Antimicrobial activity on the copolymers of 2,4‐dichlorophenyl methacrylate with methyl methacrylate: Synthesis and characterization

Copolymers of monomers 2,4‐dichlorophenyl methacrylate (2,4‐DMA) and methyl methacrylate (MMA) were synthesized with different monomer feed ratios using toluene as a solvent and 2,2′‐azobisisobutyronitrile (AIBN) as an initiator at 70 °C. The copolymers were characterized by IR‐spectroscopy, and copolymer composition was determined with UV‐spectroscopy. The linearization method of Fineman–Ross was employed to obtain the monomer reactivity ratios. The molecular weights and polydispersity indexes were determined by gel permeation chromatography (GPC). Thermogravimetric analyses of polymers were carried out in nitrogen atmosphere. The homo‐ and copolymers were tested for their antimicrobial properties against selected microorganisms. © 2004 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 42: 5227–5234, 2004     

Dark cure studies of cationic photopolymerizations of epoxides: Characterization of kinetic rate constants at high conversions

The effective propagation rate constant (k_p; averaged over all the propagating active centers) was characterized for solvent‐free cationic photopolymerizations of phenyl glycidyl ether over the entire range of conversions, including the high conversion regime in which mass transfer limitations become important. The profile for the k_p as a function of conversion was found to exhibit a constant plateau value at low to intermediate conversions, followed by a monotonic increase above a threshold value of conversion. To explain this trend, it is proposed that at high conversion the diffusional mobility of the photoinitiator counterion is reduced whereas the mobility of the cationic active center remains high because of reactive diffusion. Therefore, with increasing conversion, the average distance between the active centers and counterions may increase, resulting in an increase in the propagation rate constant. The profiles for the k_p values were investigated as a function of the temperature, photoinitiator anion, and photoinitiator concentration. As the photoinitiator concentration was increased, the plateau value of the effective propagation rate constant decreased whereas the threshold conversion increased. All of the experimental trends are consistent with the proposed increase in ion separation at high conversions. © 2004 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 42: 4409–4416, 2004     

Photopolymerization of 1,6‐hexanedioldiacrylate initiated by three‐component systems based on N‐arylphthalimides

Three‐component photoinitiators comprised of an N‐arylphthalimide, a diarylketone, and a tertiary amine were investigated for their initiation efficiency of acrylate polymerization. The use of an electron‐deficient N‐arylphthalimide resulted in a greater acrylate polymerization rate than an electron‐rich N‐arylphthalimide. Triplet energies of each N‐arylphthalimide, determined from their phosphorescence spectra, and the respective rate constants for triplet quenching by the N‐arylphthalimide derivatives (acquired via laser flash photolysis) indicated that an electron–proton transfer from an intermediate radical species to the N‐arylphthalimide (not energy transfer from triplet sensitization) is responsible for generating the initiating radicals under the conditions and species concentrations used for polymerization. © 2004 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 42: 4009–4015, 2004     

Preparation of macromonomers by copolymerization of methyl acrylate dimer involving β fragmentation

The unsaturated dimer of methyl acrylate [CH₂C(CO₂CH₃)CH₂CH₂CO₂CH₃, or MAD] was copolymerized with various monomers to prepare copolymers bearing the ω-unsaturated end group [CH₂C(CO₂CH₃)CH₂ ] arising from β fragmentation of the MAD propagating radical. Copolymerizations of MAD with cyclohexyl and n-butyl acrylate resulted in copolymers with ω-unsaturated end groups, and increasing the temperature up to 180 °C resulted in an increase in the rate of β fragmentation of MAD radicals relative to propagation. Only a small amount of unsaturated end groups was introduced by copolymerization with ethyl methacrylate (EMA), and the EMA content in the copolymer increased with temperature. These findings could be explained by the reversible addition of the poly(EMA) radical to MAD. The copolymerization with ethyl α-ethyl acrylate (EEA) did yield a copolymer containing unsaturated end groups with MAD units as part of the main chain, although the steric hindrance of the ethyl group suppressed homopropagation and crosspropagation of EEA, resulting in low polymerization rates. Therefore, the copolymerization of MAD with acrylic esters at high temperatures was noted as a convenient route for obtaining acrylate–MAD copolymers bearing unsaturated end groups at the ω end (macromonomer). © 2003 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 42: 597–607, 2004     

Strain hardening of polycarbonate in the glassy state: Influence of temperature and molecular weight

This study is concerned with the temperature and molecular weight dependence of the strain-hardening behavior of polycarbonate. It is shown that the strain-hardening modulus reduces with increasing temperature and decreasing molecular weight. This result is interpreted in terms of temperature accelerated relaxation of the entanglement network. Moreover, it is shown that frozen-in orientations, induced by homogeneous deformations above the glass transition temperature, lead to anisotropic yield behavior that can be fully rationalized (and modelled) in terms of a superimposed stress contribution of the prestrained network. © 2004 Wiley Periodicals, Inc. J Polym Sci Part B: Polym Phys 42: 2041–2049, 2004     

Announcement of Proficiency Testing Schemes

Accreditation and Quality Assurance -     

Metallo‐supramolecular block copolymer micelles: Improved preparation and characterization

Micelles prepared from amphiphilic block copolymers in which a poly(styrene) segment is connected to a poly(ethylene oxide) block via a bis‐(2,2′:6′,2″‐terpyridine‐ruthenium) complex have been intensely studied. In most cases, the micelle populations were found to be strongly heterogeneous in size because of massive micelle/micelle aggregation. In the study reported in this article we tried to improve the homogeneity of the micelle population. The variant preparation procedure developed, which is described here, was used to prepare two “protomer”‐type micelles: PS₂₀‐[Ru]‐PEO₇₀ and PS₂₀‐[Ru]‐PEO₃₇₅. The dropwise addition of water to a solution of the compounds in dimethylformamide was replaced by the controlled addition of water by a syringe pump. The resulting micelles were characterized by sedimentation velocity and sedimentation equilibrium analyses in an analytical ultracentrifuge and by transmission electron microscopy of negatively stained samples. Sedimentation analysis showed virtually unimodal size distributions, in contrast to the findings on micelles prepared previously. PS₂₀‐[Ru]‐PEO₇₀ micelles were found to have an average molar mass of 318,000 g/mol (corresponding to 53 protomers per micelle, which is distinctly less than after micelle preparation by the standard method) and an average hydrodynamic diameter (d_h) of 18 nm. For PS₂₀‐[Ru]‐PEO₃₇₅ micelles, the corresponding values were M = 603,000 g/mol (31 protomers per micelle) and d_h = 34 nm. The latter particles were found to be identical to the “equilibrium” micelles prepared in pure water. Both micelle types had a very narrow molar mass distribution but a much broader distribution of s values and thus of hydrodynamic diameters. This indicates a conformational heterogeneity that is stable on the time scale of sedimentation velocity analysis. The findings from electron microscopy were in disagreement with those from the sedimentation analysis both in average micelle diameter and in the width of the distributions, apparently because of imperfections in the staining procedure. The preparation procedure described also may be useful in micelle formation from other types of protomers. © 2004 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 42: 4458–4465, 2004     

Completely biodegradable composites of poly(propylene carbonate) and short,lignocellulose fiber Hildegardia populifolia

The composites of biodegradable poly(propylene carbonate) (PPC) reinforced with short Hildegardia populifolia natural fiber were prepared by melt mixing followed by compression molding. The mechanical properties, thermal properties, and morphologies of the composites were studied via static and dynamic mechanical measurements, thermogravimetric analysis, and scanning electron microscopy (SEM) techniques, respectively. Static tensile tests showed that the stiffness and tensile strength of the composites increased with an increasing fiber content. However, the elongation at break and the energy to break decreased dramatically with the addition of short fiber. The relationship between the experimental results and the compatibility or interaction between the PPC matrix and fiber was correlated. SEM observations indicated good interfacial contact between the short fiber and PPC matrix. Thermogravimetric analysis revealed that the introduction of short Hildegardia populifolia fiber led to a slightly improved thermooxidative stability of PPC. © 2004 Wiley Periodicals, Inc. J Polym Sci Part B: Polym Phys 42: 666–675, 2004