Synthesis and electrochemical properties of P2-Na<Subscript>2/3</Subscript>Ni<Subscript>1/3</Subscript>Mn<Subscript>2/3</Subscript>O<Subscript>2</Subscript>

The pure phase P2-Na_2/3Ni_1/3Mn_2/3O₂ was synthesized by a solid reaction process. The optimum calcination temperature was 850 °C. The as-prepared product delivered a capacity of 158 mAh g^?1 in the voltage range of 2–4.5 V, and there was a phase transition from P2 to O2 at about 4.2 V in the charge process. The P2 phase exhibited excellent intercalation behavior of Na ions. The reversible capacity is about 88.5 mAh g^?1 at 0.1 C in the voltage range of 2–4 V at room temperature. At an elevated temperature of 55 °C, it could remain as an excellent capacity retention at low current rates. The P2-Na_2/3Ni_1/3Mn_2/3O₂ is a potential cathode material for sodium-ion batteries.     

Study on LiFe<Subscript>1 − <Emphasis Type="Italic">x</Emphasis></Subscript>Sm<Subscript><Emphasis Type="Italic">x</Emphasis></Subscript>PO<Subscript>4</Subscript>/C used as cathode materials for lithium-ion batteries with low Sm component

LiFe_1???x Sm _x PO₄/C cathode materials were synthesized though a facile hydrothermal method. Compared with high-temperature solid-phase sintering, the method can allow for the fabrication of low Sm content (2 %), a scarce and expensive rare earth element, while the presence of an optimized carbon coating with large amount of sp²-type carbon sharply increases the material’s electrochemical performance. The high-rate dischargeability at 5 C, as well as the exchange current density, can be increased by 21 and 86 %, respectively, which were attributed to the fine size and the large cell parameter a/c as much. It should be pointed out that the a/c value will be increased for the LiFePO₄ Sm-doped papered by both of the two methods, while the mechanism is different: The value c is increased for the front and the value a is decreased for the latter, respectively.