硅酸铋(BSO)纳米粉体的制备与表征

Bismuth silicate nanopowders were prepared by the sol-gel method. Tetraethyl orthosilicate (TEOS) and Bi₂O₃ were used as the starting materials. The precursors were heat-treated at 750℃ for 2 h. The size distribution of Bi₄Si₃O₁₂ nanopowders is 40～100 nm. The TG-DTA curves, the XRD patterns and the TEM microphotograph of Bi₄Si₃O₁₂ are discussed. Compared with crystal materials, the excitation spectra and the emission spectra of Bi₄Si₃O₁₂ nanopowders indicate blue shift.     

石英玻璃衬底上纤锌矿Mg0.25Zn0.75O薄膜的结构及光学性能

MgxZn1-xO材料是一种新型光电功能材料.采用溶胶凝胶法在石英玻璃上制备了Mg0.25Zn0.75O薄膜,理论结合实验研究了Mg0.25Zn0.75O薄膜的结构和光学性能.研究表明,石英玻璃衬底上Mg0.25Zn0.75O薄膜呈六方纤锌矿结构,薄膜均匀,平均粒径约为20 nm.吸收光谱表明吸收带边始于360 nm,相应的禁带宽度为3.83 eV.发光光谱包含三个发射峰,分别位于384.9 nm(3.23 eV),444.8 nm(2.79 eV)和533.6 nm(2.32 eV),激发光谱峰位于378 nm.由于Mg离子的间隙缺陷导致Mg0.25Zn0.75O薄膜晶格增大,禁带宽度变宽,紫外、蓝光和绿光发射分别红移59,14和12.6 nm.     

宽频谱红外-可见转换材料CaS∶Ce,Sm的低温燃烧合成及表征

采用低温燃烧合成(LCS)法制备出宽频谱红外-可见转换材料CaS∶Ce, Sm,研究了稀土掺杂浓度对产物红外-可见转换发光性能的影响,并对样品进行了结构和性能表征。XRD分析表明样品为立方晶系CaS晶体结构。样品的激发光谱位于200～500 nm之间,紫外或可见光均可有效激发该材料完成“充能”过程,且可见光激发占优势。样品的红外响应光谱范围为800～1 600 nm,说明CaS∶Ce, Sm材料具有宽频谱红外-可见转换效应。样品的红外-可见转换发射光谱是位于450～650 nm的宽带谱,两毗邻发射峰位于513.4和572 nm,分别对应Ce3+的2T_2g(5d)→2F_5/2(4f)和2T_2g(5d)→2F_7/2(4f)跃迁。     

宽频谱红外上转换材料CaS∶Eu,Sm的快速合成及表征

分别以尿素、甘氨酸及二者一定比例混合体作为有机燃料,采用低温燃烧法快速合成了宽频谱红外上转换发光材料CaS∶Eu,Sm,反应时间为2~3 min,产物为红色疏松多孔的超细粉末。研究了燃料种类、燃料用量对于燃烧反应现象、燃烧产生的气体量及终产物表观状态的影响;研究了辅助氧化剂用量对于燃烧反应的影响。X射线衍射(XRD)物相分析表明样品为面心立方CaS晶格结构。光谱分析表明样品在800~1600 nm之间具有宽频谱红外响应效应,上转换发光峰值波长位于655 nm,对应于Eu2 离子的4f65d→4f7(8S7/2)跃迁。     

发光材料BaAl2Si2O8∶Eu2+的物相结构与发光性能

A phosphor, Ba_0.97Al₂Si₂O₈∶Eu²⁺, was synthesized by high temperature solid-phase method at different temperatures. The samples were characterized by TG/DTA, XRD and fluorescence spectroscopy. The results show that the main phase for host of these luminescence materials is barium feldspar BaAl₂Si₂O₈∶Eu²⁺ and there is a transition from hexagonal crystal system to monoclinic crystal system in the process of the sintering of barium feldspar. The luminescent phenomen of barium feldspar with hexagonal structure can not be observed under the excitation of ultraviolet lamp of 365 nm while the barium feldspar with monoclinic structure has excellent luminescence properties. The excitation spectra of all these samples show broad band spectra ranging from 250～390 nm with peak at λ_ex of 357 nm,which indicates that these samples can be effectively excited by near ultraviolet ; the emission spectra range from 380～600 nm with peak at λ_em of 433 nm. The luminescent intensity increases then decreases with the concentration of doping Eu²⁺ ions. When the concentration of dopants is 2.5mol%, the luminescent intensity reaches the maximum value. When the concentration of Eu²⁺ ions changes from 0.5mol% to 2.5mol%, the emission peak has a red shift from 427 nm to 440 nm.     

发光材料BaAl2Si2O8∶Eu^2＋的物相结构与发光性能

硅酸盐类物质作为发光材料基质．发光中心和基质相互作用能量较低。可使发光中心离子直接吸收激发能量,利于提高发光效率。目前。研究较多的硅酸盐类发光材料为Zn2SiO4、Sr2MgSi2O7、Ba3MgSi2O8等。铝硅酸钡通常归属于硅酸盐范畴,铝硅酸盐的结构复杂、物相组成变化多样．一般实验条件下很难获得单一物相产物。碱土金属铝硅酸盐作为发光材料基质由来已久,     

白光LED用SrAl_2Si_2O_8∶Eu~(2+)荧光粉的制备与发光性能研究

采用高温固相法制备了SrAl2Si2O8∶Eu2+系列荧光粉,研究了灼烧温度以及助熔剂硼酸浓度和激活剂Eu2+离子浓度对发光性能的影响,研究了SrAl2Si2O8的微结构。结果表明,以3.0wt%H3BO3为助熔剂,在1250℃灼烧3h可制备发光性能优良的SrAl2Si2O8∶Eu2+荧光粉,Eu2+离子的最佳掺杂浓度为2.5mol%,Eu2+离子浓度过大时的浓度猝灭是由电偶极-电四极之间的相互作用引起的。SrAl2Si2O8∶Eu2+的激发和发射光谱均为宽带谱,在280～380nm光的激发下,可发射峰值波长位于429nm的蓝色光。     

SrAl2O4∶Eu2+，Dy3+纳米长余辉发光材料的制备与表征

采用溶胶-凝胶法制备了SrAl₂O₄∶Eu²⁺，Dy³⁺ 纳米长余辉发光材料，研究了pH值、反应温度和络合剂等对溶胶-凝胶形成的影响，研究了灼烧温度对SrAl₂O₄∶Eu²⁺，Dy³⁺ 晶相、颗粒尺度和发光性能的影响。利用XRD, SEM，光谱分析等手段对产物进行了结构和性能分析。实验结果表明，在800 ℃时SrAl₂O₄晶相开始形成但没有发光，而在1 100 ℃烧结的样品则具有很好的发光性能。样品平均晶粒尺寸随灼烧温度升高而增加，平均晶粒尺寸为20～40 nm。样品的激发光谱是峰值在240，330，378和425 nm的连续宽带谱，发光光谱是峰值在523nm的宽带谱，与SrAl₂O₄∶Eu²⁺，Dy³⁺ 粗晶材料相比，发光光谱发生了“红移”现象。样品的热释光峰值位于157 ℃，与SrAl₂O₄∶Eu²⁺，Dy³⁺ 粗晶材料相比，峰值向低温移动了13℃。     

宽频谱红外上转换材料CaS:EU,Sm的快速合成及表征

分别以尿素、甘氨酸及二者一定比例混合体作为有机燃料，采用低温燃烧法快速合成了宽频谱红外上转换发光材料CaS：Eu，Sm，反应时间为2～3min，产物为红色疏松多孔的超细粉末。研究了燃料种类、燃料用量对于燃烧反应现象、燃烧产生的气体量及终产物表观状态的影响；研究了辅助氧化剂用量对于燃烧反应的影响。X射线衍射（XRD）物相分析表明样品为面心立方CaS晶格结构。光谱分析表明样品在800-1600nm之间具有宽频谱红外响应效应，上转换发光峰值波长位于655nm，对应于Eu^2＋离子的4f^65d→4f^7（^8S7/2）跃迁。     

SrS:Eu,Sm荧光粉的制备及性能表征

制备了用于宽频谱红外上转换的SrS:Eu,Sm荧光粉.XRD分析表明,在1 100℃,灼烧1 h获得的SrS:Eu,Sm样品较理想,为SrS的面心立方结构;激发光谱表明,样品可被紫外和可见光有效激发;样品的荧光发射光谱由4个发射峰组成,峰值分别位于567,589,602和648 nm.红外上转换发光光谱是峰值位于595nm附近的宽带谱,样品的红外响应范围主要位于800～1 400 nm.