平台石墨炉原子吸收法测定高温镍基合金中痕量碲

用镍作基体改进剂，碲的灵敏度提高的约２倍，灰化温度提高４００℃，抗干扰能力明显增强，不需要分离样品基体，采用平台石墨炉即可同温镍基金中痕量磅。方法检出限为０．０４１μｇ／ｇ，样品中碲含量为０．５μｇ／ｇ时，相对标准偏差为３－６％，回收率在９０－９９％之间，方法简单快速。     

非晶铁结构的加压模拟

本文用计算机模拟方法探讨了金属玻璃在加压过程中的变化。根据铁的状态方程拟合了Lennard-Jones双体势,用能显极小化方法松弛以得到具有周期性边界的含有1067个原子的非晶铁模型,并研究了加压状态下径向分布函数的变化。从第二峰中两个亚峰模糊化的趋势判断,加压可能破坏非晶合金中已经存在的局域有序关联。文中还估算了非晶铁的P-V曲线。 关键词：     

金属间化合物SbSn的化学合成及其对原油乳液的降黏研究

以化学法合成金属间化合物SbSn,采用XRD、DSC和XPS等手段对材料的体相、熔点和表层价电子态进行表征。将SbSn合金粉体负载于金属丝网上,考察在通电情况下两种W/O型原油乳液经循环处理后的黏度变化。结果表明,以Zn粉为还原剂所合成的产物SbSn,粒径分布为500nm-1000nm。随着循环处理时间的延长和电场电压的增大,两种乳液的黏度均明显下降。当电压为10.35V,处理20h后,W（10）/O（90）和W（20）/O（80）分别由原来的9000mPa.s和8500mPa.s下降到6000mPa.s和4500mPa.s。降黏的机理推测为,原油乳状液中的负极性有机物在电流的诱导下与SbSn的表层发生电化学反应。     

柠檬酸含量对LiFePO4/C复合正极材料形貌及电化学性能的影响

采用水热-高温煅烧法制备了具有不同形貌的LiFePO4/C复合材料,探讨了柠檬酸含量对其形貌和电化学性能的影响.结果表明,柠檬酸的添加对LiFePO4/C复合材料的形貌具有显著的影响.通过添加柠檬酸调控LiFePO4/C复合材料的形貌,可以极大地改善LiFePO4/C复合材料的电化学性能.当柠檬酸与LiFePO4的摩尔比为1∶2时,LiFePO4/C复合材料呈纳米片状,颗粒粒径最小,比表面积最大,在0.1C和5C时放电比容量为160.3mA·h·g1和130.9 mA·h·g-1.     

固态夸克星星震模型的研究

Glitch指脉冲星发生的自转角速度突然增大的现象,在许多脉冲星中都探测到了。Glitch的产生机制与脉冲星内部结构相关,而后者依然是待解决的难题。天文观测和理论研究均不能排除一类可能性,即脉冲星类天体本质上是固态夸克集团星,而固态星体发生Glitch的最自然的解释就是星震。本工作在星震模型下研究了固态脉冲星的Glitch现象。固态星体在自转减慢过程中,会发生应力能（或弹性能）的积累,当积累的应力超过星体能承受的限度,星体会发生碎裂,即发生星震,此时由于转动惯量突然减小而导致自转角速度突然增大,表现为Glitch现象。根据此模型可得到Glitch的幅度与时间间隔的关系。如果星体的质量较大而自转较慢,星震过程可能同时伴随体积的减小,即体积改变的星震,此时通常会有显著的引力能释放,可以解释观测到的反称X射线脉冲星/软伽马射线重复暴（AXPs/SGRs）;如果星体转速较快,星震过程可能只表现为形状即扁率的微小变化,此时不会有显著的能量释放。这两类Glitches可以解释观测现象。进一步的理论研究结合更多观测,有望使人们利用Glitch现象来检验固态夸克集团星这一理论猜想。The author demonstrates that how to understand the Glitches of solid pulsars in the starquake model. Glitch is the sudden spin-up during the normal spin-down process, which has been observed in many pulsars. The mechanism of Glitches is still a matter of debate because it depends on the unsolved problem that what is the nature of pulsars. One of the models of pulsars, the so-called solid quark-cluster stars, could not be ruled out by neither the astrophysics observations nor theoretical considerations. The Glitches of solid quarkcluster stars could naturally be the result of starqukes. During the spinning-down of the solid star, the strain energy develops until the stress reaches the critical value, then some parts of the star fragment, which would suddenly decrease the moment of inertia of the star, leading to the sudden increase of the rotation frequency that manifests as a Glitch. If the star has high mass or rotates slowly, the shrink of radius would happen during the starquake, leading to a huge amount of energy releasing which accounts for AXPs/SGRs. On the other hand, if the star rotates fast, only the oblateness of the star changes during the starquake, which would lead to negligible releasing of energy. This paper discusses the phenomenon of Glitches for solid quark-cluster stars, including the physical processes and consequences of starquakes, as well as the reasons for different energy releasing during Glitches. Further theoretical study combined with more observations about Glitches would be helpful for us to test the conjecture of sold quark-clusters.     

Ni-MoS2/γ-Al2O3催化剂的制备及其光催化性能研究

采用共沉淀结合水热合成方法,以γ-Al2O3为载体,制备出Ni-MoS2/γ-Al2O3复合催化剂.采用X射线粉末衍射仪(XRD)、扫描电子显微镜(SEM)等方法对样品的结构与形貌进行表征.研究了MoS2负载量、煅烧温度对Ni-MoS2/γ-Al2O3复合催化剂光催化降解罗丹明B性能的影响,并考察了催化剂的循环使用性能.结果表明:负载量为30wt;,煅烧温度为300℃的复合催化剂Ni-MoS2/γ-Al2O3表面的MoS2纳米片兼具有良好的结晶度和均匀分散性,其纳米片尺寸约为200nm.可见光下,Ni-MoS2/γ-Al2O3(MoS2 30wt;/Ni 5wt;)复合催化剂对罗丹明B的降解效率能达到100;,且循环使用5次后,对罗丹明B的降解效率仍能够达到88.9;.     

溶胶-凝胶法制备Ag掺杂的ZnO薄膜及其结构和光学性能的研究

溶胶-凝胶法制备了Ag掺杂的ZnO薄膜(AZO).采用X射线衍射(XRD)、扫描电子显微镜(SEM)、UV-VIS分光光度计、光致发光检测研究了掺杂浓度和退火温度对AZO薄膜光学和结构的影响.AZO薄膜呈(002)择优生 长的纤维锌矿六角形结构的多晶相.0.5;和1; Ag掺杂的薄膜在可见光波长区域光学透过率在70;～ 80;之间,随着Ag掺杂浓度的升高平均透过率有所降低.5; Ag掺杂的ZnO薄膜经空气中700℃退火后出现两条发射光谱带,经He气氛中退火后UV发射光谱显著增强,并且可见光发射光谱随之消失.     

二维空腔黏性流的格子Boltzmann方法模拟

用13速六方格子BhatnagarGrossKrook(缩写为BGK)模型模拟二维空腔黏性流.给出了上边界流体作匀速运动时,具有不同雷诺数的空腔黏性流的流场速度分布情况,模拟了在雷诺数Re=3000时,流场中的涡旋形成过程及流场稳定后,腔内密度、压力和温度的分布情况 关键词：     

软X射线辐照引起的铟锡氧化物表面光化学反应

利用XPS原位研究了Mg Kα X射线辐照对ITO表面的影响.结果表明,随着X射线辐射时间的延 长,表面辐照区域In,Sn相对含量增加,而O则逐渐减少,同时,In,Sn3d光电子峰随X射线 辐射的增强而变化.分析说明X射线的辐照导致了ITO表面光化学反应,氧的脱离使In,Sn有 被还原的趋势,受损较重的In明显存在亚氧化态.In,Sn俄歇参数的变化进一步证实ITO表面 发生了光化学反应.并讨论了X射线引起ITO表面光化学反应的机制. 关键词： X射线辐照 光电子能谱 光化学反应     

炸药爆轰合成纳米金刚石及其应用

本文简介通过高能炸药合成球形纳米金刚石的一些研究进展.X射线衍射谱显示,得到的纳米金刚石微晶为立方结构金刚石;晶粒尺寸为4～6nm,并有很大的微应力.高分辨率透射电镜观察表明,金刚石微晶在形成过程中经历了液态碳微滴聚结长大的过程.在这种材料的应用方面,本文报道了纳米金刚石用于提高化学气相生长金刚石薄膜的成核率:其出色的场发射性能用于电子显示材料,以及用于耐磨、减摩材料的若干试验成果.