三氟化硼引发四氢呋喃聚合的研究——以环氧氯丙烷为促进剂

<正> 四氢呋喃(THF)通过正离子开环聚合而制得的聚丁二醇(PTMG)是生产嵌段聚醚聚氨酯及嵌段聚醚聚酯弹性材料的重要原料。目前制备PTMG所采用的引发剂都是强酸型的,如高氯酸、氟磺酸或发烟硫酸等,对设备腐蚀严重。用酸性较弱的三氟化硼引发聚合在文献上也有一些研究报道,但尚难以采用,其主要困难在于实际应用的     

以有机镍配合物为前体制备担载镍催化剂的研究

描述了以镍单核配合物ＮｉＣｐ２和簇合物Ｎｉ３Ｃｐ３Ｎ－ｔ－Ｃ４Ｈ９为前体的ＳｉＯ２载镍催化剂的制备，通过元素分析、ＴＲＲ、ＴＰＤＥ、ＸＰＳ，ＣＯ吸附和苯加氢反应对以镍配合物和簇合物为前体制备的催化剂的性能及其制备过程了研究和表征。结果表明，镍与合物和簇合物在担载过程中同载体ＳｉＯ２表面发生了相互作用，其化学组成发生了变化，在苯加氢反应中，此催化剂的活性比以Ｎｉ（ＮＯ３）２为前体制备的催化剂高得多，     

四氢呋喃与环氧氯丙烷共聚合的研究

<正> 晃玉等曾以BF_3-二元醇(DO)引发四氢呋喃(THF)与环氧氯丙烷(ECH)共聚合,用所得共聚醚制成嵌段聚醚聚氨酯,与用THF均聚醚或THF-环氧丙烷(PO)共聚醚为软段的聚氨酯相比,分别在低温性能及强度上有明显改进.且由于引入氯甲基侧基可作进一步接枝共聚改性。但用BF_3-DO为引发剂很难制得不含环聚体的共聚醚,     

光同时诱导水中Cr(Ⅵ)的还原与橙黄Ⅱ的氧化

光同时诱导水中Cr(Ⅵ)的还原与橙黄Ⅱ的氧化;染料;橙黄Ⅱ;Cr(Ⅵ);光还原;光降解     

Synthesis, Crystal Structure and Electrochemistry Properties of a (N,N'-Ethylene-bis(salicylaldiminato)) Nickel(Ⅱ) Complex, [Ni2(salen)2]·NCS-NH4

A new Ni(Ⅱ) complex [Ni2(salen)2]·(NCS)·NH4 (salen = N,N'-bis(salicylidenea-mino)ethanato) has been prepared and structurally characterized by elemental analysis, IR spectra and single crystal X-ray diffraction. It crystallizes in the orthorhombic system, space group Pbca with a = 16.8725(13), b = 19.0046(15), c = 20.0583(16) (A), Z = 8, V = 6431.8(9) (A)3, C33H32N6Ni2O4S1, Mr= 726.13, Dc = 1.500 g/cm3, F(000) = 3008, μ = 1.284 mm-1, the final R = 0.0394 and wR = 0.0767 for 4449 observed reflections with Ⅰ＞2σ(Ⅰ). The complex involves a N,N'-ethylene-bis(salicylaldiminato) Schiff base, an isothiocyanato anion and an ammonium cation. The nickle(Ⅱ) ion adopts a distorted square coordination geometry with N2O2 set of Schiff base ligand. The complexes are linked into a dimmer via intermolecular hydrogen bonds and the [Ni(salen)] moieties are connected together to form a 2-D layer structure by intermolecular N-H…O hydrogen bonds and π-π stacking. Cyclic-voltammetry method was used to characterize electrochemically the complex.     

A Home-made Simple Set-up for Measurement of Electrochemical Surface Tension Spectrum on a Mercury Drop Electrode

A setup for recording surface tension curves at a mercury drop during potential scanning is designed based on photo-sensitive detection system. Surface tension spectrum at Hg drop can be recorded by voltammetric study. A Yb(III)-NO2- catalytic reduction system was used for characterization. The simple, sensitive technique can be expected to provide fresh information on molecular interactions at electrode surfaces.     

锂离子电池正极材料LiMn2O4的合成与晶体结构（英）

Spinel LiMn₂O₄ powders were prepared using two-step synthesis method consisting of solid-state reaction method and citrate modified sol-gel method. The effects of the calcination temperature and the Li/Mn ratio of raw materials were studied on the physicochemical and electrochemical properties of the spinel LiMn₂O₄ powders, such as crystallinity, lattice constant and density. The title compound was characterized by powder X-ray diffraction (XRD), scanning electron microscopy (SEM) and transmission electron microscopy (TEM). Polycrystalline LiMn₂O₄ powers calcined at 750 ℃ were found to be composed of very uniformly-sized microcrystal with an average particle size of 300 nm. The improvement in electrochemical properties was mainly attributed to the process of re-grinding by absolute alcohol.     

三氟化硼引发四氢呋喃聚合的研究——Ⅳ.1,4-丁二醇的影响

前报中已证明用三氟化硼-环氧氯丙烷(ECH)引发四氢呋喃(THF)聚合具有较高的引发效率,并对在Ac_2O、水和无水存在下的聚合反应进行了研究。本文报道1,4-丁二醇(BG)对BF_3引发THF聚合反应的影响。通常认为在BG存在下,BF_3是不能引发THF聚合的,但本工作证明BG是有效的分子量调节剂,制备分子量在     

肝素化聚甲基硅氧烷-聚氧乙烯接枝物的合成及其体外抗凝血性能评价

以二甲基硅油接枝端羟基聚氧乙烯（ＰＤＭＳ ｇ ＰＥＯ ＯＨ）为基材，用二环己基碳二亚胺（ＤＣＣＩ）作脱剂，研究了羟基（ＯＨ）与肝素上的羧基（—ＣＯＯＨ）之间的脱水缩合反应，制备出肝素化的抗血栓材料ＰＤＭＳ ｇ ＰＥＯ Ｈｅｐ，并对其涂覆表面的肝素含量和体外抗凝血性能进行了初步评价．实验结果表明，肝素接枝的共聚物具有优良的抗凝血性能和一定的应用前景．