Microstructure evolution and passivation quality of hydrogenated amorphous silicon oxide(a-SiOx:H) on〈100〉- and 〈111〉-orientated c-Si wafers

Hydrogenated amorphous silicon oxide(a-SiOx:H) is an attractive passivation material to suppress epitaxial growth and reduce the parasitic absorption loss in silicon heterojunction(SHJ) solar cells. In this paper, a-SiOx:H layers on different orientated c-Si substrates are fabricated. An optimal effective lifetime(τ(eff)) of 4743 μs and corresponding implied opencircuit voltage(iV(oc)) of 724 mV are obtained on〈100〉-orientated c-Si wafers. While τ(eff) of 2429 μs and iV_oc of 699 mV are achieved on 111-orientated substrate. The FTIR and XPS results indicate that the a-SiOx:H network consists of SiOx(Si-rich), Si–OH, Si–O–SiHx, SiO2 ≡ Si–Si, and O3 ≡ Si–Si. A passivation evolution mechanism is proposed to explain the different passivation results on different c-Si wafers. By modulating the a-SiOx:H layer, the planar silicon heterojunction solar cell can achieve an efficiency of 18.15%.     

毫米波速调管电子光学系统的研究

电子光学系统是毫米波速调管长寿命和整管性能实现的关键,毫米波速调管零件尺寸较小,为了在Ka波段和W波段实现千瓦量级的输出功率,要求具有高的电子注通过率及低的阴极负荷。对Ka波段和W波段电子光学系统特性进行了分析,确定了Ka波段10 kW分布作用速调管和W波段1 kW分布作用速调管电子光学系统的设计方案,利用软件对电子枪和聚焦系统的结构进行计算,并采用CST仿真软件对设计的电子枪发射的电子注在聚焦磁场中的状态进行优化。设计出的Ka波段速调管电子光学系统,电子枪工作电压26 kV,发射电流2 A,互作用区长度30 mm,磁场强度大于0.6 T,流通达到100%。设计的W波段速调管电子光学系统,电子枪工作电压17 kV,电流0.65 A,互作用区长度20 mm,磁场大于0.9 T,流通达到100%。已制成Ka波段速调管和W波段速调管,设计的电子光学系统能够满足速调管工程化需求。     

Free control of far-field scattering angle of transmission terahertz wave using multilayer split-ring resonators’ metasurfaces

To enhance transmission efficiency of Pancharatnam–Berry (PB) phase metasurfaces, multilayer splitring resonators were proposed to develop encoding sequences. As per the generalized Snell’s law, the deflection angle of the PB phase encoding metasurfaces depends on the metasurface period’s size. Therefore, it is impossible to design an infinitesimal metasurface unit; consequently, the continuous transmission scattering angle cannot be obtained. In digital signal processing, this study introduces the Fourier convolution principle on encoding metasurface sequences to freely control the transmitted scattering angles. Both addition and subtraction operations between two different encoding sequences were then performed to achieve the continuous variation of the scattering angle. Furthermore, we established that the Fourier convolution principle can be applied to the checkerboard coded metasurfaces.     

一个二维梯状化合物[Ni(μ1，5-dca)2(en)]n的合成，结构和磁性(英)

A new nickel(Ⅱ)-dicyanamide compound, [Ni(dca)₂(en)]_n (1) (dca=dicyanamide anion, [N(CN)₂]^-); en=ethylene diamine), has been synthesized and its structure has been determined by single crystal X-ray diffraction analysis. The crystal is monoclinic, space group P2₁/n with unit cell dimensions: a=0.694 3(1) nm, b=1.041 5(2) nm, c=1.4132(2) nm, and β=90.381°, Z=4, V=1.011 0(3) nm³. In this compound, the adjacent nickel atoms are connected by dca all in μ_1，5-bridging mode to form ladder-like units, which are linked with double dca bridges to generate a regular infinite stair-like structure. Temperature-dependent magnetic susceptibility was also characterized for this compound. CCDC: 208276.     

NaGd(WO 4)2∶Yb^3+,Ho^3+,Cr^3+微米晶的上转换发光与温度特性

采用水热法制备了NaGd(WO4)2(NGW)∶Yb^3+,Ho^3+,Cr^3+微米晶。研究了Cr^3+离子掺杂浓度对样品的晶体结构、微观形貌、上转换发光及温度传感特性的影响。在980 nm激光激发下,所有样品均发射以546 nm为中心的较弱绿光和以660 nm为中心的强红光,分别对应于Ho^3+离子的5F4,5S2→5I8和5F5→5I8能级跃迁。随Cr^3+离子掺杂量增加,绿光发射峰强度逐渐减弱,而红光发射先增大后减小,在10%时达到最大,样品色坐标逐渐向红色区域偏移。样品的变温光谱表明,NGW∶Yb^3+,Ho^3+,10%Cr^3+微米晶具有很好的温度特性,其测温灵敏度在486 K时达到最大,约为0.0337 K^-1,比NGW∶Yb^3+,Ho^3+的灵敏度提高近1倍。     

掺Cr半绝缘GaAs中Si离子注入的载流子分布尾研究

本文研究了掺Cr半绝缘GaAs中²⁸Si⁺注入后的载流子浓度分布尾,包括退火温度和时间的影响。应用计算机模拟了分布尾对GaAsMESFET器件输出特性的影响,与实测结果符合,表明分布尾会造成器件输出特性异常。讨论了产生分布尾的原因,认为与GaAs衬底中残留Si等浅施主杂质和高温退火时Cr再分布有关。 关键词：     

Nonsteady sink and source in a rotating fluid

The effect of the Coriolis force on the nonsteady two-dimensional sink or source flow has been studied theoretically. With the assumptions of incompressibility and invisddity of fluid, the equations governing the flow are still non-linear. However, a set of analytical and exact solutions is obtained for the velocity and pressure distributions. The result shows that no significant vortex flow can be induced by a source flow, the circulation produced there mainly is because the observer is moving with the rotating system; however, a sink will always induce a vortex, the strength of circulation in the sink flow is simply in proportion to the rotating speed of the system and the time integrated sink strength. As the system is under a constant rotating speed, the circulation will vanish only when the time integrated sink strength vanishes. Several special cases of sink strength are examined and their results are presented in this paper. The purpose of this study is mainly to relate the strength of circulation with the strength of sink and source. Consequently, it- can be applied to the weather forecast for hurricanes or tornadoes.     

两种Mannich碱对铜在碱性介质中的缓蚀作用与吸附行为

合成了两种曼尼希碱4-（1H-四唑-5-氨基）-V-2-酮（TB）和3-（1H-四唑-5-氨基）-1-苯基丙-1-酮（TP）,并采用失重法和电化学方法研究了这两种化合物对铜在5％（w）NaHCO3水溶液中的缓蚀性能和吸附行为．结果表明,在5％NaHCO3水溶液中,这两种化合物对铜均有较好的缓蚀作用,缓蚀效率顺序为TB〈TP;TB和TP均为阳极型缓蚀剂．两种化合物在铜表面的吸附过程为放热过程,其吸附行为服从Langmuir吸附等温式,属于物理吸附．