Study on the formation of the ketonic defects in the thermal degradation of ladder-type poly(p-phenylenes) by vibrational spectroscopy

We have investigated the thermal degradation in air by Fourier transform infrared spectroscopy of a ladder-type copolymer containing fluorene units in the backbone (Me-LPF), to reveal the formation of the ketonic defects. As thermal treatment of Me-LPF film at 200 degrees C in air proceeds, a new group of complex absorption bands due to degradation products arises in the range between 1800 and 1600 cm(-1). The observed overlapping bands were separated and assigned by utilizing the second-derivative IR spectral analysis, which can narrow the peak width to one-third of the originals and thereby eases the analysis. The degraded products were assigned as fluorenone (1718 cm(-1)) and benzophenone (Ar-(C=O)-Ar) (1665 cm(-1)), formed by the oxidation of the backbone, and acylphenone (Ar-(C=O)-R) (1685 cm(-1)) from the side chain. The fluorenone was found to be the major component among the degraded products in the main chain, and the time and temperature dependence indicated that the oxidation is a kind of autocatalytic radical-chain process. The oxidation can reach a very high degree (approximately 30% for 6 h oxidation at 240 degrees C estimated by absorption of the alkyl). Our results suggest the possibility of the oxidation of the 9-bialkylfluorene sites. We propose that the degradation of the alkyl in the side chain can help the radicals to propagate in the chain reaction.     

Synthesis and structural identification of a highly ordered mesoporous organosilica with large cagelike pores

Using 1,2-bis(trimethoxysilyl)ethane as organosiloxane precursor and a triblock copolymer surfactant, Pluronic F127, as template, a highly ordered mesoporous organosilica with large cagelike pores has been successfully synthesized. Its structure was resolved to be 3-D cubic Fmm by high-resolution transmission electron microscopy. The intergrowth of hexagonal close-packed and cubic close-packed phases was observed in this material. The effect of different siliceous precursors on the mesostructure was also investigated.     

Electronic control of chiral quaternary center creation in the intramolecular asymmetric heck reaction

The Boehringer-Ingelheim phosphinoimidazoline (BIPI) ligands were applied to the formation of chiral quaternary centers in the asymmetric Heck reaction. Several different substrates were examined in detail, using more than 70 members of this new ligand class. Hammett relationships were determined through systematic variation of the ligand electronics. All substrates showed essentially the same Hammett behavior, where enantioselectivity increased as the ligands were made more electron-deficient. Ligand optimization has led to catalysts which give the highest enantioselectivities reported to date for these difficult systems.     

Fine structures of zeolite-Linde-L (LTL): surface structures, growth unit and defects

High-resolution electron microscopy (HREM) has been used to image the surface structure of nano- and micrometer-sized synthetic crystals of zeolite-Linde-L (LTL). Columnar holes and rotational, nano-sized, wheel-like defects were observed within the crystals, where the hole has a minimum size equal to that of the rotational defect. Predictions of surface structure from atomistic computer simulation concur with the observations from HREM and provide insight into the crystal growth mechanism of perfect and defective LTL. Analysis of the energetics of the formation of rotational defect structures reveals that the driving force for defect creation is thermodynamic and furthermore, the rotational defects could be created in high concentrations. Formation of a columnar hole is found to be slightly energetically unfavourable and therefore we speculate that the incidence of both rotational and nano-sized vacancy defects is strongly dependent on kinetic factors and reaction conditions. The morphology of nano- and microcrystalline LTL is contradistinct and we use insights from simulation to propose an explanation of the disparity in crystal shape.     

Synthesis of novel 6,11-O-bridged bicyclic ketolides via a palladium-catalyzed bis-allylation

A bridging chemistry process was developed to form an ether bridge between 6-O and 11-O of erythromycin A via a tandem or stepwise palladium-catalyzed bis-pi-allylation. By applying this bridging process, new 6,11-O-bridged bicyclic ketolides (BBKs) were synthesized. These BBKs showed good antibacterial activities against the macrolide-susceptible strains as well as mef-resistant strains and served as a good core for further modifications to study the structure-activity relationship (SAR) and to overcome bacterial resistance. [reaction: see text]     

龋病人牙釉质表面硬度及抗磨损性能测试

采用人工方法制成人牙釉质浅龋及使用抗龋措施的龋损釉质样本，分别测量各组釉质表面显微硬度，并以微动摩擦磨损试验机测试其抗磨性能，试验结果表明：各组实验组釉质较对照组表面硬度都有不同程度下降，氟化钠前处理会使釉质表达硬度显著下降，人工浅龋牙釉质的抗磨损性能不如正常釉质，使用两种抗龋措施对其抗磨性能没有明显改善。     

Synthesis of alpha-MoTe2 nanorods via annealing Te-seeded amorphous MoTe2 particles

Semiconductor alpha-MoTe2 nanorods have been synthesized by annealing Te-seeded particles of an amorphous MoTe2 intermediate. This intermediate is prepared by a solution reaction between Mo(CO)6 and elemental Te in diphenylmethane. The as-synthesized products were characterized by structural, compositional, and morphological techniques of X-ray diffraction, selected area electron diffraction, selected area energy dispersive spectroscopy, energy dispersive X-ray analysis, X-ray photoelectron spectroscopy, transmission electron microscopy, and high-resolution transmission electron microscopy. The results of the annealing process are MoTe2 nanorods with diameters of 50-200 nm and lengths ranging from 0.1 to 3.0 microm. Here, the rodlike structure of MoTe2 is reported for the first time, and added to the list as one kind of new morphology of MoTe2 nanomaterials. A mechanism for the formation of the nanorods is proposed. The sandwich-layered structure of Te-Mo-Te and the similarity in the structure between hexagonal alpha-MoTe2 and hexagonal Te are responsible for the formation of nanorods of MoTe2.     

Gas purge microsyringe extraction for quantitative direct gas chromatographic-mass spectrometric analysis of volatile and semivolatile chemicals

Sample pretreatment before chromatographic analysis is the most time consuming and error prone part of analytical procedures, yet it is a key factor in the final success of the analysis. A quantitative and fast liquid phase microextraction technique termed as gas purge microsyringe extraction (GP-MSE) has been developed for simultaneous direct gas chromatography-mass spectrometry (GC-MS) analysis of volatile and semivolatile chemicals without cleanup process. Use of a gas flowing system, temperature control and a conventional microsyringe greatly increased the surface area of the liquid phase micro solvent, and led to quantitative recoveries of both volatile and semivolatile chemicals within short extraction time of only 2 min. Recoveries of polycyclic aromatic hydrocarbons (PAHs), organochlorine pesticides (OCPs) and alkylphenols (APs) determined were 85-107%, and reproducibility was between 2.8% and 8.5%. In particular, the technique shows high sensitivity for semivolatile chemicals which is difficult to achieve in other sample pretreatment techniques such as headspace-liquid phase microextraction. The variables affecting extraction efficiency such as gas flow rate, extraction time, extracting solvent type, temperature of sample and extracting solvent were investigated. Finally, the technique was evaluated to determine PAHs, APs and OCPs from plant and soil samples. The experimental results demonstrated that the technique is economic, sensitive to both volatile and semivolatile chemicals, is fast, simple to operate, and allows quantitative extraction. On-site monitoring of volatile and semivolatile chemicals is now possible using this technique due to the simplification and speed of sample treatment.     

The structure and catalytic activity of anatase and rutile titania supported manganese oxide catalysts for selective catalytic reduction of NO by NH3

The structure and catalytic properties of anatase and rutile supported manganese oxide catalysts prepared by impregnation method have been studied by using X-ray diffraction (XRD), laser Raman spectroscopy (LRS), X-ray photoelectron spectroscopy (XPS), H(2) temperature-programmed reduction (H(2)-TPR) and BET surface area measurements combined with activity testing of selective catalytic reduction (SCR) of NO by NH(3). It has been shown that the manganese oxide loadings on the two TiO(2) supports exert great influences on the SCR activity. For the rutile supported manganese oxide catalysts, increasing manganese oxide loading leads to the increase of reducibility of dispersed manganese oxide species and the rate constant k, which reaches a maximum around 9.6 × 10(-6) mol g(Mn)(-1) s(-1) at 0.5 mmol Mn per 100 m(2) TiO(2). When the manganese oxide loading is beyond this value, the existence of amorphous MnO(x) multiple layers will certainly reduce the ratio of manganese oxide species exposed on the surface and the reducibility of dispersed manganese oxide species, resulting in the rapid decrease of rate constant k. The LRS and XPS results have revealed that for the anatase supported manganese oxide catalysts manganese oxide species exist in Mn(+4) as a major species with Mn(+3) species and partially undecomposed Mn-nitrate as the minor species. Under the SCR reaction conditions, Mn(+3) species on anatase are oxidized to Mn(+4) species, inserting in the surface of anatase and promoting the anatase-to-rutile transformation in the surface layers of the anatase support. Since these Mn(4+) cations are actually dispersed on the support with a rutile shell-anatase core structure and its concentration is very near to that of MnO(x)/TiO(2) (R) catalyst, the relation between the rate constant k and the MnO(x) loading on the anatase support is similar to that on the rutile support, and that the rate constant k values for anatase and rutile supported manganese oxide catalysts are very close at the same MnO(x) loading.     

Mn（OAc）2/Schiff base as a new efficient catalyst system for the Henry reaction of nitroalkanes with aldehydes

A series of novel Schiff bases bearing triazole structure were synthesized and characterized by IR and NMR.Mn（OAc）₂/Schiff base efficiently catalyzed Henry reaction of nitroalkanes with aldehydes to produce the corresponding products of β-nitroalcohols, under mild conditions with high yields（up to 99%）.A reaction mechanism is proposed based on the experimental results.