Effect of Drying Methods on the Structure and Combustion Activity of Mn—Substituted Hexaaluminate Catalysts

Conventional oven drying (COD) and supercritical drying (SCD) methods were applied to the preparation of Mn-substituted hexaaluminate (BaMnA111O19-α) catalysts. The effect of drying methods on phase composition, specific surface area, pore structure, reduction behavior of Mn^3 ions, and combus-tion activity of the samples was investigated. The homogenous mixing of the components in the sol-gel process could be maintained by SCD, and the hexaaluminate phase was almost the only phase of the resulting materials after calcination. H2-TPR revealed that the Mn^3 ions in the sample obtained by SCD were easier to be reduced than that by COD. Moreover, the samples obtained by SCD have higher surface area, narrower pore size distribution, and higher combustion activity than those obtained by COD.     

NCO自由基与SO_2、CS_2反应的速率常数

利用波长为266nm的激光光解CHBr3产生CH自由基,其与NO反应作为NCO自由基的来源.在298K,总压2660Pa的条件下,采用激光诱导荧光的方法,研究了NCO自由基与SO2、CS2的反应.得到了NCO自由基与SO2、CS2双分子反应速率常数分别为(1.8±0.3)×10-11和(3.1±0.4)×10-12cm3·molecule-1·s-1.对这两个反应在B3LYP/6-31 G(d)的水平上进行理论研究的结果表明,NCO自由基与SO2、CS2的反应是加成反应,其机理是NCO自由基中的N原子攻击反应物的中心原子,得到加成产物.     

Properties of nanobelts and nanotubes measured by in situ TEM.

Characterizing the physical properties of individual nanostructures is challenging because of the difficulty in manipulating the objects of sizes from nanometers to micrometers. Most nanomeasurements have been carried using scanning probe microscopy. In this article, we demonstrate that transmission electron microscopy can be a powerful tool for quantitative measurements of the mechanical and electrical properties of a single nanostructure. Dual-mode resonance of an oxide nanobelt has been observed, and its bending modulus has been measured. An in situ technique was demonstrated for measuring the work function at the tip of a carbon nanotube. The ballistic quantum conductance of a multiwalled carbon nanotube was observed at room temperature using the setup in TEM. It is concluded that in situ measurement by directly linking structure with property is a future direction of electron microscopy.     

Kinetics of catalytic combustion in air over Pt/Al2O3/Al catalyst

Summary Catalytic combustion of toluene, propylene and CO over Pt/Al₂O₃ /Al catalyst was investigated. Strong inhibition effects are observed when the mixture of toluene, propylene and CO is oxidized. A reaction mechanism of catalytic combustion over Pt/Al₂O/Al is proposed. The results from kinetic models are in good agreement with the experimental data.     

微波干法催化芳香醛与绕丹宁及N－苯基绕丹宁的缩合反应

利用微波辐射和固体碱性载体试剂催化绕丹宁及Ｎ－苯基绕丹宁和芳香醛的缩合反应合成了１４个绕丹宁衍生物并研究了影响反应的因素。     

活性碳分离碳－60和碳－70

活性碳用苯胺处理后，可以减少对Ｃ＿（６０）和Ｃ＿（７０）的不可逆吸附，从而增加Ｃ＿（６０）和Ｃ＿（７０）的分离收率，同时提高了Ｃ＿（７０）的纯度。     

反相高效液相色谱法半制备分离[T(4-MOP)PS4]卟啉的研究

本文研究了新水溶性5，10，15，20-四(4-甲氧基-3-磺酸苯基)卟啉[T(4-MOP)PS4]的反相高效液相色谱(HPLC)分离条件。采用Shimpack PREP-ODS半制备色谱柱，用含有10mmol／L四乙基碘化铵的乙腈-水(体积比25：75)为流动相，流速18mL/min，于418nm波长下检测。[T(4-MOP)PS4]与合成中生成的杂质组分完全分离。经此制备的卟啉纯度高，已成功地应用于自来水样中微量钴、锌、铜离子的HPLC测定中。     

液相合成方形PbS纳米晶的光学特性

采用一种简单、温和的液相合成方法制备了PbS纳米晶，利用透射电镜和高分辨透射电镜对PbS纳米晶的形貌与晶型结构进行了表征．研究了PbS纳米晶的光学吸收和光致发光特性，并比较分析了包覆剂聚乙烯吡咯烷酮(PVP)和回流时间对产物光学特性的影响．结果表明：PVP分子链中的O原子与纳米晶表面吸附的游离态Pb原子形成Pb-O配位键，使产物的激子吸收大为减弱，同时引起了表面浅束缚态能量的升高，最终导致了荧光淬灭现象．     

Determination of Dopamine in the Presence of Ascorbic Acid on the IrO2-Ta2O5 Type DSA Electrode

IrO2Ta2O5 (70%: 30%, molar ratio) electrodes (ITEs) were prepared by the thermal decomposition method. Typical “mud-cracked” surface and surface enrichment of Ta were observed. The determination of dopamine (DA) was carried out in the presence of ascorbic acid (AA). The detection limit of DA was 5~10 5 mol/L without the interference of AA.     

Controlled/“Living “Radical Polymerization of(-)-Menthyl Methacrylate

The atom transfer radical polymerization(ARP)of (-)-menthyl methacrylatc((-)-MnMA) mediated by CuCl/bipyridine and ethy1 2-bromopropionate or 1-phenylethyl bromide in THF system has been studied.The dependence of the specific rotation on molecular weight and the CD of Poly((-)-MnMA) thus obatined was investigated.