以钛氧有机物为前驱物制备具有高光催化活性的纳米二氧化钛晶体

 纳米二氧化钛的制备方法及前驱物的差别影响其光催化活性．将20ml钛酸丁酯及30ml乙酐在密闭容器中与50ml环己烷混合，在70～85℃反应30min，生成微细的非晶钛氧有机物；经FT－IR和TGA分析，该物质被确认为计量式是TiOOOCCH3）2和TiO（OC4H9）（OOCCH3）的混合体．该钛氧有机物前驱物经焙烧后得到具有高光催化活性的纳米二氧化钛晶体．表征结果表明，钛氧有机物在焙烧过程中，其表面的吸附物及键合有机基团在400℃以前发生脱附和氧化分解；在389～405℃间形成锐钛矿型晶体，在600℃出现金红石晶型；600℃焙烧3h所得样品的比表面积为86m2／g，其二次粒子呈200～300nm条形体，孔隙大于20nm；单分散粒子为球形单晶，粒径为22nm；表面物理吸附水量为1．21％，加热至800℃时失重1．48％，粉体稳定纯净．光催化实验结果表明，以钛氧有机物为前驱物制备的纳米二氧化钛晶体具有高的光催化活性，光降解丁基罗丹明溶液的反应速率常数约为溶胶－凝胶法制备的催化剂样品的4倍．表面氧空缺和一定量的表面羟基可能是粉体具有高光催化活性的重要因素．     

Synthesis,spectral and magnetic studies of novel μ-oxamido heterotinuclear complexes

Summary Three novel heterotrinuclear complexes have been prepared, [Cu₂(oxdn)₂Zn](ClO₄)₂ (1) and [Cu₂(oxdn)₂-M(H₂O)₂](ClO₄)₂ with M=Mn (2) and Co (3) [oxdn-oxamidobis (propionato)], and characterized by spectral data. The temperature dependence of the magnetic susceptibilities of (2) and (3) has been studied in the 4–300K range, and the exchange integrals J=–20.90cm^–1 for (2) and J=–62.36cm^–1 for (3) calculated. These results are commensurate with antiferromagnetic interactions between the adjacent metal ions.     

甲烷氧化偶联催化反应的特征

应用程序升温反应（ＴＰＲ）及质谱分析表征了ＣａＯ，Ｓｍ２Ｏ３，０．５－１０％Ｓｍ／ＣａＯ催化剂上的甲烷氧化偶联反应特性。谱图分析表明，在４００－１０００℃范围内，甲烷氧化偶联反应产物的变化呈现三个反应温度区域：（１）完全氧化区，反应主要为ＣＨ３·在催化剂表面完全氧化形成ＣＯｘ和Ｈ２：（２）偶联区，主要为ＣＨ３·的氧化和偶联竞争反应，Ｈ２谱线出现明显的低温峰；（３）氧耗尽区，反应为高温气相反应，产物     

Electronic-to-vibrational energy transfer reactions.X* + CO (X = O,I and Br)

The vibrational distribution of CO produced from the following two electronic-to-vibrational energy transfer reactions:

have been determined by means of infrared resonance absorption measurements employing a cw CO laser. The CO molecules formed in both reactions were found to be vibrationally excited up to the limits of available electronic energies carried by the excited atoms. A similar result was also observed in the Br(4²P_{$\text{1}\text{2}$}) + CO reaction, in which absorption occurred only in the 1 → 2 band. For the O^* + CO reaction the efficiency of E → V energy transfer was determined to be 16%. Our present results were found to be inconsistent with the impulsive (half-collision) model.     

PEO-LiClO_4-ZSM5 composite polymer electrolyte (IV): Polarized optical microscopy study

All solid-state lithium polymer batteries may be one of the best choices for the future electrochemical power source, characterized by high energy densities, good cyclability, reliability and safety[1,2]. Owing to its potential capability to replace the t…     

Magnetically recoverable chiral catalysts immobilized on magnetite nanoparticles for asymmetric hydrogenation of aromatic ketones

Novel heterogenized asymmetric catalysts were synthesized by immobilizing preformed Ru catalysts on magnetite nanoparticles via the phosphonate functionality and were characterized by a variety of techniques, including TEM, magnetization, and XRD. These nanoparticle-supported chiral catalysts were used for enantioselective heterogeneous asymmetric hydrogenation of aromatic ketones with very high enantiomeric excess values of up to 98.0%. The immobilized catalysts were easily recycled by magnetic decantation and reused for up to 14 times without loss of activity and enantioselectivity. Orthogonal nature of the present catalyst immobilization approach should allow the design of other superparamagnetic nanoparticle-supported asymmetric catalysts for a wide range of organic transformations.     

ZrxTixAl1-2xO2的制备及其在三效催化剂上的应用

Zr_0.5Ti_0.5O₂(ZT) and Zr_0.25Ti_0.25Al_0.5O₂(ZTA) mixed oxides were prepared by co-precipitation method and characterized by low temperature adsorption-desorption， XRD and NH₃-TPD. The activity of Pt/Zr_0.5Ti_0.5O₂ and Pt/ Zr_0.5Ti_0.5Al_0.5O₂ catalysts was evaluated using the simulated gases. The results show that ZTA samples exhibit higher specific surface area， larger pore volume and proper surface acidic amount and acidity in comparison with ZT. The results of the catalytic test indicate that Pt/ZT and Pt/ZTA catalysts exhibit excellent low-temperature catalytic activity and lower light-off temperatures of hydrocarbon， carbon monoxide and nitrogen oxides， especially better conversion for nitrogen oxides (NO_x). The addition of Al₂O₃ into ZT enhanced the anti-aging property of Pt/ ZTA catalysts due to the excellent textural， structural， surface acidity and thermal stability.     

流动注射在线萃取-火焰原子吸收法测定食用盐中的锌

基于锌与 1 (2 吡啶偶氮 ) 2 萘酚 (简称PAN)形成的配合物可被氯仿萃取 ,从高盐基体样品中分离富集锌 ,利用自行设计的分相器 ,实验确定了最佳的流动注射在线萃取 火焰原子吸收光度法测定锌的流路系统和化学反应条件。在选定的工作条件下 ,其RSD和检出限分别为 4 3 % (c=0 6 μg/mL ,n =1 1 )和0 0 3 μg/mL ,测定速度为 2 5样 /h。用于实际样品的测定 ,加标回收率为 97%～1 0 6 %。     

第一性原理计算钛酸铅A位掺杂对其负热膨胀性的影响

近年来,实验发现钛酸铅基材料具有负热膨胀性,且其热膨胀程度会受到掺杂元素的影响. 目前所研究的A位掺杂体系中,仅Cd原子掺杂能使钛酸铅负热膨胀性增强. 所以研究A位掺杂钛酸铅,比较Cd原子与其他原子在掺杂钛酸铅时化学键的异同,有助于深刻理解钛酸铅负热膨胀的本质. 本文利用第一性原理,分别优化了Sr、Ba、Cd掺杂钛酸铅的晶格常数,计算了它们的态密度和电荷密度. 结果表明Cd―O键的共价性强于Pb―O键,而Ba―O键和Sr―O键几乎呈离子性,Ba/Sr对Pb的替代削弱了化合物的共价性,降低了自发极化强度. 与实验测量的热膨胀系数对比可以发现,A位原子与氧原子之间的共价性增强,化合物负热膨胀程度升高;若A位原子与氧原子之间的共价性削弱,负热膨胀程度降低. 可见A位原子与氧原子之间的共价性影响了钛酸铅基化合物负热膨胀性.     