Highly Flexible and Nonflammable Inorganic Hydroxyapatite Paper

A highly flexible and nonflammable inorganic hydroxyapatite (HAP) paper made from HAP ultralong nanowires is reported. The paper can be used for printing and writing and is promising for the permanent and safe storage of information, such as archives and important documents. The HAP paper is also an excellent and recyclable adsorbent for organic pollutants.     

Coloring properties of novel 1,4-distyrylbenzene and 4,4′-distyrylbiphenyl fluorescent brighteners and their arrangement in cotton and polyester fiber

Some novel 1,4-distyrylbenzene (DSB) and 4,4′-distyrylbiphenyl (DSBP) fluorescent brighteners (FBs) were used to dye polyester and cotton fabrics. The CIE whiteness, color hue and reflectance spectrum of dyed fabrics were compared. DSBP derivatives could dye the cotton and polyester fabrics with a higher whiteness level and had a lower fluorescent quenching concentration than DSB derivatives. The color hue for the fabric dyed with DSB FBs was yellow-green, whereas that dyed with DSBP was blue–violet. The molecular arrangement in the fiber had a significant influence on their optical properties, resulting in different coloring properties. The increase in molecule planarity and rigidity generated by the interaction between the polymer and FB molecules caused a remarkable bathochromic shift in emission and excitation spectra. The H-aggregate of the DSB molecule in the fiber was easily generated, and the degree of aggregation increased with the molecular polarity. However, the aggregation of DSBP molecules in the polyester and cotton fiber was not found. The surface region of the cotton fiber was filled with FB molecules, whereas FB molecules in the polyester fiber aggregated easily, and incident light could pass through the surface region.     

Effects of lignin and hemicellulose contents on dissolution of wood pulp in aqueous NaOH/urea solution

Four species of delignified woodchips with about 1 % lignin content (Chlorite–Woodchips) and a series of softwood pulps with different lignin contents were prepared by sodium chlorite delignification. After mechanical defibration, some Chlorite–Woodchips were directly subjected to dissolution treatment in NaOH/urea solvent; the others were first treated with NaOH solution to remove the hemicellulose to obtain NaOH–Chlorite–Woodchips or oxidized with potassium permanganate (OPP) to remove lignin completely to obtain OPP–Chlorite–Woodchips, and then subjected to the dissolution in NaOH/urea solvent. The results showed that the dissolved proportion of the Chlorite–Woodchips ranged from 36 to 46 %, the dissolved proportion of glucan was within 12 %, and most of the hemicellulose was dissolved in NaOH/urea solvent. Compared with Chlorite–Woodchips, the dissolved proportion of NaOH–Chlorite–Woodchips was lower, but their dissolved proportion of glucan was higher. After further permanganate delignification, both the dissolved proportion of the OPP–Chlorite–Woodchips and the dissolved proportion of glucan of the OPP–Chlorite–Woodchips were higher than those of the Chlorite–Woodchips. However, the dissolved proportion of glucan was still limited to only 15–30 %. The effect of the lignin content of softwood pulps on their dissolution is complicated. With the decrease of the lignin content of softwood pulp from 6.9 to 2.8 %, the dissolved proportion of pulp increased from 14 to 26 %. However, further reduction of lignin content from 2.8 to 0.3 % led to a decrease in the dissolved proportion of pulp from 26 to 12 %. The dissolved proportion of glucan followed the same tendency. These results indicated that the dissolution of wood cellulose in NaOH/urea solvent is not simply controlled by the hemicellulose and lignin contents, but also by some other factors.     

气相色谱-电子轰击源质谱法测定茶叶中氟虫腈残留量

建立了茶叶中氟虫腈残留量快速测定的气相色谱-电子轰击源质谱法。茶叶中的氟虫腈用正己烷-丙酮(7:3,V/V)混合液提取,经石墨化碳黑固相萃取小柱净化后,用正己烷-丙酮(9:1,V/V)混合液洗脱,浓缩定容后,用气相色谱-电子轰击源质谱法测定,外标法定量。结果表明,目标物质在0.001~0.040 mg/L范围内的线性关系良好;空白样品在0.002~0.010 mg/L范围三水平加标回收实验的平均回收率在96.6%~114.2%之间,相对标准偏差(n=6)为2.9%~4.4%;方法的定量限为0.001 mg/kg。该方法能满足茶叶中氟虫腈残留量0.002 mg/kg的检测要求。     

新三氮唑并嘧啶型除草剂的合成及其与人血清白蛋白的相互作用

合成了一种新型除草剂3-(4-氯苯基)-5-[(3-氯苯基)-氨基]-6-[(3-三氟甲基苯氧基甲基)-氨基]-3,6-二氢-[1,2,3]三唑并[4,5-d]嘧啶-7-酮(TAPO),并对其进行了表征。在模拟生理(pH 7.4)条件下,采用紫外光谱、荧光光谱、圆二色谱法(CD)和傅里叶红外光谱研究了TAPO与人血清白蛋白(HSA)的相互作用。结果表明:TAPO对HSA的内源荧光产生了有规律的猝灭,通过Stern-Volmer方程和紫外吸收光谱确定其猝灭过程主要为静态猝灭;由热力学公式计算出相关热力学参数ΔH,ΔS,ΔG的值分别为-100.92 KJ/mol,-234.35 J/(mol·K),-30.40KJ/mol,推断二者间的作用力主要为氢键和范德华力;根据Frster非辐射能量转移理论求得二者的结合距离r为4.02 nm(298 K)。同步荧光结果表明结合位点更接近于色氨酸残基;傅里叶红外光谱和曲线拟合数据显示,α-螺旋含量下降,β-转角结构和无规则卷曲结构上升;圆二色谱法进一步验证TAPO使HSA的二级结构发生了不可逆的变化。     

猪骨基多孔炭对六价铬吸附性能的分析

以废弃的猪骨为原料制备的多孔炭作为吸附剂,分析了其对含Cr工业废水的净化作用,并对其吸附机理进行探讨。结果表明,吸附体系的pH、吸附时间、Cr(Ⅵ)初始浓度对多孔炭吸附Cr(Ⅵ)的能力影响较大,多孔炭材料的比表面积对其吸附水溶液中的Cr(Ⅵ)起决定性作用。该吸附过程符合二级动力学吸附模型,并且可用Langmuir吸附等温线来描述。所以猪骨基多孔炭有望成为含Cr(Ⅵ)废水的良好净化剂。     

丙烯聚合催化剂载体中碳对镁含量分析的影响

采用ICP-MS以无水氯化镁、碳镁摩尔为5~8:1的氯化镁醇合物丙烯聚合催化剂载体和碳镁摩尔比为12:1的六乙醇合氯化镁为对象,分别在普通模式、He模式下采用外标曲线加内标校正法和He模式下标准加入法测定其中的镁含量,并取几个典型样品采用ICP-OES进行镁含量测定。考察了采用ICP-MS测定丙烯聚合催化剂载体中镁含量时碳可能产生的影响。实验结果表明,对于碳镁摩尔比从5~8∶1到12∶1样品,碳对镁含量分析的影响均很小,其镁含量均可以在普通模式下采用外标曲线加内标校正法进行快速、简单、准确的测定。     

(P^N^P)钴配合物/倍半氯化乙基铝催化苯乙烯聚合的研究

采用含氮双膦配体与无水氯化钴反应可制得一系列相应的(P^N^P)钴配合物,并研究了该系列钴配合物对苯乙烯聚合的催化性能.在助催化剂倍半氯化乙基铝(EASC)的活化下,该系列钴配合物对甲苯中的苯乙烯溶液聚合表现出高的催化活性(可达5.44×105g(PS)·mol-1(Co)·h-1).通过对不同苯乙烯单体用量、助催化剂用量(Al/Co摩尔比)、聚合温度以及催化剂的配体环境等的研究,详细考察了这些因素对聚合反应和聚合产物性能的影响.通过凝胶渗透色谱法(GPC)和核磁共振碳谱(13C-NMR)表征了所得聚合产物的分子量及分子量分布和微观结构,分析结果表明,所得聚苯乙烯具有较低的分子量(Mn=2000~5900)和较窄的分子量分布(1.75~2.05),其微观结构是无规的.     

氨蒸发诱导法制备纳米结构LiNi_(1/3)Co_(1/3)Mn_(1/3)O_2及其作为高功率型锂离子电池正极材料的性能

采用氨蒸发诱导法成功制备出纳米结构LiNi1/3Co1/3Mn1/3O2正极材料,借助X射线衍射(XRD)分析、扫描电镜(SEM)、透射电镜(TEM)、高分辨率透射电镜(HRTEM)、能量分散谱(EDS)和比表面测试等表征手段及恒电流充放电测试研究了其晶体结构、微观形貌和电化学性能.研究表明该方法制备出的材料具有良好的α-NaFeO2层状结构,阳离子混排程度低.纳米片交错堆积而成核桃仁状形貌,片与片之间形成许多纳米孔,而且纳米片的侧面属于{010}活性面,能够提供较多的锂离子的脱嵌通道.在室温下及3.0-4.6 V充放电范围内,该材料在电流密度为0.5C、1C、3C、5C和10C时放电比容量分别为172.90、153.95、147.09、142.16和131.23mAh?g-1.说明其具有优异的电化学性能,非常有潜力用于动力汽车等高功率密度锂离子电池中.     

锂离子电池片状四氧化三钴负极的合成及改性

采用液相沉淀法结合低温固相热解法合成了锂离子电池片状Co3O4负极.通过X射线粉体衍射(XRD)、Brunauer-Emmett-Teller(BET)比表面积分析、扫描电子显微镜(SEM)及恒电流充放电等表征手段,发现该Co3O4为立方相,结晶完整且无杂质,由直径为1.5-3.0μm、厚度约为100-300 nm的不规则片状颗粒组成,比表面积约为30.5 m2·g-1;其比容量高且容量保持率好,在0.1C倍率下,首次放电容量高达1444.5 mAh·g-1,50次循环后充电容量仍大于1100.0 mAh·g-1;但在高倍率(1C)下,50次循环后充电容量保持率仅为75.3%,倍率性能一般.故采用碳纳米管(CNTs)掺杂改性,结果表明:在1C倍率下,70次循环后复合材料充电容量保持率为96.3%;在2C倍率下,50次循环后充电容量保持率仍高达97.0%,倍率性能显著提升.