Green-Light Static Rewritable Optical Storage Properties of a Novel CuTCNQ Derivative Thin Film

A novel charge-transfer complex film: copper-(n-propyl ester 7,7,8,8- tetracyanoquinodimethane-2,5-ylene-(3-propionic acid)) (Cu-TCNQ(C2H4 COOC3H7)2 ) was prepared by spin-coating. Absorption spectra, green-light (514.5nm) static rewritable optical recording properties and rewritable mechanism of this film were studied.The results show that there are two strong absorption peaks at 388nm and 675nm, which can be assigned to electronic transitions in anion radical TCNQ( C2H4 COOC3H7 )2^-. Green-fight optical storage experimental results of this film were as follows: write-in power was 9mW, pulse duration was 80ns; erasing power was 4mW, pulse duration was 500ns; the reflectivity contrast C ≥ 15%; number of write-erase cycles N ≥ 100. It is found that the realization of rewritable optical storage of the Cu-TCNQ(C2H4COOCsH7)2 film is related to the reversible changes of the optical properties, which is caused by the reversible charge transfer between copper and n-propyl ester 7, 7,8,8- tetracyanoquinodimethane-2,5-ylene-(3-propionic acid) in the complex through inducement of laser irradiation.     

GeSb_2Te_4相变光存储薄膜材料的短波长静态记录特性的研究

研究了单层ＧｅＳｂ２Ｔｅ４真空射频溅射薄膜在４００ｎｍ～８３０ｎｍ区域的吸收、反射光谱和光学常数（ｎ，ｋ），发现ＧｅＳｂ２Ｔｅ４薄膜在４００ｎｍ～６００ｎｍ波长范围内具有较强的吸收。在短波长静态测试仪上测试了ＧｅＳｂ２Ｔｅ４薄膜的光存储记录特性，发现在５１４．５ｎｍ波长用较低功率的激光辐照样品时薄膜在写入前后的反射率变化较大，擦除前后的反射率对比度较低，可通过膜层设计来提高     

用于蓝光存储的无机材料的研究及进展

光存储朝着高密度、大容量、高数据传输率方向发展。下一代的光盘记录将从目前广泛使用的红光波段向蓝光波段发展。本文综述了可用于蓝光记录的新一代超高密度光盘无机存储材料的研究现状和新进展。     

光聚物全息光盘记录方法和光路的优化

提出了适用于光聚物厚膜盘状高密度全息存储的角度空间复用相结合的存储方法。研究了光路设置对记录容量和密度的影响 ,分析和计算表明 :对全息光盘光聚物全息存储介质来说 ,新方法可以获得比空间角度复用存储方法高近一个数量级的存储容量和密度 ,当使用平面波做参考光、介质内参物光入射角度在 32°时是获得最大存储容量和密度的最佳设置 ;对 5 0 0 μm厚的光聚物介质 ,存储密度可达到 42bit/ μm2 ,用CD ROM同样大小的全息光盘 ,在其相同的有效记录面积上 ,其总容量可以达到 40 0Gbit,表明新方法是实用化光聚物盘状全息存储比较理想的方法。     

光致聚合物中单体及粘结剂对全息性能的影响

研究了单体及粘结剂等成份对全息光致聚合物薄膜光存储性能的影响。在相同引发条件下．以丙烯酰胺作为单体时，光聚物的衍射效率明显高于以丙烯酸和N羟甲基丙烯酰胺作为单体时光聚物的衍射效率。向丙烯酰胺中加入少量N-羟甲基丙烯酰胺，可以改善膜表面的光学质量．降低散射光强度，并提高膜的保存时间。在聚乙烯醇膜中单体聚合程度明显优于在聚乙烯吡咯烷酮中的程度，在大分子量的聚乙烯醇中的衍射效率及感光灵敏度高于在小分子量中的衍射效率和感光灵敏度，而且大分子量的聚乙烯醇能够制备厚膜，这是实现全息海量存储的一个重要因素。     

突破光学衍射极限,发展纳米光学和光子学

信息技术已经进入纳米时代,纳米光学和光子学正是为满足快速和高密度信息技术的需求而产生、发展的.先进的纳米光学和光子学器件应该是高速、高分辨率和高集成的,形成各类光学和光子学芯片和盘片.由于器件最小特征尺寸和加工分辨率受限于光的衍射极限,现有技术已接近实用化技术的理论极限并且成本很高,只有突破光学衍射极限才能进一步发展纳...     

Reversible Vertical Manipulations of Single Pt Adatom on Pt（111） Surface with a Triple-Apex Tip

With a triple-apex tip, we investigate theoretically the vertical manipulation of single Pt adatom on the Pt（111） surface. The adatom adsorbed on the f cc site of the flat Pt（111） surface can be transferred vertically to the tip by adjusting the tip height properly. Moreover, based on the strong vertical trapping ability and the relatively weak lateral trapping ability of the tip, we propose a simple method to realize a reversible vertical manipulation of the Pt adatom from the highly coordinated sites, the kink and the step sites, of the stepped Pt（111） surface. All the vertical manipulations are completed using only the atomic force between the tip and the adatom, without the electric field.     

超分辨近场结构中Bubble微结构的远场光学特性分析

以菲涅尔-基尔霍夫衍射理论为基础,建立了超分辨近场结构中Bubble微结构对高斯光束的衍射模型.分析了PtOx型超分辨近场结构(PtOx-Type-Super-RENS)中Bubble微结构的远场光学特性.结果表明,设计的Bubble微结构形成过程的简化模型可基本反映超分辨近场结构中掩膜结构在激光作用下的结构变化过程,说明了高斯衍射模型是研究薄膜微结构变化的一种有效方法.     

宽带光放大器用掺Er3+碲钨酸盐玻璃

制备了掺Er^3 的TeO2-WO3-ZnO-ZnF2(TWZOF)玻璃,测量了Er^3 在玻璃中的吸收光谱和970nm激光二极管激发下的荧光光谱和荧光寿命,分别采用J-O理论和McCumber理论计算了Er^3 离子的J-O强度参量Ωt(t=2,4,6)和其1．5μm发射的吸收截面和发射截面,研究了其荧光强度、荧光寿命和发射带宽与ZnF2含量的关系。结果表明,Er^3 在TWZOF玻璃中具有较大的1．5μm发射截面,其峰值发射截面为0．86pm^2;同时,Er^3 在TWZOF玻璃中具有很大的1．5μm发射带宽,所得半峰全宽在68～83nm之间;Er^3 在TWZOF玻璃中还具有较小的Ω2值和较大的Ω6值,且随ZnF2含量的增加,Ω2和Ω4均增大;Er^3 离子1．5μm发射峰值荧光强度和荧光寿命总体也随ZnF2含量的增加而增加。     

相变记录介质GaSb薄膜的光学性质、微观结构及其记录性质

本文系统地研究了热致相变对射频磁控溅射的GaSb薄膜光学性质和微观结构的影响.发现在270℃左右具有连续无序网络结构的非晶GaSb薄膜发生相变,转变为具有立方晶系的多晶薄膜,其晶格常数为α_0=0.6095nm,相变后薄膜的吸收减小,GaSb薄膜的光能隙由0.7eV升高为0.94eV.用精密四探针法测量了GaSb薄膜电阻随温度变化的过程.给出了GaSb薄膜的一次写入记录特性,研究了光致晶化记录畴的微结构.