Bi_(25)FeO_(40)/α-Fe_2O_3复合纳米颗粒光催化剂的制备与性能

采用溶剂热法,以聚酰胺-胺(PAMAM)树形分子为稳定剂,分别制备了Bi_(25)FeO_(40)和Bi_(25)FeO_(40)/α-Fe_2O_3复合纳米颗粒,并利用X射线衍射仪(XRD)、高分辨透射电镜(HRTEM)、X射线光电子能谱仪(XPS)、紫外-可见吸收光谱仪(UV-Vis)、比表面积和孔径分析仪(BET)和超导量子干涉磁强计等对其结构和性能进行了表征.结果表明,2种颗粒均为球形,尺寸均匀,粒径小于10 nm.当原料中Bi~(3+)/Fe~(3+)摩尔比为25∶1时,产物为Bi_(25)FeO_(40)纳米颗粒;Bi~(3+)/Fe~(3+)摩尔比为1∶1时,产物为Bi_(25)FeO_(40)/α-Fe_2O_3复合纳米颗粒.与Bi_(25)FeO_(40)纳米颗粒相比,Bi_(25)FeO_(40)/α-Fe_2O_3复合纳米颗粒的带隙变窄,对可见光吸收范围变宽,饱和磁化强度和光催化活性明显增强.这是由于复合颗粒中的α-Fe_2O_3具有超顺磁性,且两相界面存在的异质结构有利于光生载流子的分离和迁移,提高催化活性.2种纳米颗粒均可磁性回收,重复使用3次后催化活性下降较小.     

Dynamic Mechanism of Sustainable Molecular Orientation Generated From Cyclic Rotational States

Recently, two papers presented by Ortigoso et al. [Phys. Rev. Lett. 93 （2004） 073001 and Phys. Rev. A 72 （2005） 053401] develop a novel strategy in which the best sustainable molecular alignment/orientation has been achieved. We intend to analyse the dynamic mechanisms, including those Ortigoso et al. have not clarified.     

Characteristics of Nd：GdVO4 Laser with Different Nd-Doping Concentrations

We report the properties of a compact diode-pumped continuous-wave Nd：GdV04 laser with a linear cavity and different Nd-doped laser crystals. In a 0.2at.% Nd-doped Nd：GdVO4 laser, 1.54 W output laser power is achieved at 912nm wavelength with a slope efficiency of 24.8% at an absorbed pump power of 9.4W. With 0.3at.% Nd-doping concentration, we can obtain the either single-wavelength emission at 1064nm or 912nm or the dual-wavelength emission at 1064nm and 912nm by controlling the incident pump power. From an incident pump power of 11.6 W, the 1064nm emission between ^4Fa/2 and ^4I11/2 is suppressed completely by the 912nm emission between ^4Fa/2 and ^4I9/2. We obtain 670 mW output of the 912nm single-wavelength laser emission with a slope efficiency of 5.5% by taking an incident pump power of 18.4 W. Using a Nd：GdV04 laser with 0.4at.% Nd-doping concentration, we obtain either the single-wavelength emission at 1064nm or the dual-wavelength emission at both 1064nm and 912nm by increasing the incident pump power. We observe a strong competition process in the dualavelength laser.     

Compact Single-Stage Femtosecond Multipass Ti：Sapphire Amplifier at 1 kHz with High Beam Quality

A compact femtosecond Ti：sapphire amplifier system is reported using single-stage multipass configuration with high beam quality. A high dispersion glass stretcher and a pair of double prisms for compression are introduced based on broadband femtosecond seed pulses. The non-grating-based pulse stretcher and compressor are advantageous to increase high beam quality and to reduce the high-order dispersion. A Gaussian filter is used to reduce the gain narrowing effect in amplification. The compact femtosecond Ti：sapphire nine-pass amplifier delivers pulses with a duration of 26 fs and an energy of 800μJ at 7mJ pumping pulses energy at I kHz. The 1-kHz femtosecond amplifier with high beam quality and high stability is very suitable for ultrafast physics research applications, such as attosecond science, ultra-precision micromachining, and THz wave generation.     

光子晶体光纤及其应用

光子晶体作为一种新兴的材料 ,将会对整个光子学和光子产业领域产生深远的影响 ,而其最重要的应用之一———光子晶体光纤已经在很多科研技术领域得到了应用 .文章综述了光子晶体光纤的研究进展 ,给出其分类 ,并重点介绍了光子晶体光纤在超短脉冲、光频测量、光纤通信等科研领域的重要应用以及未来的发展前景     

重庆地区露天石刻早期封护材料老化产物及其影响研究

重庆市市委会办公大楼旧址前有一组露天存放的清代砂岩石狮子,表面覆盖着黑色硬壳状物质, 发生大面积脱落,起翘和卷曲。为了揭示黑色硬壳状结构组成,研究其形成过程及对文物产生的影响,利用环境扫描电子显微镜(SEM),X-射线衍射仪(XRD),X-射线荧光光谱仪(XRF),傅里叶变换红外光谱仪(FTIR)和X-射线光电子能谱(XPS)对黑色硬壳及文物表层砂岩样品进行了检测分析研究。结果发现：黑色硬壳断面Mapping元素分布图显示其分为底漆层,中间层和表层,系石刻早期封护层的老化产物;中间层含有立德粉(硫化锌和硫酸钡),黑色外观源于表层中含铅颜料(铅白)变色形成黑色硫化铅及树脂碳化所致;红外光谱与光电子能谱显示出黑色硬壳中含有强的羟基(-OH)特征峰,说明封护层中有机物老化后形成了大量羟基,从而增强了自身亲水性,造成易吸水溶胀与干燥收缩情况,导致大面积脱落,起翘和卷曲现象;黑色硬壳起翘和卷曲部位与下层石刻表面之间形成了易于积水的微空隙,能够聚集雨水中的有害物质,造成石刻表层岩石发生腐蚀,例如黑色硬壳背面及下层岩石表面中高含量硬石膏(CaSO₄),经生水化作用后转化为石膏(CaSO₄·2H₂O),发生体积膨胀造成岩石表面松动和酥粉。因此,当露天文物表面上封护层已老化时,及时地进行清除是十分必要的。     

掺磷TiO_2优化TiO_2/MBA/Ag三明治结构的SERS性能

本文以磷酸为磷源,通过溶胶水热法制备磷掺杂TiO_2,利用Lee和Meisel的方法制备银溶胶,以4-巯基苯甲酸(MBA)为探针分子,通过构建TiO_2/MBA/Ag三明治结构,研究磷掺杂二氧化钛对该基底表面增强拉曼(SERS)性能的提升。通过TEM、XRD、XPS、DRS和拉曼光谱图表征二氧化钛的形貌结构、化学组成、光学和拉曼性能,结果表明,制备出的磷掺杂二氧化钛为锐钛矿型纳米颗粒,粒径范围6~12nm,XPS显示磷以P~(5+)替代了Ti~(4+),形成O-P-O键掺入TiO_2的晶格中,当磷的掺杂量在1.77%时,TiO_2/MBA/Ag三明治体系具有最佳的SERS信号,这是因为适量的磷掺杂降低了TiO_2的能带间隙,丰富TiO_2的表面态,这能促进TiO_2向MBA分子的电荷转移。     

�����ȴ���Ժ˾۱���316LN���ӽ�ͷ��Ӱ��

采用了TIG对核聚变用316LN奥氏体不锈钢进行焊接,并对焊接接头进行了焊后热处理,利用光学显微镜、扫描电镜分析手段研究了焊后热处理对焊接接头微观组织和力学性能的变化.试验结果表明,焊缝中为奥氏体组织,并未发现第二相析出物存在.焊后热处理对接头的拉伸性能影响不大,均断裂在母材位置,但显著提高了接头的延伸率.接头低温冲击试验也展现了良好的抗低温冲击性能.断口分析发现,接头呈韧性断裂.     

N2分压对ZrN/WN纳米多层膜缺陷性质与力学性能的影响

利用射频磁控溅射系统在不同N₂分压的条件下，制备了一系列ZrN/WN纳米多层膜.借助慢正电子湮没技术分析了样品的缺陷性质，采用纳米压痕仪研究了多层膜的力学性能.结果发现：N₂分压为0.4Pa的多层膜具有最小的空位型缺陷浓度，其中心层和膜基结合层的平均S参数分别为0.4402和0.4641，而较低或较高的N₂分压都可能导致空位型缺陷浓度的增加.随着空位型缺陷浓度的减小，多层膜的硬度和临界载荷增大.对于空位型缺陷浓度最小的多层膜，其硬度和临界载荷达到最大值，分别为34.8GPa和100mN，说明较低的缺陷浓度有利于提高多层膜的力学性能. 关键词： ZrN/WN纳米多层膜 缺陷性质 力学性能 慢正电子湮没