填镁改善5052铝合金激光焊接接头机械性能研究

在铝合金激光搭接焊中,镁元素烧损将大大降低焊缝的抗拉强度。为了消除铝合金激光搭接焊中镁元素的烧损对焊接接头的负面影响,采用在铝合金激光焊接接头中填加镁粉的方法,研究焊接速率对镁元素烧损的影响。实验中,测量了焊缝中镁元素在垂直和水平方向的分布,并对焊接接头抗拉强度进行了测试;分析了焊接接头中镁含量和抗拉强度之间的关系,比较了填镁量不同时各焊接接头的抗拉强度。结果表明,镁元素的烧损极大地影响了焊缝的抗拉强度,在激光焊接中填镁能有效地提高焊缝的抗拉强度;相比没填镁,填镁的焊接接头抗拉强度最大改善可以达到36.06%;当焊缝中镁元素的质量分数大约是0.026时,抗拉强度强度达到最大值。这为改善铝合金激光焊接接头强度提供了新的理论依据和方法。     

Third-Order Optical Nonlinearity of a Novel Material：（Tetramethylammonium） bis （1,3-dithiole-2-thione-4,5-dithiolato） Copper

A novel dmit^2- salt： （tetramethylammonium）bis（1,3-dithiole-2-thione-4,5-dithiolato） copper, abbreviated as MECu, is synthesized and its third-order optical nonlinearity is characterized by Z-scan technique at a wavelength of 1064nm with laser duration of 30ps. Z-scan curves reveal a negative Kerr coefficient at 1064nm and no nonlinear absorption is observed. The nonlinear refraction coefficient n2 and the second hyperpolarizability γ have been determined to be as large as 2.15 × 10^-11 esu and 3.23 × 10^-31 esu, respectively, suggesting MECu is a potential material for optical device applications.     

适用于全光开关的[(C3H7)4N][Au(C3S5)2]三阶非线性光学性质研究

合成了一种金属有机配合物[(C3H7)4N][Au(C3S5)2].配制了浓度为1×10-3 mol/L的[(C3H7)4N][Au(C3S5)2]/乙腈溶液,并用旋涂法制备了掺杂浓度质量比为1%的[(C3H7)4N][Au(C3S5)2]/PMMA复合薄膜.运用Z扫描方法,分别研究了样品溶液和薄膜在波长为1064nm...     

聚合物复合薄膜DR13/PMMA的制备及其光学特性

薄膜的厚度、折射率和传输损耗等参数在电光系数的确定和光波导器件的设计和制作过程中都是重要的参考数据。采用旋涂法制备了三种不同质量比的偶氮化合物染料分散红13(DR13)与聚合物聚甲基丙烯酸甲酯(PMMA)复合薄膜;利用分光光度计测量样品的吸收光谱;利用棱镜耦合仪测量了薄膜的厚度和折射率,并对不同波长下的折射率进行拟合得到折射率色散曲线;采用视频摄像技术研究样品的光传输特性,利用自己编写的计算机程序来处理其实验结果。DR13/PMMA复合薄膜在300nm和500nm处有两个大的吸收峰,而在其他波段,尤其是在通信波段没有明显吸收。薄膜的膜厚大约为1~2μm,其折射率随着质量比的增加而增大,随着激光波长的增大而降低,膜厚和折射率的误差分别为3.2×10-1μm和1.5×10-3。三种质量比(10%,15%和20%)的薄膜传输损耗分别为1.5269dB/cm,2.7601dB/cm和3.6291dB/cm,可以看出随着DR13质量比的增大,光传输损耗也逐渐增大,即DR13的含量对于传输损耗的影响较大。     

一种新型dmit盐的三阶非线性光学性质研究

为了研究一种新的有机金属配合物dmit盐(tetram ethylammon ium)bis(1,3-dithiole-2-thione-4,5-dithiolato)copper(简称为MeCu)的三阶非线性光学性质,采用单光束z扫描技术,在波长为1064nm、脉宽为30ps条件下对浓度为1.0×10-3mol/L的MeCu/丙酮溶液进行研究。实验结果表明,其三阶非线性折射率n2和二阶分子超极化率γ分别为-2.15×10-11esu和1.94×10-30esu,未发现三阶非线性吸收的存在。表明该材料在全光开关等非线性光学器件的研制上可能具有潜在的应用价值。     

Nonlinear optical properties of [（CH3）4N]Au（dmit）2 using Z-scan technique

The third-order optical nonlinearities of [（CH3）4N]Au（dmit）2 （dmit = 4,5-dithiolate-1,3-dithiole-2-thione） at 532 nm and 1064 nm are investigated using the Z-scan technique with pulses of picoseconds duration. The Z-scan spectra reveal a strong nonlinear absorption （reverse saturable absorption） and a negative nonlinear refraction at 532 nm. No nonlinear absorption is observed at 1064 nm. The molecular second-order hyperpolarizability γ for the [（CH3）4N]Au（dmit）2 molecule at 532nm is estimated to be as high as （2.1 ±0.1） × 10^-31 esu, which is nearly three times larger than that at 1064 nm. The mechanism responsible for the difference between the results is analysed. Nonlinear transmission measurements suggest that this material has potential applications in optical limiting.     

适用于全光开关的[(C3H7)4N][Au(C3S5)2]三阶非线性光学性质研究

合成了一种金属有机配合物[(C3H7)4N][Au(C3S5)2].配制了浓度为1×10－3 mol/L的[(C3H7)4N][Au(C3S5)2]/乙腈溶液,并用旋涂法制备了掺杂浓度质量比为1%的[(C3H7)4N][Au(C3S5)2]/PMMA复合薄膜.运用Z扫描方法,分别研究了样品溶液和薄膜在波长为1 064 nm,脉宽为20 ps条件下的三阶非线性光学性质.研究发现薄膜的三阶非线性极化率χ(3)比溶液高出三个数量级.其中,薄膜的非线性折射率n2为－1.76×10－15 m2/W、三阶非线性极化率χ(3)为9.37×10－10 esu.结果表明,该材料在全光开关方面具有潜在的应用价值.     

吡啶联异噁唑类化合物的设计、合成及抗肿瘤活性

根据已知的激酶变构抑制剂与其靶点激酶的X射线共晶结构,设计了一系列以吡啶联异噁唑为中心结构的潜在激酶变构抑制剂.以2-甲基-5-硝基-3-吡啶甲酸甲酯为原料,通过形成酰胺、磺酰胺和连接嘧啶片段等衍生化手段合成了21个新的吡啶联异噁唑类化合物,其结构经1H NMR,13C NMR和MS确证.采用噻唑蓝(MTT)法测试了所合成化合物的体外抗肿瘤活性,初步测试结果表明该类化合物对肿瘤细胞的增长具有显著的抑制作用.     

一种新型有机金属化合物纳秒时域饱和吸收特性研究

合成了一种新型有机金属配合物Cetyltrimethylammonium-bis(2-thioxo-1,3- dithiole- 4,5-dithiolato)-copper(简称CtCu)材料.采用单光束Z扫描测试技术,在波长为1 053 nm,脉宽为1 ns的条件下研究了该样品的三阶非线性光学性质.研究发现,该材料具有很强的饱和吸收特性,激发态的有效吸收截面为σeff＝1.10×10－19 cm2,与基态吸收截面的比值为1∶484.利用非线性透过率实验验证了材料的饱和吸收特性,并对其产生机理进行了分析.实验结果表明,该材料在近红外波段的激光脉冲压缩方面有潜在的应用前景.