THE EFFECT OF ADDITIVE La_2O_3 ON THE DISPERSION AND THERMOSTABILITY OF NICKEL IN METHANATION CATALYST

It is showed that La_2O_3 and NiO could disperse on γ-Al_2O_3 as a monolayer and theirutmost monolayer capacities determined by quantitative XRD are 0.28g/100m~2 and 0.09g/100m~2respectively. In the methanation catalyst, Ni/La_2O_3/γ-Al_2O_3, the La_2O_3 is dispersed on thesurface of γ-Al_2O_3 as a monolayer and the metallic nickel crystallites are supported on thesurface with La_2O_3. It has been found by the XRD peak broadening that the average size ofnickel crystallites on the surface with La_2O_3 is much smaller than that without La_2O_3. Thismay be one of the main reasons for the increase of activity and thermostability of the La_2O_3containing methanation catalyst. This idea of modifying support surface by monolayercompound can also be applied to other catalysts.     

2000年全球消除IDD

２０００年全球消除ＩＤＤ陈清硕，钱晓晴（江苏农学院，扬州２２５００１）１９８３年澳大利亚著名的医学家Ｈｅｔｚｅｌ把“碘缺乏病”称为ＩＤＤ，这个名词已在许多有关碘与健康关系研究的文献中出现。本来，碘缺乏导致甲状腺肿，严重的导致克汀病已为众所熟知，但缺碘...     

氧化钪中Ti,Mo,W,V,Zr等难熔杂质光谱分析

本用提高样品蒸发速率的方法提高氧化钪中难熔杂质光谱分析灵敏度。采用一种特殊的阴极设计，配合使用Ｎ２＋Ａｒ气氛控制，在旋流气室中放电激发，取样仅５ｍｇ的条件下，光谱测定氧化钪中难烷质Ｔｉ，Ｚｒ，Ｍｏ，Ｗ，Ｖ灵敏度可达（１－３）×１０＾－４％。测定的相对标准偏差为９％－２７％。     

One—Pot Synthese of 3,4—Dihydropyrimidine—2（1H）—thiones Catalyzed by La（OTf）3

A general and practical procedure for the syntheses of 3,4-di-hydropyrimidine-2(1H)-thiones by a one-pot condensation of aldehyde,β-ketoester or β-diketone and thiourea using La(OTf)3 as the catalyst is described.Mild reaction conditions,excellent yields as well as the environmentally friendly character of La(OTf)3 make it an important alternative to the classic acid-catalyzed Biginelli‘s reaction.     

可变色形状记忆材料

以聚乙烯醇和单宁酸为原料制备出了形状记忆水凝胶,以乙二胺四乙酸、二水合氯化铜、六水合氯化镁、氧化铝为原料制备出了无机热致变色材料,以结晶紫内酯、硼酸、十六醇为原料制备出了有机热致变色材料,并将形状记忆材料与热致变色材料结合,成功制备出了两种既能记忆形状又能变色的新型复合高分子材料。本实验原料简单易得,方法简便,并与本科阶段有机化学、无机化学、仪器分析、精细化学品化学等课程中所学习的自由基聚合反应、化学交联、络合反应等知识结合,可作为本科教学的一个综合实验,提高学生的动手能力,激发学生学习化学的兴趣和热情。     

聚丙烯及增韧剂对复合材料熔接痕强度的影响

研究了聚丙烯基体的熔体粘度(以熔体流动速率表征)、增韧剂POE的粘度(以门尼粘度表征)、增韧剂POE的含量等因素对聚丙烯复合材料熔接痕强度的影响。结果表明:聚丙烯基体/增韧剂的粘度比越小,聚丙烯复合材料的熔接痕强度越高,即聚丙烯粘度越小、增韧剂粘度越大,整个复合材料的熔接痕强度越高;增韧剂POE的含量越大复合材料的熔接痕强度越小。     

考虑承压水降水的深基坑施工变形规律研究

以宁波市轨道交通仇毕站深基坑工程为例,考虑⑧_3层承压水降水的影响,开展了深基坑开挖施工变形特性研究.首先设计了减压降水方案,然后利用Plaxis3D有限元软件对仇毕站深基坑开挖施工进行数值模拟,分析减压降水对深基坑工程变形特性的影响.结果表明:考虑基坑承压水降水的深基坑变形规律与不降水条件下的变形规律基本一致,⑧_3层承压水减压降水可导致地表沉降增大,坑底隆起减小.     

稀土元素在含残余砷、锡09Cr2AlMoRE钢中的作用

对加稀土前后09Cr2AlMoRE钢取样分析化学成分,制备金相样用SEM-EDS研究了钢中析出物特征,制备透射电镜(TEM)试样通过TEM研究元素的晶界偏聚,并用热力学计算了稀土Ce,La,S和残余元素As反应固定残余元素As的可能性。研究结果表明:在低氧、硫的条件下,稀土镧可以和09Cr2AlMoRE钢中较低含量的砷(130×10-6)作用生成镧砷金属间化合物;铈、镧主要是通过形成稀土砷硫夹杂物固定钢中残余元素砷。另外,在本实验条件下稀土元素(64×10-6)只有很微量的偏聚在晶界,残余元素As不在晶界偏聚。