大尺寸掺钕和掺铥铝酸钇晶体的生长和退火技术

通过分析铝酸钇(YAP)晶体产生孪晶、开裂、色心和弥散性散射的原因,探讨了克服这些缺陷和问题的技术途径.采用提拉法生长了b轴方向的掺钕和掺铥铝酸钇(Nd:YAP和Tm:YAP)晶体,通过温场系统、生长工艺参数和切割工艺的优化,克服了晶体开裂的问题,晶体直径达到46mm;通过真空退火工艺,既显著减轻了紫外和可见区的色心吸收,又减小了晶体的应力,有助于克服晶体在加工过程中的开裂问题.晶体生长实验和晶体的显微观察表明:YAP晶体中的弥散状散射很可能同熔体中组分的均匀性有关,通过增大晶体的直径,增强强迫对流有助于减轻晶体中的弥散状散射.高质量b轴Nd:YAP和a轴Tm:YAP晶体已分别实现二极管泵浦大于140W的1.079μm和大于10W的1.99μm激光输出.     

固相萃取/超高效液相色谱-串联质谱法测定化妆品中12种合成着色剂

建立了固相萃取/超高效液相色谱-串联质谱法(SPE/UPLC-MS/MS)同时测定指甲油、眼影、唇膏等化妆品中12种合成着色剂(酸性紫49、颜料红57、颜料红53∶1、酸性黄36、结晶紫、罗丹明B、分散黄3、颜料橙5、苏丹红Ⅰ、苏丹红Ⅱ、苏丹红Ⅳ和溶剂蓝35)的分析方法。样品用四氢呋喃(THF)、二甲基亚砜(DMSO)和甲醇分步超声波辅助萃取,HLB固相萃取柱净化后,在Acquity UPLC BEH-C18(2.1 mm×50mm,1.7μm)色谱柱上分离,乙腈和0.05%甲酸溶液为流动相梯度洗脱,采用多反应监测(MRM)模式进行检测,基质外标法定量。结果表明:12种着色剂在6 min内均显示较好峰形,其线性范围为0.5~800μg·L-1,相关系数均大于0.99。定量下限(LOQ,S/N10)为1.4~2 000μg·kg-1。在指甲油、眼影和唇膏中分别添加0.025~20 mg·kg-1浓度的着色剂进行加标回收实验,测定回收率为60.8%~118.0%,相对标准偏差(RSD)为2.3%~10.8%。该方法快速、简便、灵敏,适用于油状、粉状及膏状化妆品中禁限用着色剂的定量和确证分析。     

傅立叶变换红外光谱法对聚氯乙烯及邻苯二甲酸酯类增塑剂的快速鉴定

应用傅立叶变换红外光谱法实现了聚氯乙烯及邻苯二甲酸酯类增塑剂的快速鉴别。对聚氯乙烯的定性采用了衰减全反射技术,用锗作为晶体材料,对邻苯二甲酸酯类的定性则采用透射法。用溶解-沉淀法对试样进行分离和纯化,所用溶剂为四氢呋喃,沉淀剂为无水乙醇。经过此方法,聚合物与增塑剂达到很好的分离和纯化。     

热致液晶共聚酯／Nylon－1010共混物的研究

利用偏光显微镜（ＰＬＭ），差示扫描量热计及广角Ｘ－射线衍射等手段研究了热致液晶共聚酯／Ｎｙｌｏｎ－１０１０共混体系．发现当热致液晶共聚酯（ＨＴＨ１０）含量达到３０％时共混物微结构与纯ＨＴＨ１０相似．尼龙－１０１０的结晶度先是随ＨＴＨ１０含量增加而增加，随后又随之下降，但其结晶温度却随ＨＴＨ１０加入而单调下降，共混物的熔融热焓△Ｈｍ在ＨＴＨ１０含量为３０％时与计算值有较大的偏差，广角Ｘ－射线衍射结果表明，此时共混物结构发生了较为明显的变化，两组份之间在此时存在一定的相互作用．     

聚（β－羟基丁酸酯）／聚双酚A羟基醚共混体系相容性及结构的研究

ＤＳＣ和ＦＴＩＲ测试表明，结晶／非晶共混体系聚（β－羟基丁酸酯）（ＰＨＢ）／聚双酚Ａ羟基醚（ＰＢＨＥ）是部分相容的．熔融结晶退火可以大大提高共混物的结晶度，增加其相容性，７５／２５组分ＰＨＢ相结晶度最大，５０／５０组分（０２０）、（１３０）晶面微晶尺寸最大．ＳＡＸＳ研究表明，纯ＰＨＢ的中间层约为１．５ｎｍ，片层厚约４．０ｎｍ；共混物的中间层在２．０ｎｍ左右，片层厚在５．０—７．２ｎｍ之间，５０／５０组分片层最厚．７５／２５组分晶相和非晶相的密度差最大．     

热致液晶乙基纤维素与尼龙－1010共混物的研究

在自制单螺杆小型挤出机上通过熔融共混的办法，制备了不同配比（５／９５—２５／７５）的ＥＣ／Ｎｙｌｏｎ—１０１０共混物．用ＷＡＸＤ、ＤＳＣ、毛细管流变仪、力学性能测试等方法对共混物进行了研究．发现共混后尼龙－１０１０的形态结构有明显改变，其强度、模量都有提高，在高剪切速率下，共混物粘度大大降低．配比为１５８５时，这些性能的改进尤为明显．     

Ⅱ conjugation in the butadiene

The π electronic delocalization in trans-C4H6 and cis-C4H6 has been investigated in the frame of ab initio valence bond theory with 6-31G basis set. The result shows that the Csp2-Csp2 single bond length (1.506 A) is only about 0.024 A shorter than the Csp3-Csp3 bond, thus the central bond length shortening would be mainly due to π conjugation. The theoretical resonance energies of the trans-C4H6 and cis-C4H6 are 8.48 and 7.44 kcal/mol, respectively.     

Utilization of a spiropyran derivative in a polymeric film optode for selective fluorescent sensing of zinc ion

Spiropyrans are the most studied families of func- tional materials due to their reversible structural con- version in response to external optical, chemical, and thermal stimulation[1]. Irradiation with ultraviolet light causes formation of an extended π-conjugation open form (merocyanine form) by heterolytic cleavage of the C (spiro)-O bond, which generates an intense ab- sorption in the visible region. Under the irradiating of visible light, the opened form will come back to the closed spi…     

一种二维多孔窗口型膦酸锆材料的合成及其对不同金属离子的吸附性能

合成了一种二维窗口型膦酸锆材料β-丙氨酸-N,N-双亚甲基膦酸锆(ZrNCP),采用X射线衍射仪、扫描电镜、透射电镜分析了合成产物的相组成和微观结构;利用N2吸脱附试验装置测定了合成产物对不同金属离子的吸附性能,考察了浓度、温度及pH对其吸附性能的影响.结果表明,合成产物内部存在大量分布均匀的微介孔,材料微观形貌为规整片状.随着金属离子半径的增大,ZrNCP对各种金属离子的平衡吸附量(mmol/g)呈逐渐减小趋势.     

扫帚状氧化铈制备及其对Pt基阳极催化剂催化性能的影响

采用水热合成法,合成了比表面积为175 m²·g^-1,孔径在2~4nm范围内的扫帚状CeO₂。通过微波辅助乙二醇还原氯铂酸法制备了Pt-CeO₂/RGO催化剂,探究扫帚状CeO₂的添加对Pt基催化剂电催化性能的影响。利用X射线衍射仪（XRD）、扫描电镜（SEM）、N₂吸附-脱附、X射线光电子能谱（XPS）对所制备的CeO₂及催化剂进行表征。利用电化学工作站对催化剂进行电化学性能测试。结果表明,催化剂中CeO₂保持原有扫帚状,Pt纳米粒子均匀分布于石墨烯载体表面;当m_RGO∶m_CeO2=1∶2时,添加了扫帚状CeO₂的Pt-CeO₂/RGO催化剂的电催化性能最优,电化学活性表面积为102.83 m²·g^-1,对乙醇氧化的峰值电流密度为757.17 A·g^-1,1 000 s的稳态电流密度为108.17 A·g^-1,对乙醇催化氧化反应的电荷转移电阻最小,活化能最低。