TEOS-MTES基SiO2溶胶微结构的SAXS研究

正硅酸乙酯(TEOS)为前驱体,在碱性条件下制备含有无定形SiO2颗粒的溶胶,以甲基三乙氧基硅烷(MTES)在酸性条件下获得聚甲基硅氧链,二者混合后应用同步辐射X射线进行混合溶胶的SAXS散射强度测定,计算了溶胶的平均回转半径、平均粒径、两相界面层厚度、散射体体积分数、两相间比表面积等参数,辅以光子相关光谱法(PCS)和透射电子显微镜(TEM)观测溶胶粒度,证实SiO2颗粒被MTES混合物连接成族团.实验发现所测混合溶胶样品均表现出对Porod定理的负偏离,说明溶胶中颗粒与溶剂之间存在很明显的两相间界面层.     

聚酰亚胺中空纤维膜用于甲醇/甲基叔丁基醚的分离

甲醇／甲基叔丁基醚混合物的膜法分离，大多采用渗透汽化方法，少有采用蒸汽渗透法。用聚酰亚胺中空纤维膜，对以蒸汽渗透和渗透汽化两种方式分离甲醇／甲基叔丁基醚混合物（甲醇质量分数为0．01－0．30）的效果进行了对比。结果显示，在甲醇质量分数低于0．05时，蒸汽渗透较渗透汽化法的分离性能优越。     

Preliminary study of trace elements in human brain tumor tissues by instrumental neutron activation analysis

Elemental profiles of brain tumor tissues from 15 patients of astrocytomas (grade I–III) and normal human brain tissues of 23 male age matched autopsies as controls have been studied by instrumental neutron activation analysis. The SLOWPOKE reactor with a thermal neutron flux of 8·10¹¹n·cm^–2·s^–1 and swimming pool type reactor with a thermal neutron flux of 1·10¹³n·cm^–2·s^–1 were used for short and long irradiation of samples, respectively. Spectrophotometry was only used for analyzing phosphorus. A total of 18 elements Se, Na, K, Br, Cl, Mn, Mg, S, Ca, Cu, Hg, Cr, Fe, Rb, Zn, Co, Sc and P has been determined for this purpose. The reliability of methods has been checked by analyzing biological standard reference materials horse kidney (IAEA H-8) and bovine liver (NBS SRM 1577a). The analytical results showed that compared with the normal brain tissues, concentrations of Ca, Fe, Cu, Zn, Se, Mn, Br and Sc were significantly higher in tumor tissues (P<0.01) and concentrations of Rb, K and P were lower, while no differences for contents of Mg, S, Cr, Hg, Na and Cl were observed. A negative correlation between P and Ca in malignant and normal brain tissues was observed.     

Synthesis and Crystal Structure of Complex of Sodium Perrhenate with Tetraethyl p-tert-Butylcalix[4]arene Tetraacetate

Recently,theconformationofthecalixarenehasbeenshowntobeimportantincontrollingtheseIectivityofthereceptor.Forexample,sodiumioncouldbeboundverystronglybyesterderivativesofcalix[4]areneintheconeconformationl.Wehavefoundthatinthepresenceofcertainamountofsodiumion,microamountofReO4-canbequantitativelyextractedintol,2-dichloroethanebytheligandtetraethylp-tert-butylcalix[4]arenetetraacetate(L).ItshowsthatthepresenceofNa inaqueoussolutioncanpromotetheformationofhydrophobiccomplex[NaL] .ReO'-whichc…     

草莓型SiO2/PMMA纳米复合微球的制备

在纳米二氧化硅水分散体系中,借助于碱性辅助单体1-乙烯基咪唑(1-VID)与未改性纳米二氧化硅表面羟基之间的酸-碱作用,通过1-VID与甲基丙烯酸甲酯(MMA)的自由基共聚合,制备了草莓型的SiO2/PMMA复合微球.整个反应过程中,纳米二氧化硅无需表面处理,体系中无需另外加入乳化剂或助乳化剂,微球表面吸附的纳米二氧化硅对颗粒起稳定作用.用动态光散射粒度分布仪测得复合微球粒径在120-330nm之间,热重分析结果表明,复合微球中二氧化硅含量介于15%-20%之间.透射电镜和扫描电镜显示所得复合微球具有草莓型结构,二氧化硅富集在表面.     

PREPARATION AND SWELLING PROPERTIES OF SUPER-ABSORBENT POLYMER

A super-absorbent polymer is prepared by graft polymerizing acrylamide (AM) ontopotato starch using ceric ammonium nitrate (CAN) and N, N′-methylene-bis-acrylamide(bisAM) as an initiator and cross-linking agent respectively, and then subjecting the potatostarch-poly(acrylamide) (PAM) graft copolymer (SPAM ) to alkaline saponification. Thewater absorbency (WA) of the sample is nearly 5000 g H_2O/g for dry sample in 24 hat room temperature and is far larger than that of reported in the literature. Thevariables affecting the WA were investigated and optimized, they were: concentrations ofpotato starch, AM, CAN and bisAM were 26.3 g/L, 1.14 mol/L, 10.3 mmol/L and 0.53mmol/L, respectively. The amount of sodium hydroxide was 15 g and the temperatures ofgraft copolymerization and saponification reactions were 60℃ and 95℃. The time of graftcopolymerization and saponification reactions was 2 h, respectively.     

Synthesis of new 1,3-bis（phenylethynyl）disilazanes

Three new 1,3-bis(phenylethynyl)disilazanes were synthesized from the reaction of 1,3-dichlorodisilazanes with (phenylethy- nyl)lithium,and characterized by infrared (IR) spectra,nuclear magnetic resonance (NMR) and mass spectrometry (MS).     

选择性远程DEPT NMR技术用于萜类生物碱的结构测定

从中草药勒党根茎中分离出二个化合物, 其一为已知的萜类生物碱culamtraramine, 其二为它的差向立体异构体, 为新化合物, 定名为isoculantraramine。用选择性远程核磁共振技术测定了它们的结构。     

Interlayer Energy Transfer from Naphthalene to Anthracene Chromophores Organized in Langmuir—Blodgett Films

Interlayer energy transfer between 2,3-naphthol-10-hexadecylaza-15-crown-5(NC16) and N-[1-(9-methoxyanthryl)] decylaza-15-crown-5(A10C) within multilayer Langmuir-Blodgett films has been studied by steady-state fluorescence spectra. The donor and acceptor could be separated precisely by inserting stearic acid (SA) spacers. The efficiency of the energy transfer increases with the decrease in the donor-acceptor distance by a quadratic manner, suggesting the donor excitations are delocalized in the layer.     

高比表面积介孔网状氧化镁的制备、表征及对废水中Pb(Ⅱ)的吸附性能和机理

以天然水菱镁矿为原料，通过"煅烧-水化-煅烧"的简单方法制备了高比表面积介孔网状MgO，且实验过程中无须加入任何试剂。系统性研究了氧化镁用量、吸附时间、吸附温度及pH对氧化镁吸附模拟废水中铅离子吸附性能的影响，揭示了吸附机理，并考察了氧化镁对多种离子的吸附效果。结果表明：该氧化镁吸附剂具有188 m²·g^-1的高比表面积和0.85 cm³·g^-1的高孔体积，平均孔径为12.33 nm，其吸附动力学和等温线数据与伪二级模型和Langmuir模型高度吻合，表明重金属离子在氧化镁上为单层化学吸附。MgO介孔网状结构表现出对Pb（Ⅱ）的高吸附性能，最大吸附量为7 431.5 mg·g^-1，该数值远高于其他报道的基于MgO吸附剂的数值，铅去除率高达99.8%以上。介孔网状MgO的吸附机理主要是羟基官能团以及Mg（Ⅱ）与MgO表面重金属离子之间的离子交换所致。另外，该氧化镁可同时吸附多种离子，对Cd、Cr、Ni、As、Co、P、Se、Be、Bi、Cu、Fe、Mn、V、Zn、Al离子均具有优异的吸附性能。