激光能量对反钙钛矿GaCMn_3薄膜结构与物性的影响

本文采用脉冲激光沉积方法在LaAlO3(001)单晶衬底上制备了反钙钛矿GaCMn3薄膜,通过控制制备过程中脉冲激光的能量,研究了不同激光能量条件对GaCMn3薄膜结构与物理性能的影响.分别利用X射线衍射仪、原子力显微镜、超导量子干涉仪和物理性能测试系统,对所制备的薄膜的晶体结构、表面形貌和磁性、电输运性质进行了研究.结果表明,制备的样品均为具有多个晶面取向的反钙钛矿薄膜,且薄膜结构和物性明显随制备激光能量的变化而变化.当激光能量为450mJ时,制备的薄膜多晶面取向性最弱,结晶性和表面形貌最优良.实验所得的薄膜均表现出顺磁-铁磁-反铁磁相转变,然而转变过程比块材较平缓,同时薄膜的电阻率并未表现出块材中的突变特征,我们推测该现象很可能是由衬底的应力及衬底的晶格膨胀对薄膜反常晶格变化的抑制作用造成的.     

PtII-Catalyzed Hydroxylation of Terminal Aliphatic C(sp3)−H Bonds with Molecular Oxygen

The practical application of Shilov-type Pt catalysis to the selective hydroxylation of terminal aliphatic C−H bonds remains a formidable challenge, due to difficulties in replacing Pt^IV with a more economically viable oxidant, particularly O₂. We report the potential of employing FeCl₂ as a suitable redox mediator to overcome the kinetic hurdles related to the direct use of O₂ in the Pt reoxidation. For the selective conversion of butyric acid to γ-hydroxybutyric acid (GHB), a significantly enhanced catalyst activity and stability (turnover numbers (TON)>30) were achieved under 20 bar O₂ in comparison to current state-of-the-art systems (TON<10). In this regard, essential reaction parameters affecting the overall activity were identified, along with specific additives to attain catalyst stability at longer reaction times. Notably, deactivation by reduction to Pt⁰ was prevented by the addition of monodentate pyridine derivatives, such as 2-fluoropyridine, but also by introducing varying partial pressures of N₂ in the gaseous atmosphere. Finally, stability tests revealed the involvement of Pt^II and FeCl₂ in catalyzing the non-selective overoxidation of GHB. Accordingly, in situ esterification with boric acid proved to be a suitable strategy to maintain enhanced selectivities at much higher conversions (TON>60). Altogether, a useful catalytic system for the selective hydroxylation of primary aliphatic C−H bonds with O₂ is presented.     

QEPAS系统中石英音叉模态仿真计算与研究

对石英音叉增强型光声光谱(QEPAS)系统中常用的石英音叉进行了有限元模态计算，获得石英音叉前6阶振型与模态频率，认知了第4阶对称摆动振型为有效振动，利用单因素法分析了石英音叉的音臂长度l₁、音臂宽度w₁、音臂厚度t、音臂切角θ、音臂圆孔直径d及音臂圆孔高度h对低阶有效共振频率(Fre)的影响，敏感度依次为： l₁> w₁>d>θ>t>h，考虑实际设计情形，筛选出了l₁，w₁，d与h四个石英音叉设计变量，采用Box-Behnken实验设计方案与RSM(response surface methodology)方法，以Fre为函数目标，建立l₁，w₁，d与h的二次回归响应面模型，得到了参数之间的交互作用，利用Design-Expert软件对响应面模型进行设计参数反求，结果表明，在15 000 Hz≤Fre≤25 000 Hz计算区域内误差较小，基本满足QEPAS系统的计算需求，所提出的研究与设计方法具有一定通用性，可为QEPAS系统中石英音叉结构参数设计提供参考。     

Numerical Evaluation of a Two-Loop Diagram in the Cutoff Regularization

The sunset diagram of λφ4 theory is evaluated numerically in cutoff scheme and a nonzero finite term(in accordance with dimensional regularization (DR) result) is found in contrast to published calculations. This findingdramatically reduces the critical couplings for symmetry breaking in the two-loop effective potential discussed in ourprevious work.     

扩宽OMA-Ⅵ同时谱宽的新方法

OMA－Ⅵ存在同时谱宽窄的缺点，本文用一种新方法大幅度地扩宽了它的同时谱宽，且不降低其系统分辨率，应用效果甚佳。     

钙钛矿型Sr_（1－x）Bi_xFeO_（3－y）系列物的结构、电性及铁氧化态研究

在１１００℃制备了钙钛矿型非计量系列物Ｓｒ_（１－ｘ）Ｂｉ_ｘＦｅＯ_（３－ｙ），与文献相比，明显具有温度低、时间短、能耗少的特点。用化学分析方法测得其化学式及Ｆｅ离子的平均价态，用ＸＲＤ、交流阻抗、ＩＲ、Ｍｏｓｓｂａｕｅｒ谱等方法研究了其结构与性质，该类化合物具有Ｐｍ３ｍ对称性和半导体性质，铁离子会产生电荷歧化现象。     

织构C60薄膜的生长与光致发光特性

用Hot Wal方法，在氟金云母单晶上生长出了（111）织构的C₆₀薄膜．用X射线衍射、Raman散射、扫描电子显微镜和原子力显微镜研究了织构C₆₀薄膜的结晶质量和结构特性．测量了织构C₆₀薄膜在室温300K和低温77K的光致发光光谱．对所得结果进行了分析与讨论 关键词：     

共沉淀法制备Y_2O_2S∶Eu~(3+),Mg~(2+),Ti~(4+)红色长余辉材料

用共沉淀法制备了Y2O2S∶Eu3 ,Mg2 ,Ti4 红色长余辉材料。测量了材料的电子显微形貌、晶体结构和发射光谱。通过与固相法制备的Y2O2S∶Eu3 ,Mg2 ,Ti4 长余辉材料比较,发现两种方法都可以制备粒度基本相同的纯相Y2O2S基质晶体,但共沉淀法样品的颗粒结构更松散。研究了Eu3 浓度对两种方法制备样品的谱线发射强度的影响,通过比较共沉淀法和高温固相法制备的样品中Eu3 的5D1→7F3较高能级跃迁的587.6 nm谱线强度随Eu3 浓度的变化,发现共沉淀法更有利于Eu3 均匀进入Y2O2S基质晶格而形成有效的发光中心。