Facile modifications of a polyimide via chloromethylation. I. Novel synthesis of a new photosensitive polyimide

A soluble aromatic polyimide was chloromethylated via a reaction with chloromethyl methyl ether in the presence of tin(IV) chloride to produce a new starting material for the modification of aromatic polyimides. The chemical structure of the resulting polymer was confirmed by ¹H NMR and Fourier transform infrared spectroscopy. The maximum number of chloromethyl groups per repeat unit was 1.81. The chloromethylated polyimide was stable up to 250 °C and soluble in both chloroform and tetrahydrofuran. So that its utilization for further modification could be demonstrated, cinnamic acid was reacted with the formed polyimide, and it produced a new photosensitive polyimide with a cinnamoyl side chain. The photosensitivity of the resulting polyimide was investigated with ultraviolet spectroscopic methods. © 2002 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 41: 22–29, 2003     

Cauchy problems for linear thermoelastic systems of type III in one space variable

The goal of the paper is to analyse properties of solutions for linear thermoelastic systems of type III in one space variable. Our approach does not use energy methods, it bases on a special diagonalization procedure which is different in different parts of the phase space. This procedure allows to derive explicit representations of solutions. These representations help to prove results for well‐posedness of the Cauchy problem, L^P–L^q decay estimates on the conjugate line and results for propagation of singularities. Copyright © 2005 John Wiley & Sons, Ltd.     

D. Liu and X. Zhu,Erratum to: “Fractional chromatic number and circular chromatic number for distance graphs with large clique size”. Journal of Graph Theory47(2) 2004, 129–146

The original article to which this Erratum refers was published in Journal of Graph Theory 47:129–146,2004 .     

Computations of two passing‐by high‐speed trains by a relaxation overset‐grid algorithm

This paper presents a relaxation algorithm, which is based on the overset grid technology, an unsteady three‐dimensional Navier–Stokes flow solver, and an inner‐ and outer‐relaxation method, for simulation of the unsteady flows of moving high‐speed trains. The flow solutions on the overlapped grids can be accurately updated by introducing a grid tracking technique and the inner‐ and outer‐relaxation method. To evaluate the capability and solution accuracy of the present algorithm, the computational static pressure distribution of a single stationary TGV high‐speed train inside a long tunnel is investigated numerically, and is compared with the experimental data from low‐speed wind tunnel test. Further, the unsteady flows of two TGV high‐speed trains passing by each other inside a long tunnel and at the tunnel entrance are simulated. A series of time histories of pressure distributions and aerodynamic loads acting on the train and tunnel surfaces are depicted for detailed discussions. Copyright © 2004 John Wiley & Sons, Ltd.     

Least‐squares meshfree method for incompressible Navier–Stokes problems

A least‐squares meshfree method based on the first‐order velocity–pressure–vorticity formulation for two‐dimensional incompressible Navier–Stokes problem is presented. The convective term is linearized by successive substitution or Newton's method. The discretization of all governing equations is implemented by the least‐squares method. Equal‐order moving least‐squares approximation is employed with Gauss quadrature in the background cells. The boundary conditions are enforced by the penalty method. The matrix‐free element‐by‐element Jacobi preconditioned conjugate method is applied to solve the discretized linear systems. Cavity flow for steady Navier–Stokes problem and the flow over a square obstacle for time‐dependent Navier–Stokes problem are investigated for the presented least‐squares meshfree method. The effects of inaccurate integration on the accuracy of the solution are investigated. Copyright © 2004 John Wiley & Sons, Ltd.     

The glow curve structure for the LiF:Mg,Cu,Na,Si TL detector with dopants concentrations and sintering temperatures

The glow curve structures for LiF:Mg,Cu,Na,Si TL detectors with various dopant concentrations and sintering temperatures were investigated for the improvement of the glow curve structure and sensitivity of the TL detector. The dopant concentrations were varied over the following ranges: Mg (0–0.25 mol%), Cu (0–0.07 mol%), Na and Si (0–1.5 mol%). With increasing Cu concentration, the intensity of the main peak was intensified and reached a maximum at a concentration of 0.05 mol%. The high-temperature peak was reduced. The dependency of the main peak intensity on the Mg concentration exhibits a sharp maximum at 0.2 mol%. The intensity of the high-temperature peak tends to rise slightly with increasing Mg concentration. It was found that the optimum concentrations of the dopants in the LiF:Mg,Cu,Na,Si TL material are Mg: 0.2 mol%, Cu: 0.05 mol%, Na and Si: 0.9 mol%. The dependency of the main peak intensity on sintering temperature exhibits a very sharp maximum at 830°C. The high-temperature peak was rapidly reduced after 825°C.     

Synthesis and association of poly(N,N‐dimethylacrylamide) copolymers with perfluorocarbon pendent groups connected through polyethylene‐glycol tethers

The synthesis is reported of copolymers of N,N‐dimethylacrylamide (DMA) and methacrylates containing 2,2′‐dihydroperfluorodecanoyl (RF) groups separated from the methacrylate by long polyethylene glycol (PEG) tether groups (between 1000 and 14,000 Da). At concentrations of between 1 and 8 wt % the copolymers with macromonomer contents of 1 mol % or less give gels in organic solvents such as dioxane, THF, or methanol, as well as in water. Given the low molecular weights, this indicates very efficient association of very low numbers of RF groups. Association and gel formation is enormously enhanced in the presence of longer PEG tethers. This is consistent with smaller poly(N,N,‐dimethylacrylamide) (PDMA) intermolecular excluded volume effects that are mediated by the longer PEG tethers and possibly by the incompatibility of PEG and PDMA that may lead to the formation of PEG microdomains. This increases the local concentrations of the RF groups in the PEO domains that are not diluted by the PDMA chains, as would be the case in the absence of PEG tethers. © 2003 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 42: 360–373, 2004     

Novel,biodegradable, functional poly(ester‐carbonate)s by copolymerization of trans‐4‐hydroxy‐L‐proline with cyclic carbonate bearing a pendent carboxylic group

Water‐soluble poly(ester‐carbonate) having pendent amino and carboxylic groups on the main‐chain carbon is reported for the first time. This article describes the melt ring‐opening/condensation reaction of trans‐4‐hydroxy‐N‐benzyloxycarbonyl‐L ‐proline (N‐CBz‐Hpr) with 5‐methyl‐5‐benzyloxycarbonyl‐1,3‐dioxan‐2‐one (MBC) at a wide range of molar fractions. The influence of reaction conditions such as catalyst concentration, polymerization time, and temperature on the number average molecular weight (M_n) and molecular weight distribution (M_w/M_n) of the copolymers was investigated. The polymerizations were carried out in bulk at 110 °C with 3 wt % stannous octoate as a catalyst for 16 h. The poly(ester‐carbonate)s obtained were characterized by Fourier transform infrared spectroscopy, ¹H NMR, differential scanning calorimetry, and gel permeation chromatography. The copolymers synthesized exhibited moderate molecular weights (M_n = 6000–14,700 g mol^?1) with reasonable molecular weight distributions (M_w/M_n = 1.11–2.23). The values of the glass‐transition temperature (T_g) of the copolymers depended on the molar fractions of cyclic carbonate. When the MBC content decreased from 76 to 12 mol %, the T_g increased from 16 to 48 °C. The relationship between the poly(N‐CBz‐Hpr‐co‐MBC) T_g and the compositions was in approximation with the Fox equation. In vitro degradation of these poly(N‐CBz‐Hpr‐co‐MBC)s was evaluated from weight‐loss measurements and the change of M_n and M_w/M_n. Debenzylation of 3 by catalytic hydrogenation led to the corresponding linear poly(ester‐carbonate), 4 , with pendent amino and carboxylic groups. © 2004 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 42: 2303–2312, 2004