Sm3+掺杂稀土硼酸盐玻璃的光谱参数计算和荧光光谱分析

制备了具有高效可见荧光发射的Sm3 掺杂稀土硼酸盐(LBLB)玻璃,对玻璃的吸收和荧光光谱展开了测试与分析.根据Judd-Ofelt理论对吸收光谱进行了拟合,求得Sm3 离子的晶场调节参数Ωt=(2,4,6)分别为6.81×10-20,4.43×10-20和2.58×10-20 cm2,并进一步计算出各能级跃迁的谱线强度、自发辐射跃迁概率、辐射寿命和荧光分支比等光谱参数.紫外光激发下,Sm3 掺杂LBLB玻璃发出明亮的橙红色光.激发光谱表明,氩离子激光器是Sm3 掺杂LBLB玻璃有效的激发光源.     

基于B3PyMPM∶Cs高效叠层OLED器件的制备

以B 3 PyMPM∶Cs/Al/HAT-CN作为电荷生成单元制备高效叠层绿色磷光有机电致发光器件,叠层器件的最大电流效率和最大流明效率分别为172.2 cd/A和111.0 lm/W,在5 mA/cm^2电流密度下,叠层器件的电压和亮度分别为传统器件的2.04倍和2.84倍.为了探究叠层器件性能优于传统器件的原因,研究了电荷生成单元内的电荷产生和注入过程,以及薄层铝对电子注入特性和电荷生成单元稳定性的影响.实验结果表明,电荷能够有效地在电荷生成单元内产生并顺利注入电子传输层中,B3PyMPM∶Cs和HAT-CN间Al薄层的插入能够进一步提高电子注入效率及器件结构的稳定性.     

A Novel Energetic Ionic Salt: Hydroxylammonium Potassium 3,3’-Dinitro-5,5’-bis-1,2,4-triazole-1,1’-diolate Dihydrate

A novel energetic ionic salt,hydroxylammonium potassium 3,3?-dinitro-5,5?-bis-1,2,4-triazole-1,1?-diolate dihydrate[(NH3OH)2K(DNOBT)1.5?2H2O],was synthesized and structurally characterized by elemental analysis,IR spectra,13C NMR and single-crystal X-ray diffraction.(NH3OH)2K(DNOBT)1.5?2H2O crystallizes in triclinic system,space group P with a=7.9212(6),b=9.1924(7),c=14.2549(15)?,a=103.917(2)°,β=99.736(2)°,g=104.8110(10)°,V=944.16(14)?^3,Z=2,Dc=1.855 g/cm^3,F(000)=538,μ=0.386 mm^-1,S=1.070,the final R=0.0525 and wR(I>2s(I))=0.1593.Thermal decomposition of(NH3OH)2K(DNOBT)1.5?2H2O and its intermediate potassium 1?-hydroxy-3,3?-dinitro-5,5?-bis-1,2,4-triazole-1-olate monohydrate[K(HDNOBT)?H2O]was studied by using DSC and TG-DTG.It was found that(NH3OH)2K(DNOBT)1.5?2H2O,which has primarily one exothermic decomposition process at 248.2℃,has better thermal stability than K(HDNOBT)?H2O which is decomposed at 210.9℃.     

A Novel Hybrid Solid Constructed from Tetramolybdate and Copper Complexes with Mixed Ligands: [{(Cu·phen)2(tp)}{(Cu·phen·H2O)2(tp)}{Mo4O14}]

A novel copper molybdate with mixed ligands, [{(Cu·phen)2(tp)}{(Cu·phen·H2O)2(tp)}{Mo4O14}] (phen=1,10-phenanthroline, tp=terephthalate) 1, has been hydrothermally synthesized and structurally characterized. The crystal belongs to monoclinic system, space group P21/c with a=13.1711(7), b=19.6132(10), c=13.6910(7) (A), β=117.6870(10)°, V=3131.8(3)(A)3, Z=2, C64H44Cu4Mo4N8O24, Mr=1946.99, Dc=2.065 g/cm3, F(000)=1920, μ(MoKα) (A) 2.198 mm-1, R=0.0810 and wR=0.2012 for 4233 observed reflections (Ⅰ ＞ 2σ(Ⅰ)). The structural analysis indicates that the title compound contains a discrete tetramolybdate cluster decorated with copper complex fragments and tp ligands bridging the clusters into a wave-like layer. The hydrogen bonding between adjacent layers further extends the compound into a 3-D framework.     

Synthesis and Crystal Structures of Novel Keggin and Dawson Polyoxometalates Containing Amantadine

Heteropolyoxometalates are a large family of potent medicines due to their excellent antiviral and antitumor activity 1-4, while their application in clinic meets great difficulties for their toxicity 5. How to synthesize heteropolyoxometalate medicines possessing high activity and low toxicity has become the focus in heteropolyoxometalate medicine research. Previously reported polyoxometalates showing medical activities are all salts simple Na+, K+ or NH4+ etc. inorganic cations, in which o…     

活性炭负载TiO2-Fe3O4磁性光催化剂的制备及性能

采用溶胶-凝胶法制备了易于固液分离的活性炭（AC）负载磁性光催化剂（TiO2-Fe3O4／AC）．样品通过SEM-EDX和X射线衍射法进行表征．通过在紫外光照射下降解亚甲基蓝评价其光催化降解能力．结果表明：负载22％Fe3O4的光催化剂（含20％TiO2和58％AC）的光催化活性最强（120min时亚甲基蓝的降解率达到87％,是纯TiO2的2．7倍）;磁性光催化剂可实现磁分离回收．     

C4烃在FAU、BEA、LTL型分子筛中吸附的蒙特卡罗研究

应用蒙特卡罗(MC)模拟方法研究了1,3-丁二烯、1-丁烯、正丁烷三种C4烃在FAU、BEA、LTL三种分子筛中的吸附行为. 模拟分别得到了298 K时这些C4烃的纯组分在分子筛中的吸附等温线、吸附质分布和吸附热. 结果表明, 在饱和吸附状态下这些C4烃在FAU分子筛中的吸附量最大, 在BEA分子筛中的吸附量居中, 在LTL分子筛中的吸附量最少. 对于同一种分子筛来说, 正丁烷在其中的等量吸附热最大, 1-丁烯居中, 1,3-丁二烯最小. 对于同一种C4烃来说, 它在LTL分子筛中的吸附热与在BEA分子筛中的吸附热相近, 并且高于在FAU分子筛中的吸附热. 还模拟了543 K、2.0 MPa时这些C4烃的三元混合组分在分子筛中的吸附, 发现正丁烷的吸附量占的比例最大, 1-丁烯居中, 1,3-丁二烯最少.     

Ti对铸造镍基高温合金中碳化物和拓扑密排相影响

采用光学显微镜、扫描电子显微镜和透射电子显微镜等测试技术,研究了经过标准热处理和时效处理后的不同Ti含量合金的微观组织。 研究发现,标准热处理后不同Ti含量合金的相组成相同,主要由γ、γ′、MC和M23C6型碳化物组成;随着Ti含量增加,合金组织中的碳化物数量逐渐增加。 不含Ti的合金中的MC碳化物的组成主要是TaC,而含Ti合金中MC型碳化物组成为(Ta,Ti)C,并且随着Ti含量增加,MC碳化物中M组成元素Ta和Ti的比值（Ta/Ti）逐渐减小。 通过研究900 ℃不同时间时效处理后合金微观组织发现,随着Ti含量增加,合金中拓扑密排相(TCP)析出趋势逐渐增加。 含质量分数2.7%Ti的合金经900 ℃/500 h时效处理后,组织中析出了针状富含Cr、W和Mo的σ相。 这表明要保证合金具有良好的组织稳定性,需要控制合金中Ti的加入量。     

苯乙烯嘧啶化合物的合成及其作为pH探针的光谱特点

合成并表征了化合物4,6-二[（4′-二乙基胺基）苯乙烯基]嘧啶-2-醇。 通过研究该化合物在不同pH值的磷酸盐缓冲溶液中紫外-可见吸收光谱和荧光光谱的变化,发现λmax约为500 nm的吸收峰在溶液pH=6.78中吸收强度最大。 荧光发射峰随着pH值的升高逐渐减弱,直至淬灭（pH=5.51）。     

异质结Bi_2WO_6/ZnO复合光催化剂的制备及其光催化降解含酚废水的研究

采用水热法制备了一系列Bi2WO6/Zn O异质结光催化剂,并对其进行X射线衍射(XRD)、紫外-可见光谱(UV-Vis DRS)、扫描电镜(SEM)、光电子能谱(EDS)等手段对其结构性质进行了表征。在含酚废水的液相反应体系中,研究了异质结Bi2WO6/Zn O复合光催化剂光催化降解苯酚的性能。结果表明,Bi2WO6/Zn O异质结的形成可以有效的抑制光生电子和空穴对的结合,使其光催化活性明显优于纯的Zn O和Bi2WO6;另外,异质结型Bi2WO6/Zn O复合光催化剂的表面OH·自由基更有利于光催化活性的提高。当Bi2WO6复合量为4wt%时,异质结Bi2WO6/Zn O复合光催化剂光催化降解苯酚的效果最佳。