Preparation of Nanoelectrode Ensembles by Assembly of Nano—Silver Colloid on Gold Surface

A novel method for preparing silver nanoelectrode ensembles(SNEEs) and gold nanoelectrode ensembles (GNEEs) has been developed. Silver colloid particles were first absorbed to the gold electrode surface to form a monolayer silver colloid. N-hexadecyl nercaptan was then assembled on the electrode to form a thoil monolayer on which hydrophilic ions cannot be transfered. The SNEEs was prepared by removing thiol from silver colloid surface through applying and AC voltage with increasing frequency at 0.20V(vs.SCE). Finally,GNEEs was obtained by immersing a SNEEs into 6 mol/L HNO3 to remove the silver colloid particles. By comparison with other methods such as template method ect., this method enjoys some advantages of lower resistance, same diameter,easy preparation,controllable size and density.     

Reactions of sulfur(IV) with an octahedral manganese(IV) complex of 1,8-bis(2-hydroxy benzamido)-3,6-diaza octane: the role of phenolate–amide–amine coordination

The Mn^IV complex of tetra-deprotonated 1,8-bis(2-hydroxybenzamide)-3,6-diazaoctane (Mn^IVL) engrossed in phenolate-amido-amine coordination is reduced by HSO₃⁻ and SO₃²⁻ in the pH range 3.15–7.3 displaying biphasic kinetics, the Mn^IIIL⁻ being the reactive intermediate. The Mn^IIIL⁻ species has been characterized by u.v.–vis. spectra {λ _max, (ε, dm³ mol⁻¹ cm⁻¹): 285(15 570), 330 sh (7570), 469(6472), 520 sh (5665), pH=5.42}. SO₄²⁻ was the major oxidation product of S^IV; dithionate is also formed (18 ± 2% of [Mn^IV]_T) which suggests that dimerisation of SO₃^−• is competitive with its fast oxidation by Mn^IV/III. The rates and activation parameters for Mn^IVL + HSO₃⁻ (SO₃²⁻) → Mn^IIIL⁻; Mn^IIIL⁻ + HSO₃⁻ (SO₃²⁻) → Mn^IIL²⁻ are reported at 28.5–45.0 °C (I=0.3 mol dm⁻³, 10% (v/v) MeOH + H₂O). Reduction by SO₃²⁻ is ca. eight times faster than by HSO₃⁻ both for Mn^IVL and Mn^IIIL⁻. There was no evidence of HSO₃⁻/SO₃²⁻ coordination to the Mn centre indicating an outer sphere (ET) mechanism which is further supported by an isokinetic relationship. The self exchange rate constant (k₂₂) for the redox couple, Mn^IIIL⁻/Mn^IVL (1.5 × 10⁶ dm³ mol⁻¹ s⁻¹ at 25 °C) is reported.     

Molecular Spectroscopic Study on the Interaction between Heparin and Neutral Red

The interaction between heparin and neutral red was investigated by molecular spectroscopic methods. The change of all spectra suggested that positively charged neutral red had interacted with negatively charged heparin. The study of influence factors indicated that electrostatic force and hydrophobic bond might be involved in the interaction. The total binding number per disaccharide unit and intrinsic binding constant were obtained using Scatchard model.     

铁－铜－锰氧化物／海泡石催化剂对苯羟基化为苯酚的催化作用

铁－铜－锰氧化物／海泡石催化剂对苯羟基化为苯酚的催化作用曹声春，黄孟光，李克，杜兴军（湖南大学化工系，长沙４１００８２）关键词氧化铁，氧化钢，二氧化锰，海泡石，负载型催化剂，苯，羟基化，苯酚由苯合成苯酚的现行方法存在着反应步骤多，工艺过程复杂，总转化...     

Thermal decomposition of the composite hydrotalcites of iowaite and woodallite

The thermal stability and thermal decomposition pathways for synthesized composite iowaite/woodallite have been determined using thermogravimetry analysis in conjunction with evolved gas mass spectrometry. Dehydration of the hydrotalcites occurred over a range of 56–70°C. The first dehydroxylation step occurred at around 255°C and, with the substitution of more iron(III) for chromium(III) this temperature increased to an upper limit of 312°C. This trend was observed throughout all decomposition steps. The release of carbonate ions as carbon dioxide gas initialised at just above 300°C and was always accompanied by loss of hydroxyl units as water molecules. The initial loss of the anion in this case the chloride ion was consistently observed to occur at about 450°C with final traces evolved at 535 to 780°C depending of the Fe:Cr ratio and was detected as HCl (m/z=36). Thus for this to occur, hydroxyl units must have been retained in the structure at temperatures upwards of 750°C. Experimentally it was found difficult to keep CO₂ from reacting with the compounds and in this way the synthesized iowaite-woodallite series somewhat resembled the natural minerals.     

Mesoporous micelle templated silica with incorporated C<Subscript>8</Subscript> and C<Subscript>18</Subscript> phase

Mesoporous silica material of MCM-41 type was synthesized by co-condensation of highly concentrated octyltriethoxysilane (OTEOS), octadecyltriethoxysilane (ODTEOS) and tetraethoxysilane (TEOS). The obtained hybrid materials were characterized using XRD, TG-DSC and low temperature adsorption/desorption of nitrogen. It was shown that the applied method of synthesis allows to obtain silica of MCM-41 type with a high degree of hydrocarbon saturation.     

Preparation of HPMC–EA–DMAEMA nanosized latex

Nanosized copolymer latex of hydroxypropylmethylcellulose (HPMC) grafted with ethyl acrylate (EA) and dimethylaminoethyl methacrylate (DMAEMA) has been prepared by acidifying submicron-sized latex particles synthesized by soap-free emulsion graft copolymerization using potassium persulfate (KPS) as initiator. The effects on the diameter of the latex particles of different conditions, for example concentration of DMAEMA, amount of HPMC, and ratio of HCl to DMAEMA for acidification, were investigated. It was found that increasing the mole ratio of HCl to DMAEMA to 1.0 and increasing the DMAEMA content both resulted in a decrease in particle diameter, whereas increasing the amount of HPMC resulted in larger particle sizes. Measurement by dynamic light scattering (DLS) revealed the diameter of the latex particles was >200 nm before acidification and <100 nm after acidification. Evidence of grafting was obtained by use of Fourier transform infrared (FTIR) spectroscopy. Transmission electron microscopy (TEM) was used to characterize the morphology of the copolymer particles before and after acidification.     

Influence of thermal and thermo-mechanical treatment

Two lipids with similar melting ranges but of different composition were analyzed using differential scanning calorimetry and X-ray diffraction. The lipids were processed via extrusion or were tempered at different temperatures; they were analyzed directly after extrusion and after storage at 40°C. Precirol ATO 5® showed high sensitivity to storage time and varied temperature exposure. Extrusion showed only marginal influences on the solid state. Melting peaks were narrower and shifted to higher temperatures in comparison to the untreated powder. Dynasan 114® was more robust, changes in the solid state could only be shown for samples treated above the melting range. Thus, Dynasan 114® is more appropriate for solid lipid extrusion of pharmaceutical products.