DEHYDROGENATION AND AROMATIZATION OF METHANE IN THE ABSENCE OF OXYGEN OVER DOPED Mo/HZSM-5 CATALYSTS

研究了在Ｍｏ／ＨＺＳＭ－５催化剂上添加助剂以及不同的反应预处理温度对甲烷无氧脱氢芳构化反应的影响。实验结果表明，由于第二组分的添加，Ｍｏ／ＨＺＳＭ－５催化剂的活性和选择性都得到了较大程度的改善。预处理温度是影响催化剂反应性能的关键因素。Ｍｏ－Ｒｕ／ＨＺＳＭ－５催化剂经过８７３Ｋ空气预处理后，甲烷在９７３Ｋ的转化率约为１０％，催化剂的稳定性也得到较大程度的提高。ＴＰＳＲ实验结果表明，Ｒｕ的加入降低了芳烃生成的温度。ＴＰＯ和ＤＴＡ实验结果表明，在Ｍｏ－Ｒｕ／ＨＺＳＭ－５催化剂上可生成较多的碳物种，结合反应结果，可以认为反应过程中生成的碳物种对甲烷的无氧脱氢芳构化反应是起积极作用的     

BEHAVIOR OF SUPPORTED NANO-COPPER CATALYST IN CO OXIDATION

IntroductionNanomaterialisanewkindofmaterialwithparticlesizebetWeenIurnand100urn.Becauseofthesmallparticlesizeandthelargespecificsufficearea,nanomaterialpossessesmanyparticularproperties,suchashighersufficeenergyandhighersurfaceactivity.t.[l]Thehigheracti…     

Promoting effect of sol-gel method and pre-treatment on the activity of SnO2/Al2O3 catalyst for NO reduction by propene

SnO₂/Al₂O₃ catalyst prepared by sol-gel method showed higher activity than those prepared by impregnation method, and their activity was significantly improved by pre-treatment in the reaction gas. The increased activity is closely related to the agglomeration of SnO₂ species and the re-exposure of Al₂O₃, which was previously covered by dispersed SnO₂ species. This revised version was published online in June 2006 with corrections to the Cover Date.     

红外光谱法研究LB膜中的分子取向

The structure information of orientation and packing of molecular chains can be obtained from infrared transmission and reflection-absorbance (RA) spectra. In the present paper, on the basis of Umemura et al., their FORTRAN program of minicomputer was developed and can be run on 486 personal computer. By comparison of infrared transmission and RA intensities, surface enhancement factors and molecular orientation angle were calculated using the above program, and the influence of complex refractive index, angle of incidence, and thickness of LB film were discussed. These results are consistent with that of Umemura et al.     

Semipreparative separation and determination of eleutheroside E in Acanthopanax giraldii Harms by high-performance liquid chromatography

A method for the isolation, purification, and determination of eleutheroside E in Acanthopanax giraldii Harms, collected in the Sichuan province (China), is established. The water extraction of A. giraldii Harms is pre-isolated using macroporous adsorption resin (D-101) and a C18 solid-phase extraction cartridge, and the enriched extract is purified to give eleutheroside E (syringaresinol-di-O-beta-D-glucoside; liriodendrin) by semipreparative reversed-phase high-performance liquid chromatography. Structure identification is performed by a comparison of IR, 1H-NMR, 13C-NMR, and electrospray ionization-mass spectrometric data with the literature. The final purity of the compound is 97%. Quantitative determination of eleutheroside E in A. giraldii Harms is performed on a Zorbax SB C18 (150- x 4.6-mm i.d., 5 microm) column. The linear range of eleutheroside E is 4.85-194 mg/L (r = 0.9998), and the average recovery is 99.6-101%. The developed method is simple, reproducible, and easy to operate. It is useful for the evaluation of Acanthopanax giraldii Harms.     

pH值对聚四氨基酞菁钴膜电化学和紫外光谱性质的影响

用循环伏安法在导电玻璃(ITO)和玻碳电极(GC)上制备了聚氨基酞菁钴(CoTAPc)修饰电极(CoTAPc/GC)。探讨了pH值对CoTAPc膜的光谱和电化学性质的影响，发现其氧化还原电位与pH值有线性关系，电催化活性也随酸度的增加而增加。CoTAPc膜的紫外吸收带变化与溶液pH值及在溶液中浸泡时间有关。     

稀土变质热锻模具铸钢高温磨损性能的研究

研究了稀土（RE）变质热锻模具铸钢的高温磨损性能，并与热锻模具钢H13钢和3Cr2W8V钢进行对比，探讨了稀土元素的作用和热锻模具铸钢的高温磨损机理。结果表明：随着RE加入量的增加，热锻模具铸钢的磨损率先减后增，RE加入量在质量分数为0．05％时热锻模具铸钢具有最佳的高温磨损性能。RE变质热锻模其铸钢的高温耐磨性明最高于H13钢和3Cr2W8V钢。高温磨损机理为氧化磨损和氧化物的疲劳剥落，磨屑为块状的Fe2O3和Fe3O4。     

Crystalline Morphology and Polymorphic Phase Transitions in Electrospun Nylon 6 Nanofibers

Uniform nylon 6 nanofibers with diameters around 200 nm were prepared by electrospinning. Polymorphic phase transitions and crystal orientation of nylon 6 in unconfined (i.e., as-electrospun) and a high T(g) (340 degrees C) polyimide confined nanofibers were studied. Similar to melt-spun nylon 6 fibers, electrospun nylon 6 nanofibers also exhibited predominant, meta-stable gamma crystalline form, and the gamma-crystal (chain) axes preferentially oriented parallel to the fiber axis. Upon annealing above 150 degrees C, gamma-form crystals gradually melted and recrystallized into the thermodynamically stable alpha-form crystals, which ultimately melted at 220 degrees C. Release of surface tension accompanied this melt-recrystallization process, as revealed by differential scanning calorimetry. For confined nanofibers, both the melt-recrystallization and surface tension release processes were substantially depressed; gamma-form crystals did not melt and recrystallize into alpha-form crystals until 210 degrees C, only 10 degrees C below the T(m) at 220 degrees C. After complete melting of nano-confined crystals at 240 degrees C and recrystallization at 100 degrees C, only alpha-form crystals oriented perpendicular to the nanofiber axis were obtained. In the polyimide-confined nanofibers, the Brill transition (from the monoclinic alpha-form to a high temperature monoclinic form) was observed at 180-190 degrees C, which was at least 20 degrees C higher than that in unconfined nylon 6 at approximately 160 degrees C. This, again, was attributed to the confinement effect.     

聚吡咯水杨酸修饰电极的电化学行为及水杨酸含量测定

本用电化学方法制备了聚吡咯－水杨酸修饰电极；并进行了电化学行为的研究，经电化学处理该是电极对水杨酸根具有选择性响应，响应线性范围在１．０×１０＾－＾５－１．０×１０＾－＾３ｍｏｌ／Ｌ之间。电极斜率为４０ｍＶ／ｐＣ，该电极具有较好的稳定性，响应时间在１８０－３００ｓ之间；电极寿命可达６０ｄ。     

Synthesis and photoluminescence of single crystals europium ion-doped BaF2 cubic nanorods

In this work, we used the hydrothermal method to synthesize Eu³⁺ ion-doped cubic BaF₂ nanorods, which is a luminescent material. The clubbed structures were well crystallized and exhibited face-centred cubic structures, as indicated by powder X-ray diffraction, scanning electron microscopy, electron diffraction, and transmission electron microscopy. The luminescent properties were studied, and local symmetry surrounding Eu³⁺ ions and electronic transition processes included. The results indicated that Eu³⁺ occupied only one C_4ν site in nanorods.