13 nm窄带Si/Mo/C多层膜反射镜

基于多层膜准单色覆盖50~1500 eV能谱的多能点发射光谱测量系统可获得聚龙一号装置Z-pinch等离子体X射线源的能谱结构和总能量等信息。考虑装置的条件,在13 nm处的多层膜需要工作在掠入射角60。常规的Mo/Si多层膜尽管反射率最高,但其带宽较大,不能满足多层膜准单色的要求。因此提出将Mo和C共同作为多层膜的吸收层材料与Si组成Si/Mo/C多层膜,可使反射率降低较小而带宽明显减小。采用磁控溅射方法制备了Si/Mo/C多层膜,其掠入射X射线反射测量表面多层膜的结构清晰完整,同步辐射工作条件下反射率测量,得到Si/Mo/C多层膜在13 nm处和掠入射角60时的反射率为56.5%,带宽为0.49 nm（3.7 eV）。     

磁控溅射制备横向梯度分布的Mo/Si周期多层膜

 采用磁控溅射方法在Si基板上镀制了横向梯度分布的Mo/Si周期多层膜。以X射线掠入射反射测量了横向梯度多层膜的膜系结构,在基板65 mm长度范围内,多层膜周期从8.21 nm线性减小到6.57 nm,周期梯度为0.03 nm/mm。国家同步辐射实验室反射率计的反射率测试结果表明：该横向梯度分布周期多层膜上不同位置,能反射在13.3~15.9 nm波段范围内不同波长的极紫外光,反射率为60%~65%。     

用傅里叶变换方法实现的纳米多层膜性能表征

利用傅里叶变换(FFT)分析了纳米多层膜的X射线掠入射反射率测试曲线,模拟了各种制备和测试条件对多层膜结构参数测试结果的影响,检验了傅里叶变换方法的适用性和精确度.分析结果表明,相对于传统的反射曲线拟合方法,傅里叶变换方法具有直观和快速的优点,在不引入主观的膜层结构模型的情况下可以较为准确地定出复杂的多层膜结构参数,为多层膜结构表征提供了一种分析方法.     

Influence of interface roughness on reflectivity of tungsten/boron-carbide multilayers with variable bi-layer number by X-ray reflection and diffuse scattering

Infuence of interface roughness on the reflectivity of Tungsten/boron-carbide （W/B4C） multilayers varying with bi-layer number, N, is investigated. For W/B4C multilayers with the same design period thickness of 2.5 nm, a real-structure model is used to calculate the variation of reflectivities with N = 50, 100, 150, and 200, respectively. Then, these multilayers are fabricated by a direct current （DC） magnetron sputtering system. Their reflectivity and scattering intensity are measured by an X-ray diffractometer （XRD） working at Cu Kα line. The X-ray reflectivity measurement indicates that the reflectivity is a function of its bi-layer number. The X-ray scattering measured results show that the interface roughness of W/B4C multilayers increases slightly from layer to layer during multilayer growing. The variation of the reflectivity and interface roughness with bi-layer number is accurately explained by the presented realstructure model.     

30.4 nm波长处Mg基多层膜反射镜

太阳光谱中重要的He-Ⅱ谱线(波长30.4 nm)的观测对于研究太阳活动和日地空间环境具有重要意义,实现空间极紫外太阳观测需要采用多层膜作为反射元件.研究了工作在30.4 nm的Mg基多层膜.以反射率最高为评价函数设计了多层膜,采用直流磁控溅射技术制备了SiC/Mg,B4C/Mg和C/Mg多层膜,用X射线衍射仪测量了多层膜的结构.研究表明虽然B4C/Mg多层膜理论反射率最高,但实际制备结果显示,SiC/Mg多层膜的成膜质量最好,反射率最高.同步辐射反射率测量表明:在入射角10°时实测的SiC/Mg多层膜反射率为44.6%.     

Thinning and polishing of cross-section of depth-graded WSi2 /Si multilayer for linear zone plate application

A linear zone plate named multilayer laue lens (MLL) is fabricated using a depth-graded multilayer structure. The lens shows considerable potential in focusing an X-ray beam into a nanometer scale with high efficiency. In this letter, a depth-graded multilayer consisting of 324 alternating WSi 2 and Si layers with a total thickness of 7.9 μm is deposited based on the thickness sequence according to the demands of the zone plate law. Subsequently, the multilayer sample is sliced and thinned to an ideal depth along the cross-section direction using raw abrasives and diamond lapping. Finally, the cross-section is polished by a chemical mechanical polishing (CMP) technique to remove the damages and improve the surface smoothness. The final depth of the MLL is approximately 7 μm with an achieved aspect ratio greater than 400. Results of scanning electron microscopy (SEM) and atomic force microscopy (AFM) indicate that interfaces are sharp, and the multilayer structure remains undamaged after the thinning and polishing processes. The surface roughness achieved is 0.33 nm.     

Fabrication and characterization of sliced multilayer transmission grating for X-ray region

To develop high quality dispersion optics in the X-ray region, the sliced multilayer transmission grating is examined. Dynamical diffraction theory is used to calculate the diffraction property of this volume grating. A WSi 2 /Si multilayer with a d-spacing of 14.3 nm and bi-layer number of 300 is deposited on a superpolished silicon substrate by direct current magnetron sputtering technology. To make the transmission grating, the multilayer is sliced and thinned in the cross-section direction to a depth of 23-25 μm. The diffraction efficiency of the grating is measured at E = 8.05 keV, and the 1st-order efficiency is 19%. The sliced multilayer grating with large aspect ratio and nanometer period can be used for high efficiency and high dispersion optics in the X-ray region.     

Epoxy replication of hard X-ray supermirrors

The direct replication of W/Si supermirrors is investigated systematically. W/Si supermirrors are fabricated by direct current(DC) magnetron sputtering technology. After deposition,the supermirrors are replicated from the supersmooth mandrels onto ordinary float glass substrates by epoxy replication technique. The properties of the supermirrors before and after the replication are characterized by grazing incidence X-ray reflectometry(GIXR) measurement and atomic force microscope(AFM) . The results show that before and after replication,the multilayer structures are almost the same and that the surface roughness is 0.240 and 0.217 nm,respectively,which are close to that of the mandrel. It is demonstrated that the W/Si supermirrors are successfully replicated from the mandrel with good performance.     

大尺寸高性能X射线双通道多层膜反射镜研制

为满足同步辐射装置中X射线单色器的需求,在直线式磁控溅射设备上制备了W/Si和Ru/C双通道多层膜反射镜。制备的W/Si多层膜和Ru/C多层膜的周期厚度均为3 nm,平均界面宽度分别为0.30 nm和0.32 nm。在320 mm长度范围和20 mm宽度范围内,W/Si多层膜膜厚误差的均方根值分别为0.30%和0.19%,Ru/C多层膜膜厚误差的均方根值分别为0.39%和0.20%。对制备的样品进行了表面形貌测试和非镜面散射测试,对比了W/Si多层膜和Ru/C多层膜的表面和界面粗糙度大小。硬X射线反射率测试结果表明,W/Si多层膜和Ru/C多层膜在8.04 keV能量点处的一级布拉格峰测试反射率分别为63%和62%,角分辨率均为2.6%。基于以上研究,在尺寸为350 mm×60 mm的高精度Si平面镜表面镀制了W/Si和Ru/C双通道多层膜,并且其被成功应用于上海同步辐射光源线站中。