Synthesis and properties of zirconium-doped RbTiOPO<Subscript>4</Subscript> single crystals

Single crystals of the solid solutions RbTi_{1 ? x} Zr _x OPO₄ (0.015 < x < 0.034) were grown and their physical properties were studied. In the presence of zirconium in the crystals with the maximum content x = 0.034, the ferroelectric phase transition and the high-temperature transition from the orthorhombic to the cubic phase are shifted to lower temperatures by 100 and 50°C, respectively. In the temperature range from 700°C to room temperature, the conductivity of doped crystals decreases compared to that of the undoped crystals. It is of particular interest that the intensity of the second-harmonic generation of the doped crystals is substantially higher than that of RbTiOPO₄.     

Characteristics of the thermodynamic and kinetic properties of NbH0.83 in the phase transition region

Measurements were made of the specific heat (in the temperature range 80–400 K), electrical resistivity (4.2–300 K), thermo-emf (4.2–300 K), thermal conductivity (7–300 K), magnetic susceptibility (4.2–400 K), and lattice parameters (30–300 K) of the alloy NbH_0.83. The λ′→λβ phase transitions were studied. It was established that the structure of the niobium matrix of the hydride remains unchanged as a result of these transitions. It is shown that the β→λ phase transition (one-dimensional hydrogen ordering) is a three-stage one and is accompanied by a substantial change in the shear modulus of the hydride. The λ′ phase existing at T<110 K was determined. The electron thermal conductivity κ_el calculated for the λ′ phase in the range T<23 K is 25% higher than the measured thermal conductivity. In order to explain this fact and also the discontinuity in the concentration dependence of the coefficient of thermal expansion of NbHx for x?0.83–0.84 and the approximately 1.5% compression of the NbH_0.84 volume it is assumed that in the region of x _c in the λ′ phase the topology of the Fermi surface of the NbH_x interstitial alloy changes substantially.