二氧化碳—环氧丙烷—甲苯二异氰酸酯的三元共聚

二氧化碳和环氧丙烷(PO)在阴离子配位催化剂,如二乙基锌和等摩尔的水作用下,可接式(1)发生共聚。但产物聚丙撑碳酸酯(PPC)的热稳定性较差。改进途径之一是在反应中引入甲苯二异氰酸酯(TDI)进行三元共聚。本文报导在双金属阴离子配位催化剂PBM存在下合成一种热稳定性优于PPC的聚碳酸酯聚氨酯(PCPU)的研究结果(式2)。     

PLLA/β-TCP杂化微纳米纤维的制备及其性能

将湿法工艺合成的β-磷酸钙纳米粒子与左旋聚乳酸(PLLA)的混合溶液通过电纺丝法制成杂化纳米纤维膜,以期制备一种新型纳米纤维骨组织修复材料。采用FT-IR,XRD,TEM,DSC等手段研究了β-磷酸钙(β-TCP)的结构和形态,采用SEM和直径分布探讨了优化PLLA/β-TCP纤维的电纺丝工艺。结果表明:采用湿法合成β-TCP的纳米粒子具有良好的晶型结构,直径在219~328 nm之间;采用双溶剂体系在优化条件下制备的PLLA/β-TCP杂化纳米纤维直径在500~700 nm之间,PLLA/β-TCP界面结合良好,β-TCP起到了增强作用。在湿态条件下,PLLA纤维膜的力学性能有所提高,而PLLA/β-TCP纤维膜的力学性能则呈现下降趋势。     

Preparation and Characterization of Microencapsulated Hexadecane Used for Thermal Energy Storage

Polyurea microcapsules about 2.5μm in diameter containing phase change material for thermal energy storage application were synthesized and characterized by interfacial polycondensation method with toluene-2,4-diisocyanate and ethylenediamine as monomers in an emulsion system. Hexadecane was used as a phase change material and OP, which is nonionic surfactant, and used as an emulsifier. The chemical structure and thermal behavior of the microcapsules were investigated by FTIR and thermal analysis respectively. The results show encapsulated hexadecane has a good potential as a solar energy storage material.     

Co—Mo／MgO—Al2O3水煤气耐硫变换催化剂失活的研究

利用Ｘ－射线衍射，扫描电镜，拉曼光谱，等离子发射光谱和比表面测定等方法研究了不同状态下失活及新鲜催化剂的结构，杂种类及含量。结果表明，超温使催化剂晶化明显，制备方法对催化剂结构有直接影响，再生使其强度降低，条形催化剂比较容易粉化，无机杂质是次要的失活原因。     

双(N 氧化吡啶 2-甲醛)缩1,2-丙二胺镍配合物的合成和晶体结构

合成所得双(N-氧化吡啶-2-甲醛)缩1,2-丙二胺的镍(II)配合物[Ni(piopn)(H_2O)_2](ClO_4)_2的晶体属空间群C_s~4-C_c, 晶胞参数a=0.7397(3) nm, b=1.3187(7) nm, c=2.5502(14) nm, β=102.18(4)°. 用分子轨道理论的近似方法分析了该配合物的电子结构和分子轨道, 探讨了分子的结构特征与红外光谱的关系.     

稀土钨青铜K0.71Nd0.028WO3的制备及其电性能

Tetragonal tungsten bronze K_0.71Nd_0.028WO₃ was synthesized by rare earth co-permeation method using Keggin type POMs of α-K₁₀[SiCu₃(OH₂)W₉O₃₇]·6H₂O (abbreviated as SiW₉Cu₃) as precursor. XRD, XPS, XRF, TG-DTA were used to characterize the resulting material. The XPS results indicate that Nd has permeated and diffused into the body of the sample and exists in tungsten bronze in the form of K_0.71Nd_0.028WO₃. The results of TG-DTA show that K_0.71Nd_0.028WO₃ begins to decompose at 320 ℃. The consequence of DC four-probe shows that the conductivity of the sample permeated by rare earth is 10³ times higher than that of the sample only permeated by methanol at room temperature. The conductivity of the sample only permeated by methanol is only 10^-3 S·cm^-1 but the conductivity of the sample permeated by rare earth is 1.65 S·cm^-1.     

Voltammetric Behavior of the Alizarin Red S Interaction with DNA and Damage to DNA

The electrochemical behavior and the interaction of alizarin red S (ARS) with calf thymus DNA was investigated on a bare glassy carbon electrode (GCE) and DNA modified GCE (DNA/GCE), respectively. ARS showed a pair of redox peaks at ?0.445 V and ?0.414 V on a bare GCE. On addition of DNA into the ARS solution, the peak current of ARS decreased and the peak potential positively shifted, but without new redox peaks appeared. The ARS reduction peak current increased with immersion time on a DNA/GCE. The results showed that ARS could interact with DNA molecules by intercalative binding mode. The equilibrium constant, binding number and the ratio of binding constant for oxidized and reduced ARS forms were obtained. The DNA damage was directly detected by appearance of guanosine and adenosine bases oxidation signal. The influence of experimental conditions on DNA damage extent was discussed in detail.     

N‐Heterocyclic Carbene–Palladium Complexes as Efficient Catalysts for the Oxidative Carbonylation of Amines to Ureas

A highly efficient oxidative carbonylation reaction of amines to ureas was developed making use of carbene–palladium complexes in the absence of any promoter. Both aliphatic amines and aromatic amines were transformed in good to excellent yields to the expected ureas.     

表面电沉积Ni—La2O3复合镀层的Fe26Cr1Mo不锈钢的氧化行为研究

Ｆｅ２６Ｃｒ１Ｍｏ不锈钢在９００℃氧化时，生成的氧化层在冷却过程中大量剥落，经表面共电沉积ＮｉＬａ２Ｏ３复合镀层后，抗热循环能力明显提高。     

Topologies of capillary condensation

Calculations are presented to illustrate the dependence of capillary adsorption upon the interactions present in model pores. The sequence of phase transitions at zero temperature is determined for a Lennard-Jones lattice gas in a pore consisting of 4 × 4 × sites. The dependence of the specific filling sequence upon the comparative strength of the gas-pore wall and the gas-gas interaction well-depths is determined. Grand canonical Monte Carlo simulations of sorption at finite temperature in the continuum version of the same model pore are also reported. Both the theory and the simulations were performed with variable gas-solid and gas-gas energy well-depths. At a temperature of 90 K, the gas-solid heterogeneity associated with atoms adsorbed in the corners, on the walls and in the interior pore volume gives rise to sequential adsorption similar to that observed in the lattice gas calculation at 0 K. A gradual approach to non-wetting behavior is observed as the gas-solid well-depth decreases. Values of the gas-solid well-depth needed to produce pore filling at saturation (i.e., pore-wetting) are discussed.