两个包含醚氧桥联三羧酸配体的锌(Ⅱ)配位聚合物的合成、晶体结构及荧光性质

选用2种醚氧桥联三羧酸配体(H_3cpta和H_3dbba)和4,4′-联吡啶(4,4′-bipy)或菲咯啉(phen)与ZnCl_2进行水热合成反应,构筑了2个一维链状配位聚合物[Zn(μ-Hcpta)(4,4′-bipy)(H_2O)]_n(1)和{[Zn_3(μ_3-dbba)_2(phen)_3]·6H_2O}_n(2),并对其结构和荧光性质进行了研究。结构分析结果表明2个配合物分别属于单斜晶系,P2_1和I2空间群。配合物1和2具有两种不同的一维链结构。     

SO_4~(2-)/TiO_2固体超强酸新制备方法及其对形成邻苯二甲酸二丁酯的催化活性

建立了用钛白粉制备固体超强酸SO42-/TiO2的新方法.考察了超强酸SO42-/TiO2的制备条件对催化邻苯二甲酸酐和正丁醇酯化反应的催化活性的影响.实验表明,以合成的超强酸为催化剂,在160℃反应4h,邻苯二甲酸二丁酯的产率大于99%.     

Determination of 6-Mercaptopurine in Rat Blood by Microdialysis Coupled with High Performance Liquid Chromatography on a Functionalized Multi-wall Carbon Nanotubes Modified Electrode

Introduction Sincecarbonnanotubeswerediscoveredin 1991,theyhaveattractedmuchattentionbecause oftheirremarkablenanostructureswithhighsur- facearea,highelectricalconductivity,goodchemi- calstabilityandsignificantmechanicalstrength[1]. Reportshavealreadybeenpublishedonthecata- lyst[2],nanoscaleelectronicandmechanicalsys- tems[3],andscannedprobemicroscopesandelec- tronfieldemissiontips[4].Itwasreportedthatcar- bonnanotubescouldbemadeintocarbonnan- otubeselectrodesandhavebeensuccessfullyused intheo…     

PEO-LiClO_4-ZSM5 composite polymer electrolyte (IV): Polarized optical microscopy study

All solid-state lithium polymer batteries may be one of the best choices for the future electrochemical power source, characterized by high energy densities, good cyclability, reliability and safety[1,2]. Owing to its potential capability to replace the t…     

载钛催化剂的气固相法制备及其在环氧化氯丙烯反应中的催化活性

利用TiCl4气固相法,以含硅物质为原料,制备了7种钛硅氧化物类催化剂,并考察了其在H2O2环氧化氯丙烯反应中的催化活性。实验结果表明：只有以HZSM-5为载体制备的催化剂具有催化环氧化活性。酸处理HZSM-5对催化剂活性的影响并不大,分子筛的硅铝比和气固相反应时间是影响其催化活性的重要因素,且催化活性随着硅铝比的降低而降低。气固相反应时间16h时,催化剂的活性最高。     

固相萃取高效液相色谱-质谱法测定动物组织中硝基呋喃代谢产物

研究了对动物组织中4种硝基呋喃类代谢产物AOZ、AMOZ、SEM和AHD的自动固相萃取HPLC-MS分析方法，分别以2-氯苯甲醛和2-硝基苯甲醛作为衍生化试剂，分别用AMOZ-d5、AOZ-d4作内标，用ENSPE柱进行提取，以乙腈-0．1％甲酸为流动相，采用梯度洗脱，可在15min内将4种代谢产物完全分离并进行测定。回收率为85％-90％；检出限可达0．5μg／kg。采用两种衍生化方法可获得较多的定性确证信息。采用本方法研究了硝基呋喃在鸡饲养过程中的残留规律。     

BaCe0.8Ho0.2O3-a陶瓷的性质与应用

Ceramic BaCe0.8Ho0.2O3-α with orthorhombic perovskite structure was prepared by conventional solid state reaction, and its conductivity and ionic transport number were measured by ac impedance spectroscopy and gas concentration cell methods in the temperature range of 600-1000 ℃ in wet hydrogen and wet air, respectively. Using the ceramics as solid electrolyte and porous platinum as electrodes, the hydrogen-air fuel cell was constructed, and the cell performance at temperature from 600-1000 ℃ was examined. The results indicate that the specimen was a pure protonic conductor with the protonic transport number of 1 at temperature from 600-900 ℃ in wet hydrogen, a mixed conductor of proton and electron with the protonic transport number of 0.99 at 1000 ℃. The electronic conduction could be neglected in this case, thus the total conductivity in wet hydrogen was approximately regarded as protonic conductivity. In wet air, the specimen was a mixed conductor of proton, oxide ion and electron hole. The protonic transport numbers were 0.01-0.09, and the oxide-ionic transport numbers were 0.27-0.32. The oxide ionic conductivity was increased with the increase of temperature, but the protonic conductivity displayed a maximum at 900 ℃, due to the combined increase in mobility and depletion of the carriers. The fuel cell could work stably. At 1000 ℃, the maximum short-circuit current density and power output density were 346 mA/cm^2 and 80 mW/cm^2, respectively.     

苯乙烯/甲基丙烯酸和苯乙烯/甲基丙烯酸(β-羟丙酯)嵌段共聚物的表面动态行为

通过测定表面动态接触角研究了两亲性的苯乙烯／甲基丙烯酸嵌段共聚物（ＰＳ ｂ ＰＭＡＡ）和苯乙烯／甲基丙烯酸（β 羟丙酯）嵌段共聚物（ＰＳ ｂ ＰＨＰＭＡ）的表面动态行为及温度、嵌段长度比等因素对其值的影响,讨论了聚合物表面当接触介质改变时链段或基团的再取向行为和表面性质     

溶胶-凝胶法制备丙烯酸甲酯-衣康酸酐共聚物/SiO_2杂化材料

以丙烯酸甲酯（ ＭＡ） 和衣康酸酐（Ｉｔｎ） 的无规共聚物和原硅酸四乙酯（ＴＥＯＳ） 作为有机相与无机相前驱体,以３ 氨丙基三乙氧基硅烷（ＡＰＴＥＳ） 为偶联剂,通过溶胶 凝胶过程制备出有机 无机杂化材料．并通过ＳＥＭ、ＤＳＣ 等方法考查了偶联剂用量对所得材料结构及性能的影响．     

CH4,CO2和O2制合成气反应中载体对Ni催化剂抗氧化性能的影响

在ＣＨ４、ＣＯ２ 催化氧化制合成气反应中, Ｎｉ／Ａｌ２Ｏ３ 催化剂在高温下生成ＮｉＡｌ２Ｏ４ 尖晶石,是导致催化剂失活的一个重要因素． 通过向载体（Ａｌ２Ｏ３）中添加各种氧化物, 使得催化剂的抗氧化性能得到改善． 并运用ＴＰＲ、ＸＲＤ对催化剂进行表征, 发现催化剂的抗氧化性顺序为： Ｎｉ／ＣａＯ－Ａｌ２Ｏ３ ＞ Ｎｉ／ＭｇＯ－Ａｌ２Ｏ３ ＞ Ｎｉ／ＣｅＯ２－Ａｌ２Ｏ３ ＞ Ｎｉ／Ｌａ２Ｏ３－Ａｌ２Ｏ３ ＞ Ｎｉ／Ｙ２Ｏ３－Ａｌ２Ｏ３ ＞ Ｎｉ／ＴｉＯ２－Ａｌ２Ｏ３＞ Ｎｉ／Ａｌ２Ｏ３＞ Ｎｉ／Ｆｅ２Ｏ３－Ａｌ２Ｏ３．