A novel supramolecular graft copolymer via cucurbit[8]uril-based complexation and its self-assembly

A novel supramolecular graft copolymer（SGP） composed of viologen-containing copolymer（P（DMA-co-diEV）） as the main chain and Np ended PNIPAM（Np-PN1PAm） as the grafts is prepared（DMA:N,N- dimethylacryamide,diEV:ethylviologen dimer,Np:naphthalene,PNIPAM:poly（N-isopropylacrylamide））. The grafting is based on the triple complexation among a host of cucurbit[8]uril（CB[8]）and two guests of diEV and Np,which is characterized by UV-vis spectra and ITC.Temperature sensitive property of PNIPAm moiety allows SGP to self-assemble into non-covalently connected micelle（NCCM） at high temperature. The micelles are sensitive to reducing agents,for example Na₂S₂O₃,which breaks the current inclusion complex pair and induces aggregation.     

微波诱导燃烧法合成类花状ZnO纳米材料及其晶体结构、荧光性质研究

以硝酸锌[Zn(NO3)2.6H2O]和尿素[CO(NH2)2]作前驱体,通过微波诱导燃烧技术可控合成具有不同形貌的ZnO纳米晶体,并用热重分析和差热分析进行了研究。对各种生长条件:微波功率,辐射时间和尿素/Zn2+物质的量的比对ZnO纳米晶体形貌的影响作了分析。结果表明:尿素/Zn2+物质的量的比对ZnO纳米材料的形貌具有显著影响。X衍射图表明合成的ZnO纳米结构呈六角形。傅里叶变换红外光谱图中400~500 cm-1处明显的峰为Zn-O的振动峰。ZnO纳米结构的发光光谱在366 nm的带边发射,因缺陷又由许多可见光发射峰组成。用扫描电子显微镜、透射电子显微镜、选区电子衍射研究了花状ZnO纳米结构的增长机理。本方法仅需几分钟就获得的了ZnO纳米结构。     

氨基三唑分子印迹聚合物的制备及性能表征

采用分子印迹技术,以氨基三唑(AMI)为模板分子,异丁醇为溶剂,甲基丙烯酸(MAA)为功能单体,乙二醇二甲基丙烯酯(EDMA)为交联剂,合成了氨基三唑分子印迹聚合物(AMI-MIP)。采用静态平衡结合实验和选择性实验评价了AMI-MIP对底物分子的结合特性及分子识别性能,并进行了吸附动力学研究。结果表明,AMI-MIP对AMI存在不同亲和力的两类结合位点,且对AMI具有很高的选择吸附特性和良好的分子识别性能,AMI-MIP对AMI的吸附行为可用准二级吸附动力学方程加以描述。     

三种查尔酮类化合物与人血清白蛋白相互作用及其构效关系研究

在模拟人体生理条件下,采用紫外光谱法、荧光光谱法和同步荧光光谱法研究查尔酮、4′-甲氧基查尔酮和4′-氯查尔酮与人血清白蛋白(HSA)的相互作用及其构效关系。实验表明:三种查尔酮类化合物对HSA的荧光猝灭机制主要为静态猝灭,与HSA均形成1∶1复合物,结合常数K分别为2.50×104、0.697×104和0.277×104 L.moL-1,结合距离r分别为3.78、3.93和4.25nm,其作用力均以氢键和范德华力为主。查尔酮类化合物中取代基的不同对其与HSA的结合产生影响,其作用力大小依次为查尔酮>4′-甲氧基查尔酮>4′-氯查尔酮。     

聚苯乙烯提取物的检测与评价

随着材料科学的迅速发展,聚合物材料以不同的形态越来越广泛地应用于食品包装中。但是由于聚合物材料自身的特性及其改性加工,导致了很多低分子量化合物的形成,因而给食品安全性带来很大隐患,也危害着人们的身体健康。为了解决这一问题,在选用材料前,必须分析聚合物材料中低分子化合物的迁移情况,考虑迁移过程对包材使用的影响。实验中选用正庚烷、8%乙醇、50%乙醇和蒸馏水作为食品模拟液,用气相色谱测定聚苯乙烯提取物的迁移量,进而将实验数据分析比较。结果显示,迁移量随着温度的升高和时间的延长而不断增加,溶剂种类的影响为:正庚烷>50%乙醇>8%乙醇>蒸馏水。     

多孔炭载聚钴酞菁修饰电极用于苯二酚的电催化及检测

以二氧化硅纳米球为模板,通过葡萄糖的水热聚合反应制备了具有三维结构的多孔炭(PC)。采用电化学聚合方法将单体钴酞菁聚合在多孔炭修饰的玻碳电极(PC/GC)表面,制备了多孔炭载聚钴酞菁的修饰电极(Co-TAPc/PC/GC)。通过循环伏安法(CV)研究了间苯二酚、邻苯二酚和对苯二酚在此修饰电极的电化学响应。结果表明,相对于裸玻碳电极、多孔炭或聚钴酞菁单独修饰的电极,该修饰电极对3种同分异构体的酚类物质均有更好的电催化活性。利用计时安培技术,该修饰电极对间苯二酚、邻苯二酚及对苯二酚分别在5.0×10-6～5.0×10-4 mol/L,6.0×10-6～2.5×10-4 mol/L和2.0×10-6～8.0×10-4 mol/L范围内具有较好的线性响应。此修饰电极具有制备简单、响应灵敏、稳定性好等优点。     

Effect of Plasma Treatment on the Structures and Properties of Konjac Glucomannan Film

To understand the effect of plasma treatment on the Konjac glucomannan film, the nitrogen plasma was injected into the film by ion beam injection machine in this study. The structures and properties of Konjac glucomannan film after plasma treatment were analyzed by Infrared spectroscopy, Raman spectrum, X-ray, ect. The result showed that nitrogen groups appeared in the KGM molecular chain and part of this chain fractured, and the number of hydrogen bonds increased after the treatment of plasma. The form of KGM molecule remained amorphous non-crystalline state, but the crystalline region was increased and became more ordered. The mechanical property of tensile strength and breaking elongation was improved, while the WVP was decreased. The nitrogen groups were grafted on the KGM molecular chain after plasma treatment, which led to the improvement of the properties of KGM film.     

稀释蒸汽中Na+及积炭对甲醇制丙烯催化剂性能影响

考察了稀释蒸汽中Na⁺及积炭对甲醇制丙烯(MTP)催化剂物理化学性质和催化性能影响, 及离子交换后催化性能. 采用X射线衍射(XRD)、扫描电镜(SEM)、X射线荧光(XRF)光谱、N₂吸附-脱附、程序升温氨脱附(NH3-TPD)和热重(TG)分析等方法对失活和再生催化剂进行了表征, 并在101325 Pa、470℃ 和甲醇空速(WHSV)为1.0-3.0 h^-1的反应条件下, 采用连续流动固定床微型反应器考察其催化甲醇制丙烯性能. 结果表明: MTP反应970 h后的催化剂晶体结构和形貌没有受到明显破坏, 但稀释蒸汽中Na⁺极易扩散至催化剂表面,部分取代H质子的位置, 从而使催化剂酸性逐渐下降而中毒失活; 另外, MTP催化剂表面的积炭导致分子筛微孔堵塞是造成其失活的主要原因, 可通过烧炭再生过程消除, 而水蒸汽脱铝对催化剂性能的影响缓慢但更严重. 用再生和离子交换处理后, Na⁺中毒催化剂MTP反应性能基本完全恢复. 在470 h反应过程中, 甲醇转化率保持在99%以上, 丙烯选择性大于46%, 且随着反应时间的延长, 丙烯选择性逐渐升高、乙烯选择性逐渐下降.     

AgGa(S1-xSex)2固溶体的电子结构和光学性质

采用基于赝势平面波基组的密度泛函理论方法, 对一系列具有黄铜矿结构的AgGa(S_1-xSe_x)₂固溶体的构型、电子结构、线性和二阶非线性光学性质进行了系统研究. 结果表明, 各固溶体具有类似的能带结构, 体系带隙随x值增加而逐渐减小. 当所引入的Hartree-Fock交换项贡献为22.56%时, 对应的杂化PBE泛函得到的带隙值与实验结果相近. 固溶体的各种光学性质, 包括折射率、双折射率、反射率、吸收系数和二阶倍频系数等均随着组成的改变呈现出有规律的变化趋势, 变化范围介于AgGaS₂和AgGaSe₂二者之间. 因此, 利用固溶体光学性质的变化规律, 可从中寻找出具有特定光学性能的晶体材料.     

Ca0.8-2x(YbxTb0.1Na0.1+x)2xWO4近红外下转换荧光粉水热合成及发光性质

一种在近红外光谱(NIR)区域高效的量子剪裁现象已在Ca0.8-2x(Ybx Tb0.1Na0.1+x)2x WO4(x=0～0.2)荧光粉中得到证实,该量子剪裁通过吸收紫外线光子发射近红外光子,能量传递包括两个协同过程,分别是WO42-基团到Yb3+离子和WO42-基团到Tb3+离子再到Yb3+离子,Yb3+离子的掺杂浓度对荧光粉在可见光和近红外光谱的发光,荧光寿命和量子效率的影响已进行了详细的研究。经计算,量子效率最大达到135.7%。铽与镱共掺钨酸钙的近红外量子剪裁,通过吸收太阳光谱的1个紫外光子到2个1 000 nm光子(2倍光子数增加)的下转化机制实现高效率硅太阳能电池的途径。