Synthesis and light emitting properties of polyacetylenes having pendent fluorene groups

Five novel fluorene‐containing polymers, poly[(9,9‐dimethylfluoren‐2‐yl)acetylene] ( PFA1 ), poly[(1‐pentyl‐2‐(9,9‐dimethylfluoren‐2‐yl)acetylene) ( PFA2 ), poly[1‐decyl‐2‐(9,9‐dimethylfluoren‐2‐yl)acetylene] ( PFA3 ), poly[1‐phenyl‐2‐(9,9‐dimethylfluoren‐2‐yl)acetylene] ( PFA4 ), and poly[1‐(3,4‐difluorophenyl)‐2‐(9,9‐dimethylfluoren‐2‐yl)acetylene] ( PFA5 ) were synthesized by the polymerization of the corresponding fluorene‐substituted acetylenic monomers ( M1–M5), using WCl₆, MoCl_5, and TaCl₅ as catalysts and n‐Bu₄Sn as a cocatalyst. The synthesized polymers were thermally stable and readily soluble in common organic solvents. The degradation temperatures for a 5% weight loss of the polymers were ∼352–503 °C under nitrogen. PFA1–PFA5 show emission peaks from 402 to 590 nm. Besides, their electroluminescent properties were studied in heterostructure light‐emitting diodes (LEDs), using PFA2–PFA5 as an emitting layer. The PFA5 device revealed an orange‐red emission peak at 602 nm with a maximum luminescence of 923 cd/m² at 8 V. A device with the ITO/PEDOT/ a mixture of PFA2 (98 wt %) and PFA5 (2 wt %)/Ca/Al showed near white emission. Its maximum luminance and current efficiency are 450 cd/m² at 15 V and 1.3 cd/A, respectively. © 2005 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 44: 519–531, 2006     

Highly substituted poly(2,3‐diphenyl‐1,4‐phenylenevinylene) derivatives having bulky phenyl and fluorenyl pendant groups: Synthesis,characterization, and electro‐optical properties

Two series of poly(2,3‐diphenyl‐1,4‐phenylenevinylene) (DP‐PPV) derivatives containing multiple bulky substituents were synthesized. In the first series, two different groups were incorporated on C‐5,6 positions of the phenylene moiety to increase steric hindrance and to obtain blue‐shifted emissions. In the second series, bulky fluorenyl groups with two hexyl chains on the C‐9 position were introduced on two phenyl pendants to increase the solubility as well as steric hindrance to prevent close packing of the main chain. Polymers with high molecular weights and fine‐tuned electro‐optical properties were obtained by controlling the feed ratio of different monomers during polymerization. The maximum photoluminescent emissions of the thin films are located between 384 and 541 nm. Cyclic voltammetric analysis reveals that the band gaps of these light‐emitting materials are in the range from 2.4 to 3.3 eV. A double‐layer EL device with the configuration of ITO/PEDOT/P4/Ca/Al emitted pure green light with CIE′1931 at (0.24, 0.5). Using copolymer P6 as the emissive layer, the maximum luminescence and current efficiency were both improved when compared with the homopolymer P4. © 2006 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 44: 6738–6749, 2006     

Evaluation of piezoelectric PVDF polymers for use in space environments. III. Comparison of the effects of vacuum UV and gamma radiation

Films of piezoelectric PVDF and P(VDF‐TrFE) were exposed to vacuum UV (115–300 nm VUV) and γ‐radiation to investigate how these two forms of radiation affect the chemical, morphological, and piezoelectric properties of the polymers. The extent of crosslinking was almost identical in both polymers after γ‐irradiation, but surprisingly, was significantly higher for the TrFE copolymer after VUV‐irradiation. Changes in the melting behavior were also more significant in the TrFE copolymer after VUV‐irradiation due to both surface and bulk crosslinking, compared with only surface crosslinking for the PVDF films. The piezoelectric properties (measured using d₃₃ piezoelectric coefficients and D‐E hysteresis loops) were unchanged in the PVDF homopolymer, while the TrFE copolymer exhibited more narrow D‐E loops after exposure to either γ‐ or VUV‐radiation. The more severe damage to the TrFE copolymer in comparison with the PVDF homopolymer after VUV‐irradiation is explained by different energy deposition characteristics. The short wavelength, highly energetic photons are undoubtedly absorbed in the surface layers of both polymers, and we propose that while the longer wavelength components of the VUV‐radiation are absorbed by the bulk of the TrFE copolymer causing crosslinking, they are transmitted harmlessly in the PVDF homopolymer. © 2006 Wiley Periodicals, Inc. J Polym Sci Part B: Polym Phys 44: 3253–3264, 2006     

Study of ferromagnetism–superconductivity interactions in Co/Nb multilayers

We investigate Co/Nb multilayers to explore the spontaneous π-phase shift between the superconducting (SC) layers, which is attributed for causing the non-monotonic change of the SC transition temperature (T_c) with the ferromagnetic (FM) layer thickness (t_FM) in several FM/SC multilayered systems. The issue of interfacial roughness is also explored by growing Co/Nb multilayers at various sputtering pressures. Transport measurements show a non-monotonic dependence of T_c on t_FM, and this dependence is insensitive to the structural variation present in the samples, as measured by X-ray scattering.     

Hölder exponents and box dimension for self-affine fractal functions

We consider some self-affine fractal functions previously studied by Barnsleyet al. The graphs of these functions are invariant under certain affine scalings, and we extend their definition to allow the use of nonlinear scalings. The Hölder exponent,h, for these fractal functions is calculated and we show that there is a larger Hölder exponent,h , defined at almost every point (with respect to Lebesgue measure). For a class of such functions defined using linear affinities these exponents are related to the box dimensionD _B of the graph byh2–D _Bh .Communicated by Michael F. Barnsley.     

Synthesis of selenium-containing polyphenolic acid esters and evaluation of their effects on antioxidation and 5-lipoxygenase inhibition

Six novel selenium-containing polyphenolic acid esters were synthesized and evaluated as antioxidants and 5-lipoxygenase inhibitors. Synthesis of the title compounds involved the Mitsunobu reaction of polyphenolic acids with 2-phenylselenoethanol. Compounds and were found to be very effective antioxidants and 5-lipoxygenase inhibitors with activity comparable to or better than caffeic acid (3,4-dihydroxycinnamic acid) phenethyl ester (CAPE).