以谷氨酸氟硼酸(GluBF₄)离子液体水溶液为反应介质,以物质的量比为1:6的二水合醋酸锌[Zn(Ac)₂·2H₂O]和氢氧化钠为原料,室温下制备前驱体,再微波辅助加热制备了纳米氧化锌粉体,获得了纳米结构微米尺寸纳米ZnO绒球.利用场发射扫描电镜(FESEM)、X射线衍射(XRD)、比表面(BET)、能量色散谱(EDS)等对产物进行了表征.所得产物为六方晶系纤锌矿结构,粉体粒径20.4 nm,绒球比表面积为28.3 m²·g^-1,产物纯度较高,收率95.3%.同时探讨了纳米ZnO绒球生成的可能机理.该纳米材料在日光下显示较高的光催化活性和稳定性.分别配制浓度为10 mg·L^-1的100 mL甲基橙(MO)和甲基紫(MV)水溶液, 30 mg纳米氧化锌为光催化降解催化剂,太阳光激发下5 h脱色率分别达到74.3%和96.9%;溶液总有机碳(TOC)含量随光降解的进行缓慢下降;光催化剂重复利用5次,催化剂形貌不变、颜色不变,质量基本未发生变化.     

Cobalt(II)‐Catalyzed C?H Alkynylation/Annulation with Terminal Alkynes: Selective Access to 3‐Methyleneisoindolin‐1‐one

A highly efficient cobalt(II)‐catalyzed alkynylation/annulation of terminal alkynes assisted by an N,O‐bidentate directing group is described. This protocol is characterized by wide substrate scope utilizing cheap cobalt catalysts, and offers a new approach to 3‐methyleneisoindolin‐1‐one, which can be converted into an oxadiazine salt in one step. Moreover, the directing group could be removed in three steps.     

A Novel Zirconium-Based Perovskite-Type Membrane Material for Oxygen Permeation

Zirconia with fluorite structure stabilized by doping rare earth or alkaline earth metal oxides such as Y2O3 and CaO (YSZ and CSZ) is a class of traditional mixed conducting membrane materials, which have been widely investigated for their high oxygen ionic conductivity and excellent chemical and thermal stability1-3. But the electronic conductivity of these materials is very small, unless operated with an internal or external circuitry, the oxygen flux through membranes in usual ranges of …     

Preparation and Structural Defects of Al2-xZrx＋yTi1-yO5 and Al4.54Si1.46O9.73 Multiphase Material

In the study, sludge from the aluminum profile factory and kaolin were used as the raw materials. Through adding ZrO2 mineralizer in different contents, Al2-xZrx+yTi1-yO5 and Al4.54Si1.46O9.73 solid solution multiphase material was prepared to effectively inhibit the decomposition of aluminum titanate solid solution and optimize high temperature property of the multiphase material. With XRD and SEM means, crystalline structure and microstructure of each sample were characterized, and properties of each sample were tested. According to experimental results, the optimal addition amount of ZrO2 mineralizer was determined to be 1.5%. Correspondingly, contents for aluminum titanate solid solution, mullite solid solution and α-Al2O3 were 70.3%, 26.8% and 2.9% respectively, bulk density was 3.20 g/cm3, degree of porosity was 5.57%, water absorption rate was 1.74%, and the once thermal shock rupture strength retention rate was 90.52%.     

液相色谱-串联质谱法检测血清中15种甾体激素的动态变化

建立了用液相色谱-串联质谱检测血清中15种甾体激素的方法。在血清样品中加入含内标的乙腈沉淀蛋白质后,用100 mmol/L盐酸羟胺衍生,经Agilent-C18柱(50 mm×3.0 mm,2.7μm)分离,内标法定量。质谱分析采用电喷雾电离(ESI)正离子扫描,多反应监测(MRM)模式检测。数据显示,13种激素在0.05~20 ng/mL范围内线性关系良好(相关系数(R2)不小于0.995 6),检出限不大于1 ng/mL;皮质醇及脱氢表雄酮硫酸酯在50~2 000ng/mL范围内线性关系良好(R2不小于0.997 9),检出限不大于0.5 ng/mL。将该方法应用于女性月经周期激素变化规律的研究,结果表明,15种甾体激素在一个完整的月经周期内有不同特征的动态变化,其中雄激素在滤泡期的后期达到最高值,孕(雌)激素在黄体期达到最高值,而皮质激素则波动不明显。该方法灵敏度高、重复性好,为临床诊疗提供了参考。     

新的溶胶-凝胶法制备Ge/SiO2量子点玻璃

以3－三氯锗丙酸和正硅酸乙酯为原料,通过水解、缩聚凝胶热处理及氢气反应,在SiO2凝胶玻璃中析出立方相Ge纳米晶,当x=30时,凝胶玻璃中除了析出立方相Ge纳米晶处,还析出六方相GeO2,利用XRD测试了Ge纳米晶的大小,发现随着掺杂量的增加,纳米颗粒粒径从1nm增大到10nm,电子衍射表明镶嵌在SiO2凝交玻璃中的Ge纳米晶为多晶结构。     

官能团转化法制备羧基硅油及其柔软性能研究

用氨值为0．2895mmol/g、－／Mn=52650的氨丙基硅油（APS）与环状二元酸酐如琥珀酸酐（SA）、马来酸酐（MA）、邻苯二甲酸酐（PA）反应得了三种不同羟基烃基的硅油（CAS）,对其结构,性能进行了表征和测定。实验结果表明：三种CAS均能改善聚酯／粘胶纤维织物的柔软弹性,撕裂和断裂强度,但PA改性APS制备的CAS－3硅油,其分子侧链中的邻羧基苯甲酰基对硅油的柔软性能有影响;另外较高分子量的CAS能捉供织物更好的柔软性,而羧值变化对织物的吸湿性,回弹性影响较大,但对织物的柔性影响较小。     

强聚电解质对离子型芘衍生物探针的键合

由于芘单线态寿命长 ,单体态发射光谱精细结构对微环境极性敏感 ,在特定的环境下能形成激基缔合物 ,而且可作为非辐射能量转移过程的受体 ,因而被广泛应用于水溶性聚合物的研究 [1～ 3] .芘微溶于水 ,可以作为自由“探针”加入体系探测环境极性的变化与疏水微区的形成 .而离子型的芘衍生物由于良好的水溶性 ,可以同相反电荷的聚电解质发生静电键合 ,最近已经被用来研究聚电解质多层膜的结构 [4 ] .但是芘的离子衍生物同聚电解质键合的规律还不是十分清楚 ,例如聚电解质的电荷密度和化学结构对键合的影响 ,尤其是键合的化学计量关系 ,这对芘…     

糠醛系氮配位螯合树脂对贵金属元素的吸附性能

呋喃衍生物糠醛与二乙烯三胺反应制得了含有Schiff碱基,胺基及大共轭π键地的氮配位螯合树脂,应用电感耦合等离子体发射光谱研究了所得螯合树脂对贵金属元素Au,Pd,Pt,Rh,Ru,Ir及重金属元素Hg的吸附性能。结果表明,所得螯合树脂在较宽的酸度范围内能很好地吸附Au,Pd,Pt,Rh,Ru元素,具有优良的吸附选择性及较高的富集倍数,特别是对Au能达到定量吸附与洗脱,同时,在一定酸度条件下亦对Pt,Ir及Hg显示良好的吸附性能。     

高表面电荷密度单分散苯乙烯磺酸钠纳米微球的制备

利用无皂乳液聚合 ,在苯乙烯 (St)的反应体系中引入适量的苯乙烯磺酸钠 (NaSS)参加共聚合 ,在聚合过程中分两阶段加料 ,第一阶段中NaSS浓度是决定乳胶粒粒径及单分散性的关键因素。当反应达到较高转化率 ( >90 % )时加入第二阶段单体混合物 ,此阶段中NaSS与St的比例决定了最终胶粒的表面电荷密度。利用上述两阶段无皂乳液聚合法成功地制备了粒径小于 10 0nm、单分散性指数小于 1.0 5以及表面电荷密度大于 3 0 μC·cm-2 的一系列乳胶粒