Influence of aramid fiber moisture regain during atmospheric plasma treatment on aging of treatment effects on surface wettability and bonding strength to epoxy

One of the main differences between a low-pressure plasma treatment and an atmospheric pressure plasma treatment is that in atmosphere, the substrate material may absorb significant amount of water which may potentially influence the plasma treatment effects. This paper investigates how the moisture absorbed by aramid fibers during the atmospheric pressure plasma treatment influences the aging behavior of the modified surfaces. Kevlar 49 fibers with different moisture regains (MR) (0.5, 3.5 and 5.5%, respectively) are treated with atmospheric pressure plasma jet (APPJ) with helium as the carrier gas and oxygen as the treatment gas. Surface wettability and chemical compositions, and interfacial shear strengths (IFSS) to epoxy for the aramid fibers in all groups are determined using water contact angle measurements, X-ray photoelectron spectroscopy (XPS), and micro-bond pull out tests, respectively. Immediately after the plasma treatment, the treated fibers have substantially lower water contact angles, higher surface oxygen and nitrogen contents, and larger IFSS to epoxy than those of the control group. At the end of 30 day aging period, the fibers treated with 5.5% moisture regain had a lower water contact angle and more polar groups on the fiber surface, leading to 75% improvement of IFSS over the control fibers, while those for the 0.5 and 3.5% moisture regain groups were only 30%.     

ICP微等离子体射流在快速成形制造中的应用

本文开展了大气压甚高频感应耦合(ICP)微等离子体射流的特性与应用研究.在150 MHz甚高频,功率为90 W条件下获得温度高达上千度的温热等离子体射流,射流长度近3 cm.随着气流量的增加射流将呈现层流到湍流的转变,长度先增后减;而功率对于射流长度的影响存在着一个上限,当等离子体吸收的能量与扩散损失的能量达到平衡时,射流长度将达到最大.利用这种ICP微等离子体射流进行了微尺寸金属铜的快速成形制造,得到了球冠状和柱状铜金属件.在扫描电子显微镜下观察到沉积物表面最小颗粒尺寸远小于铜粉颗粒;X射线衍射结果显示沉积物表面存在弱氧化物峰,这是沉积过程中空气被射流卷入所致.     

相变域硅薄膜材料的光稳定性

采用RF-PECVD技术，通过改变反应气体的硅烷浓度制备了一系列不同晶化率不掺杂的硅薄膜材料，研究了工艺变化对材料结构的影响及材料光电特性同微结构的关系.随后进行了光衰退试验，在分析光照前后光电特性变化规律的基础上，认为材料中的非晶成分是导致材料光电特性衰退的主要原因.在靠近过渡区非晶一侧的硅材料比普通非晶硅稳定，衰退率较少；高晶化率微晶硅材料性能稳定，基本不存在光衰退；在靠近过渡区微晶一侧的硅材料虽然不是完全不衰退，但相比高晶化率硅材料来说更适合制备高效微晶硅电池. 关键词： 射频等离子体增强化学气相沉积 硅薄膜 Staebler-Wronski(SW)效应 稳定性     

蛇足石杉及其近缘种表征关系的FTIR主成分分析

蛇足石杉是一种重要药用植物,其种内变异程度高,近缘种多,植株体型小,可供鉴别性状少。运用OMNI采样器-傅里叶变换红外光谱直接测定法,获得了蛇足石杉(Huperzia Serrata)及其5个近缘种：四川石杉(Huperzia Sutchueniana)、闽浙马尾杉(Phlegmariurus Mingchegensis)、石松(Lycopodium Japonicum)、深绿卷柏(Selaginella Doederleinii)和异穗卷柏(Selaginella Heterostachys)16个叶片样品的红外光谱,以666～3 145 cm-1范围内吸收峰吸光度为指标,以红外光谱图为对象,应用主成分分析(Principal Component Analysis),比较了16个样品在红外光谱上的差异程度。发现基于傅里叶变换红外光谱的主成分分析排序图能够在一定程度上表征16个样品的分类关系。应用FTIR直接测定法能够鉴别蛇足石杉及其近缘物种。     

Second-harmonic generation in thermally poled chalcohalide glass

Second-harmonic generation in 60GeS(2)-20Ga(2)S(3)-20KBr chalcohalide glass was investigated by the thermal poling method. A large second-order nonlinear susceptibility, as high as 7.0 pm/V, was obtained in a poled sample by Maker fringe analysis. We believe this to be the first time that a clear second-harmonic wave was observed in chalcohalide glasses containing large amount of alkali ions (6.25 at. %). Such observation is of great potential use in all optical waveguide devices.     

ZnO/A1lN/Si(111)薄膜的外延生长和性能研究

用常压金属化学气相沉积法(MOCVD)在Si(111)衬底上制备了马赛克结构ZnO单晶薄膜.引入低温AlN缓冲层以阻止衬底氧化、缓解热失配和晶格失配.薄膜双晶X射线衍射2θ/ω联动扫描只出现了Si(111)、ZnO(000l)及AlN(000l)的衍射峰.ZnO/AlN/Si(111)薄膜C方向晶格常量为0.5195 nm,表明在面方向处于张应力状态;其对称(0002)面和斜对称(1012)面的双晶X射线衍ω摇摆曲线半峰全宽分别为460"和1105";干涉显微镜观察其表面有微裂纹,裂纹密度为20 cm-1;3 μm×3μm范围的原子力显微镜均方根粗糙度为1.5 nm激光实时监测曲线表明薄膜为准二维生长,生长速率4.3μm/h.低温10 K光致发光光谱观察到了薄膜的自由激子、束缚激子发射及它们的声子伴线.所有结果表明,采用金属化学气相沉积法并引入AlN为缓冲层能有效提高Si(111)衬底上ZnO薄膜的质量.     

催化剂组分对制备单壁碳纳米管的影响

利用柠檬酸法制备出了Mo-Fe-MgO，Mo-Co-MgO和W-Co-MgO催化剂，在小型流化床中，以Ar气为载气，在1123 K下催化裂解CH₄来制备单壁碳纳米管(SWCNTs).利用透射电子显微镜和拉曼光谱方法研究了催化剂组分对SWCNTs制备的影响，并对SWCNTs的生长机理进行了探索，研究结果表明，柠檬酸法是一种制备负载型SWCNTs催化剂的有效方法，三种催化剂都能够得到质量较好的SWCNTs,在1123 K左右，SWCNTs在三种催化剂上的生长过程可能类似于“微液相模型”.催化剂的组分对SWCNTs的管径分布影响较小，不同催化剂所得到的SWCNTs在内部结构上存在一定的差异.催化剂中加入第二组分Mo和W能有效提高产物的碳产率. 关键词： 单壁碳纳米管 催化化学气相沉积法 生长机理 拉曼光谱     

单双层共轭系统的共轭高度对等晕角的影响

 简要介绍了传统自适应光学系统的局限性和多层共轭自适应光学基本原理。模拟了单双层共轭校正系统的共轭高度,并结合平程与垂程(HV模型)两种传输状态对系统等晕角增益作了进一步的分析。对单层共轭系统,在20 km的传输距离内,在平程中整个区域都属于等晕角放大区,共轭高度的最佳位置在传输距离的中间（约10 km处）,等晕角取极大值,增益效果较好;但垂程中增益效果变差,且等晕角放大区也仅在3.6 km之内。对双层共轭系统来说,第1层共轭高度的变形镜主要对近距离畸变波前进行校正,并对整个传输距离的等晕角影响很大,是双层共轭系统的关键因素;第2层共轭高度对远距离等晕角影响较大。     

Mechanisms of the pancake vortex and vortex line movement in the high Tc superconductors Bi2Sr2CaCu2O8+δand La1.93Sr0.07CuO4+δ

In the strict sense, it is not very clear why with magnetic field increasing, the normal-superconductive (NS) transition becomes broad for Bi2Sr2CaCu2O8+δ(Bi2212) while the NS transitions are almost parallel for La1.93Sr0.07CuO4+δ(La214). In this paper, R-T relations are measured by the six-probe method. We propose a moving mechanism of the pancake vortex and vortex line for Bi2212. The theoretical curves fit the experiment data well.     

基于超临界流体技术制备葡萄糖脂质体的实验研究

脂质体由于其特殊的结构和性能,是一种很有发展潜力的药物载体,在医药和化妆品等行业具有广阔的应用前景。超临界逆向蒸发法是用超临界流体代替有机溶剂制备脂质体的方法,具有对水溶性药物脂质体制备过程简单、包覆率高等特点。以葡萄糖为模型药物,利用该方法制备出了葡萄糖脂质体,并详细考察了不同工艺条件对脂质体粒径和包覆率的影响。结果表明:用超临界逆向蒸发法可成功地制备出最小粒径为290nm、包覆率最高可达41.3%的葡萄糖脂质体。压力、温度和平衡时间对粒径和包覆率都有较大的影响。压力在10~30MPa时,随压力的增加,脂质体粒径显著减小至某一值后,基本趋于稳定,而包覆率逐渐增加,达到25.7%~27.5%,随后包覆率逐渐减小;温度在35~65℃时,随温度的增加粒径显著减小至最小值,然后逐渐增大,而包覆率一直增大,最高可达41.3%;平衡时间在15~45min时,随平衡时间的增加,粒径相对稳定,而包覆率显著增加,超过45min之后,粒径显著增加,包覆率显著下降。