Synthesis of self‐photosensitizing polyesters containing donor–acceptor norbornadiene moieties and benzophenone groups and their photochemical reactions

The ring‐opening copolymerization of a glycidyl ester derivative having a benzophenone group and the donor–acceptor norbornadiene (D‐A NBD) dicarboxylic acid, 5‐(4‐methoxyphenyl)‐1,4,6,7,7‐pentamethyl‐2,5‐norbornadiene‐2,3‐dicarboxylic acid, monoglycidyl ester derivatives with D‐A NBD dicarboxylic anhydride using tetraphenylphosphonium bromide as a catalyst proceeded smoothly to give novel self‐photosensitizing NBD polymers in good yields. The molecular weight of these polyesters was about 4,000, and lower than that of analogous NBD polymers having no benzophenone group. All the synthesized NBD polymers isomerized smoothly to the corresponding quadricyclane (QC) polymers upon UV irradiation in tetrahydrofuran (THF) solution and in the film state. The rate of the photoisomerization of the D‐A NBD moieties in these polymers was higher than that of the D‐A NBD moieties in the polymer having no photosensitizing group. Furthermore, the rate of the photoisomerization of the D‐A NBD moieties in these polymers was also higher than that of the NBD polymer with low molecular weight photosensitizer in dilute solution. The photo‐irradiated polymers having QC moieties released thermal energies of 146–180 J/g. The D‐A NBD moieties contained in these NBD polymers possessed fair to good fatigue resistance. The degradation of the NBD moieties in these polymers was 15–30% after 50 repeated cycles of interconversion. © 2007 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 45: 2978–2988, 2007     

Synthesis and orientation study of a magnetically aligned liquid‐crystalline chitin/poly(acrylic acid) composite

A high magnetic field of 5 T was used to fabricate a magnetically aligned, optically anisotropic, liquid‐crystalline chitin/poly(acrylic acid) composite. The aligned mesophase was fixed by photoinitiated free‐radical polymerization. From an examination of polarized optical micrographs and an X‐ray diffraction study, a high degree of orientation of 0.70 was observed for the composite with a higher liquid‐crystalline chitin concentration (10.70 wt %); the orientation was reduced with a decreased chitin concentration at a given acrylic acid concentration. The X‐ray data for the developed composite showed a uniplanar orientation for the chitin crystallites, with its molecular long axes perpendicular to the direction of the magnetic field. © 2003 Wiley Periodicals, Inc. J Polym Sci Part B: Polym Phys 41: 711–714, 2003     

Effect of the pore surface modification of an inorganic substrate on the plasma‐grafting behavior of pore‐filling‐type organic/inorganic composite membranes

We have investigated the effect of the surface state and surface treatment of the pores of an inorganic substrate on the plasma‐grafting behavior of pore‐filling‐type organic/inorganic composite membranes. Shirasu porous glass (SPG) was used as the inorganic substrate, and methyl acrylate was used as the grafting monomer. The grafting rate increased as the density of silanol on the SPG substrate increased. This result suggests that radicals are generated mainly at the silanol groups on the pore surface by plasma irradiation. The SPG substrates were treated with silane coupling agents used to control the mass of organic material bonded to the pore surface. The thickness of the grafted layer became thinner as the mass of organic material bonded to the pore surface of SPG increased. This decrease in the thickness of the grafted layer could be explained by the decrease in the penetration depth of vacuum ultraviolet rays contained in plasma having a wavelength of less than 160 nm that generated radicals in the pores of the substrate. The thickness of the grafted layer inside the SPG substrates could be controlled through the control of the mass of organic material bonded to the pore surface of the SPG substrate. © 2005 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 44: 846–856, 2006     

Preparation and certification of the new reference materials; plastics (disk form, JSAC 0621-0625) for determination of mercury using x-ray fluorescent analysis.

The Japan Society for Analytical Chemistry has developed some new plastic certified reference materials (CRMs) for the analysis of mercury in polyester disks using XRF analysis. These CRMs (named as JSAC 0621-0625) were prepared by casting polyesters including a toluene solution of organometallic compounds as a standard. Concentrations of the five levels of mercury ranged from 0 to 250 mg/kg. Homogeneity tests of prepared disks had shown excellent results. Interlaboratory comparison study for the certification was performed by 15 laboratory participants. The z-scores in robust statistical method was applied for the evaluation of outliers. The certified values were assigned after discarding outliers. The uncertainties of certified values were determined as the confidence levels of 95%.     

Catalytic property of Europium supported on alumina from its ammoniacal solution

Europium supported on alumina (Eu/Al₂O₃) was prepared by impregnation from an ammoniacal solution of the metal. The catalytic activity of Eu/Al₂O₃ for the isomerization of 2,3-dimethylbut-1-ene to 2,3-dimethylbut-2-ene was examined. Eu/Al₂O₃ showed the highest catalytic activity for the isomerization when heated under a vacuum at 523 K, the yield of 2,3-dimethylbut-2-ene in 20 min being 81.6% at 314 K. IR spectrum shows the presence of two kinds of Eu amides. The change of the IR spectra and the catalytic activities with evacuation temperature suggest that only one of the two Eu amides is catalytically active for this base-catalyzed isomerization.     

A novel transformation of a 1 : 1 : 1 racemic complex of 2,2'-dihydroxy-1,1'-binaphthyl, Me4N+ Cl- and MeOH into a conglomerate in the solid state by heating or contact with MeOH vapour

The title racemate-to-conglomerate transformation which occurs in the solid state on heating or contact with MeOH vapour has been studied by IR and DTA spectral measurements, microscopic observation, and by X-ray structural and X-ray powder diffraction analysis.