Photochemical etching of GaAs with Cl2 induced by synchrotron radiation

The quality and efficiency of etching at room temperature is determined in the wavelength range from 105 nm to 300 nm by replicating a mask on a GaAs(100) wafer and by wavelength selection of synchrotron radiation with filters and a monochromator. A good anisotropy and selectivity is found for Cl₂ pressures from 10^–2 mbar up to 1.5 mbar, but above 3 mbar the selectivity is lost. Efficiencies for stimulation of the chlorination reaction and for desorption are separated and an optimal efficiency for stimulation of about 100 removed Ga and As atoms per photon is obtained around a wavelength of 122 nm at 1.5 mbar. Growth of reaction products on the surface occurs for short wavelengths and transport processes through layers up to a thickness of 350 nm are relevant. The efficiency and quality of etching can be improved by additional desorption with long wavelengths especially with lasers.     

Metal core bonding motifs of monodisperse icosahedral Au13 and larger Au monolayer-protected clusters as revealed by X-ray absorption spectroscopy and transmission electron microscopy

The atomic metal core structures of the subnanometer clusters Au13[PPh3]4[S(CH2)11CH3]2Cl2 (1) and Au13[PPh3]4[S(CH2)11CH3]4 (2) were characterized using advanced methods of electron microscopy and X-ray absorption spectroscopy. The number of gold atoms in the cores of these two clusters was determined quantitatively using high-angle annular dark field scanning transmission electron microscopy. Multiple-scattering-path analyses of extended X-ray absorption fine structure (EXAFS) spectra suggest that the Au metal cores of each of these complexes adopt an icosahedral structure with a relaxation of the icosahedral strain. Data from microscopy and spectroscopy studies extended to larger thiolate-protected gold clusters showing a broader distribution in nanoparticle core sizes (183 +/- 116 Au atoms) reveal a bulklike fcc structure. These results further support a model for the monolayer-protected clusters (MPCs) in which the thiolate ligands bond preferentially at 3-fold atomic sites on the nanoparticle surface, establishing an average composition for the MPC of Au180[S(CH2)11CH3]40. Results from EXAFS measurements of a gold(I) dodecanethiolate polymer are presented that offer an alternative explanation for observations in previous reports that were interpreted as indicating Au MPC structures consisting of a Au core, Au2S shell, and thiolate monolayer.     

Sorption of inorganic nanoparticles in woven cellulose fabrics

Titanium dioxide was deposited from aqueous suspension onto cellulosic surfaces.Titania was sourced from Degussa (P25TM,70:30 anatase:rutile).Dry uptake of particles was shown to be rapid and dominant with one-third of the deposition occurring in less than 30 s and over one-half in the first minute.Isotherms were recorded to compare the rate of titanium deposition on dry and pre-wetted cotton.In the dry case uptake reached a maximum in 30 min whereas in the pre-wetted case the uptake was seen to continue beyond 180 min.A broad trend of higher deposition occurring at lower pH was seen,corresponding to the region where surface charges were opposite and thus attractive.Dry pickup was less significant at high pH.The response to varying ionic strength was complex and was attributed to the combined effect of charge screening,particle aggregation and consequent particle entrapment or occlusion.Titania deposition into the interstices of woven cotton sheets resulted in the formation of inorganic,nanoparticulate skeletons which could be isolated by controlled combustion of the cellulose and thus cotton was suggested to have potential for the templated synthesis of high surface area semiconductor materials.     

Syntheses and reactions of some fluorinated dienes,cyclobutenes and furans

There are many reports¹ of the pyrolysis of fluorinated organic compounds, including the defluorination of cyclic fluorocarbons over iron to give aromatic compounds. Extending this technique we have investigated the flow pyrolysis of some readily accessible unsaturated fluorocarbons, such as I, II, and III, and found these to be synthetically

useful routes to fluorinated dienes, cyclobutenes, and furans. Pyrolyses were carried out using a nitrogen flow over platinum, iron or caesium fluoride heated at 430–700°. The various products can all be rationalized in terms of intermediate allylic radicals, and the solid substrate influences which allylic radicals are formed.We are also investigating the chemistry of those now accessible compounds, such as IV, V, and VI, and some of the preliminary results are described.

For example the fluoride ion induced dimerisation of IV gave two major products VII and VIII via a particular interesting mechanism.