Investigation of the Effect of Artificial Internal Defects on the Tensile Behavior of Laser Powder Bed Fusion 17–4 Stainless Steel Samples: Simultaneous Tensile Testing and X-Ray Computed Tomography

Experimental Mechanics - Insufficient data are available to fully understand the effects of metal additive manufacturing (AM) defects for widespread adoption of the emerging technology....     

A model for crack formation during active solid pyrolysis of a char-forming solid: crack patterns; surface area generation; volatile mass efflux

A model is developed for the formation and propagation of cracks in a material sample that is heated at its top surface, pyrolyses, and then thermally degrades to form char. In this work the sample is heated uniformly over its entire top surface by a hypothetical flame (a heat source). The pyrolysis mechanism is described by a one-step overall reaction that is dependent nonlinearly on the temperature (Arrhenius form). Stresses develop in response to the thermal degradation of the material by means of a shrinkage strain caused by local mass loss during pyrolysis. When the principal stress exceeds a prescribed threshold value, the material forms a local crack. Cracks are found to generally originate at the surface in response to heating, but occasionally they form in the bulk, away from ever-changing material boundaries. The resulting cracks evolve and form patterns whose characteristics are described. Quantities examined in detail are: the crack spacing in the pyrolysis zone; the crack length evolution; the formation and nature of crack loops which are defined as individual cracks that have joined to form loops that are disconnected from the remaining material; the formation of enhanced pyrolysis area; and the impact of all of the former quantities on mass flux. It is determined that the mass flux from the sample can be greatly enhanced over its nominal (non-cracking) counterpart. The mass efflux profile qualitatively resembles those observed in Cone Calorimeter tests.     

A Multiscale-Porous Anion Exchange Membrane for Convenient and Scalable Electrokinetic Concentration of Cationic Species

A device able to electrokinetically concentrate cationic samples has many potential medical and industrial applications, but until now has remained undeveloped due to the lack of a commercial anion-permselective material leading to a prohibitively complex fabrication procedure. Herein, a novel multiscale-porous anion exchange membrane (MP-AEM) that enables the convenient and scalable electrokinetic concentration of cationic species is proposed. A mechanically enhanced multiscale-porous structure with a solid framework is realized by adopting polyester resin as an additive to overcome the intrinsic limitations of the AEM material. The scalable MP-AEM-embedded electrokinetic concentrator is devised based on the peculiar properties of the MP-AEM that for allow both ion and fluid transport. With the MP-AEM, the concentrator is fabricated in a highly streamlined manner consisting only of a simple insertion and assembly. The concentration performance of the MP-AEM-embedded electrokinetic concentrator is demonstrated with a positively charged fluorescent dye and a fluorescein-labeled protein, and the results show enrichment factors of 250 and 500, respectively. The MP-AEM makes cationic electrokinetic concentration more accessible and scalable, thereby enabling further progress in a wide range of fields.     

Methyl orange degradation enhanced by hydrogen spillover onto platinum nanocatalyst surface

Following a thermal reduction method, platinum nanoparticles were synthesized and stabilized by polyvinylpyrrolidone. The colloidal platinum nanoparticles were stable for more than 3 months. The micrograph analysis unveiled that the colloidal platinum nanoparticles were well dispersed with an average size of 2.53 nm. The sol–gel‐based inverse micelle strategy was applied to synthesize mesoporous iron oxide material. The colloidal platinum nanoparticles were deposited on mesoporous iron oxide through the capillary inclusion method. The small‐angle X‐ray scattering analysis indicated that the dimension of platinum nanoparticles deposited on mesoporous iron oxide (Pt‐Fe₂O₃) was 2.64 nm. X‐ray photoelectron spectroscopy (XPS) data showed that the binding energy on Pt‐Fe₂O₃ surface decreased owing to mesoporous support–nanoparticle interaction. Both colloidal and deposited platinum nanocatalysts improved the degradation of methyl orange under reduction conditions. The activation energy on the deposited platinum nanocatalyst interface (2.66 kJ mol^?1) was significantly lowered compared with the one on the colloidal platinum nanocatalyst interface (40.63 ± 0.53 kJ mol^?1).