化合物对苯酚过氧化氢羟化作用的研究于剑锋，杨宇，吴通好，孙家锺（吉林大学化学系理论化学研究所，长春，１３００２３）关键词Ｄａｗｓｏｎ结构钼钒磷杂多化合物，苯酚羟化，过氧化氢苯二酚（ＤＢＨ）是重要的化工原料．由芳香化合物羟化制...     

辐照对聚己内酯结构和性能的影响

研究了γ 辐照对不同分子量的聚己内酯 (PCL)的力学性能、热性能、结晶行为的影响 ,在此基础上 ,研究了辐射交联后的PCL的形状记忆行为 .研究结果表明 ,PCL的分子量越大 ,辐射交联所需的凝胶化剂量越低 .溶胶分数S +S1 2 与 1 D的关系很好地符合Charlesby Pinner关系式 ,说明PCL的辐射交联属于无规交联 .剂量对PCL的力学性能影响显著 ,剂量越大 ,抗张强度和断裂伸长率下降越多 ,但分子量较高的PCL的抗张强度受剂量的影响较小 .DMA分析表明 ,聚己内酯辐照交联后的弹性模量和耐热性能显著提高 .交联度较高的PCL表现出高弹态 ,可以拉伸 ,并具有较好的形状记忆行为 .DSC分析表明 ,辐射交联使PCL的结晶度有所增加 ,但也使结晶熔点有所降低     

A New and Efficient Synthetic Method and Antibacterial Activities of Oxazolidinone Analogues

A series of novel oxazolidinone analogues were prepared by a new and efficient synthetic method and their antibacterial activities were determined. These compounds wer echaracterized by LC-MS and ^1H NMR.     

微波合成铝掺杂钻酸锂材料及性能研究

以LiOH·H2O，Al2O3和Co3O4为原料，微波加热合成Li离子电池正极材料LiAlxCo（1-x）O2．通过XRD测试表征了不同Al加入量时合成产物的晶体结构，确定当x≤0．4时，产物为单一相层状结构．计算了不同x时LiAlxCo（1-x）O2的晶胞参数，随着x的增大，a值减小，c值增大．对合成LiAlxCo（1-x）O2样品进行DSC—TGA测试，结果表明，当x不同时，合成样品的热稳定性不同．SEM测试表明，合成晶体粒度较均匀，粒径在5μm左右．电化学测试表明，LiAl0.2Co0.8O2的电化学性能最好，首次循环放电容量为127mAh／g，多次循环容量损失率小于LiCoO2．     

丁二烯催化环化三聚中多金属的协同效应

研究了第二过渡金属化合物对ＴｉＣｌ４／ＡｌｅＴ１．４６ｃＬ１．５４催化丁二烯环化三聚的多金属协同效应。结果表明，极少量的第二过渡金属化合物，如Ｃｒ，（ａｃａｃ）３，Ｍｎ（ａｃａｃ）３，ＮｉＣｌ２，ＺｒＣｌ４等加入ＴｉＣｌ４／ＡｌＥｔ１．４６Ｃｌ１．５４体系后不同程度地提高了丁二烯环化三聚的选择性，并改变了体系的最大速率和催化剂效率。