Generation of highly stable amidate anion in anionic polymerization of 3‐(triethylsilyl)propyl isocyanate

To study living anionic polymerization, 3‐(triethylsilyl)propyl isocyanate (TEtSPI) monomer was synthesized by hydrosilylation of allylamine with triethylsilane and treatment of the resulting amine with triphosgene. The polymerization of TEtSPI was performed with sodium naphthalenide (Na‐Naph) as an initiator and in the absence and presence of sodium tetraphenylborate (NaBPh₄) as an additive in tetrahydrofuran (THF) at ?78 and at ?98 °C. A highly stabilized amidate anion for living polymerization of isocyanates was generated for the first time with the combined effect of the bulky substituent and the shielding action of the additive NaBPh₄, extending the living character at least up to 120 min at ?98 °C. Even the anion could exist at ?78 °C for 10 min. A block copolymer, poly(n‐hexyl isocyanate)‐b‐poly[(3‐triethylsilyl)propyl isocyanate]‐b‐poly(n‐hexyl isocyanate), was synthesized with quantitative yields and controlled molecular weights via living anionic polymerization in THF at ?78 °C for TEtSPI and ?98 °C for n‐hexyl isocyanate, respectively, with Na‐Naph with three times of NaBPh₄ as a common ion salt. © 2004 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 42: 933–940, 2004     

Intramolecular energy transferable (2,2‐diphenylvinyl)phenyl substituted poly(p‐phenylenevinylene) derivative with efficient photoluminescence and electroluminescence

A poly(p‐phenylenevinylene) (PPV) derivative containing a bulky (2,2‐diphenylvinyl)phenyl group in the side chain, EHDVP‐PPV, was synthesized by Gilch route. The reduced tolane‐bisbenzyl (TBB) defects, as well as the structure of the polymer, was confirmed by various spectroscopic methods. The intramolecular energy transfer from the (2,2‐diphenylvinyl)phenyl side group to the PPV backbone was studied by UV‐vis and photoluminescence (PL) of the obtained polymer and model compound. The polymer film showed maximum absorption and emission peaks at 454 and 546 nm, respectively, and high PL efficiency of 57%. A yellow electroluminescence (λ_max = 548 nm) was obtained with intensities of 6479 cd/m² when the light‐emitting diodes of ITO/PEDOT/EHDVP‐PPV/LiF/Al were fabricated. The maximum power efficiency of the devices was 0.729 lm/W with a turn‐on voltage of 3.6 V. © 2004 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 42: 5636–5646, 2004     

Thermal behavior of metallodendrimers possessing bis(terpyridinyl)Ru(II) connectivity and different surface functionality

A series of metallodendrimers, assembled by means of bis(terpyridinyl)Ru^(II) connectivity on poly(propylene imine) dendrimer scaffolds, with homogeneous or heterogeneous surfaces, were prepared. Differential scanning calorimetry and thermogravimetric analysis were used to determine their thermal behavior, glass‐transition temperatures, and the decomposition kinetics and temperatures; no synergy effects for these properties were observed for the heterogeneously surfaced constructs in contrast to the corresponding homogeneously coated materials, which exhibited different values depending on their surface functionalities. © 2004 Wiley Periodicals, Inc. J Polym Sci Part B: Polym Phys 42: 1487–1495, 2004     

Ferritin immunosensing on microfabricated electrodes based on the integration of immunoprecipitation and electrochemical signaling reactions.

A signal registration strategy from micropatterned immunosensors that converts antigen-antibody binding reactions into electrochemical signals was demonstrated. An array-type micropatterned gold electrode on a silicon wafer was fabricated, containing two electrode geometries of rectangular (100 microm x 500 microm) and circular (r. 50 microm) types, exhibiting electrochemical characteristics of bulk and micro-electrodes, respectively. Ferritin was employed as a model analyte for immunosensing because it has an advantageous molecular structure for functionalization to the sensing interface, and is regarded as a general marker protein for tumors and cancer recurrence. With the fabricated and ferritin-functionalized immunosensors, biospecific interactions were performed with antiferritin antiserum and secondary antibody samples, followed by electrochemical signaling via an immunoprecipitation reaction by the label enzyme. Under the optimized affinity-surface construction steps and reaction conditions, both types of microfabricated electrodes exhibited well-defined calibration results as a function of the protein concentration in antiserum samples. Furthermore, circular-type micropatterned immunoelectrodes exhibited voltammetric characteristics of microelectrodes, which is advantageous in terms of sensor operation under a fixed potential and low signal drift during the signaling reaction compared with the bulk-type electrodes. The results support that the employed signaling method with the proposed immunosensor configuration is fit for sensor miniaturization and integration to future biomicrosystems.     

Photoswitching of holographic polymer-dispersed liquid crystals doped with chiral dopant

Chiral dopants were added to the formulation of holographic polymer-dispersed liquid crystals and the effects studied in terms of grating formation dynamics, morphology, diffraction efficiency, contrast ratio and electro-optical properties of the films. A gradual increase of real-time diffraction efficiency, decrease of droplet size and increase of diffraction efficiency of the composite film were obtained with the addition and increasing content of chiral dopant, due to the increased viscosity of the liquid crystal (LC) doped with the chiral dopant leading to decreased droplet coalescence. The contrast ratio decreased with increasing content of chiral dopant due to the difficult orientation of LC molecules caused by the formation of a helical structure. Addition of a small amount of the chiral dopant increased the driving voltage slightly, whereas the decay time is decreased significantly as a result of the high twisting of the helical structure.     

Cellulose dimethylphenylcarbamate-bonded carbon-clad zirconia for chiral separation in high performance liquid chromatography.

Porous zirconia particles are very robust material and have received considerable attention as a stationary phase support for HPLC. We prepared cellulose dimethylphenylcarbamate-bonded carbon-clad zirconia (CDMPCCZ) as a chiral stationary phase (CSP) for separation of enantiomers of a set of 14 racemic compounds in normal phase (NP) and reversed-phase (RP) liquid chromatography. Retention and enantioselectivity on CDMPCCZ were compared to those on CDMPC-coated zirconia (CDMPCZ) to see how the change in immobilization method of the chiral selector affects the retention and chiral selectivity. In NPLC, retention was longer and the number of resolved racemates was smaller on CDMPCCZ than on CDMPCZ. However, chiral selectivity factors for some resolved racemates were better on CDMPCCZ than on CDMPCZ. The longer retention on CDMPCCZ is likely due to strong, non-chiral discriminating interactions with the carbon layer on CDMPCZ. In RPLC only two racemates were resolved on CDMPCCZ, but retention times were shorter than, and resolutions were comparable to, those in NPLC, indicating a potential for improving chromatographic performance of the CDMPCCZ column in RPLC with optimized column preparation and separation conditions.     

Synthesis and adsorption properties of gold nanoparticles within pores of surface‐functional porous polymer microspheres

Mesoporous polymer microspheres with gold (Au) nanoparticles inside their pores were prepared considering their surface functionality and porosity. The Au/polymer composite microspheres prepared were characterized by transmission electron microscope (TEM), X‐ray diffraction (XRD), and Brunauer–Emmett–Teller (BET) techniques. The results showed that the adsorption of Au nanoparticles could be increased by imparting the pore structure and surface‐functional groups into the supporting polymer microspheres (in this study, poly (ethylene glycol dimethacrylate‐co‐acrylonitrile) and poly (EGDMA‐co‐AN) system). Above all, from this study, it was established that the porosity of the polymer microspheres is the most important factor that determines the distribution and adsorption amount of face‐centered cubic (fcc) Au nanoparticles in the final products. Our study showed that the continuous adsorption of Au nanoparticles with the aid of the large surface area and surface interaction sites formed more favorably the Au/polymer composite microspheres. The BET measurements of Au/poly(EGDMA‐co‐AN) composite microspheres reveals that the adsorption of Au nanoparticles into the pores kept the pore structure intact and made it more porous. © 2004 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 42: 5627–5635, 2004     

Singlewall carbon nanotubes covered with polystyrene nanoparticles by in‐situ miniemulsion polymerization

This work is to make carbon nanotubes dispersible in both water and organic solvents without oxidation and cutting nanotube threads. Polystyrene‐singlewall carbon nanotube (PS‐SWNT) composites were prepared with three different methods: miniemulsion polymerization, conventional emulsion polymerization, and mixing SWNT with PS latex. The two factors, crosslinking and surface coverage of PS are important factors for the mechanical and electrical properties, including dispersion states of SWNT in various solvents. The PS‐SWNT composite prepared via a conventional emulsion polymerization showed SWNT bundles entirely covered with PS, whereas the PS‐SWNT composite prepared via a miniemulsion polymerization showed SWNT partially covered with crosslinked PS nanoparticles. The method of mixing SWNTs with PS latex did not show the well dispersed state of carbon nanotubes because PS was not crosslinked and was dissolved in a solvent, and nanotubes separated from PS precipitated. So the PS nanoparticle‐SWNT composite had lower electrical resistance, and higher mechanical strength than the other composites made by the latter two methods. As the amount of SWNT increases, the bare surface area of SWNT increases and the electrical conductivity increases in the composite made by the miniemulsion polymerization. © 2005 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 44: 573–584, 2006     

Synthesis and characterization of novel perfluorinated polyimides with 3D‐controlled structures for photonic applications

We have designed and synthesized novel perfluorinated polyimides with 3D controlled structure. At first, we successfully developed the new synthetic routes to diamines with pendant bulky perfluorinated aromatic units in a multi‐step synthetic procedure. Novel perfluorinated polyimides were prepared in a two‐step reaction in N‐methyl‐2‐pyrrolidinone (NMP) solution: The first step was for the synthesis of polyamic acids (PAAs) and the second reaction was for the imidization of PAA. The polymer yield was over 89% and the inherent viscosity of PAAs was in the range of 0.24–0.36 dL/g. The thin films were prepared by spin‐coating the PAA solution in NMP onto various substrates such as a Si wafer or a KBr pellet, dried at 80 °C and further cured at 230 °C. The resultant polyimides are thermally stable over 400 °C. The refractive index and birefringence of the resultant polyimides are 1.5858–1.6452 and 0.01–0.005, respectively. The refractive index of polyimide decreases with increasing the fluorine content. The copolymerization and the ether linkages into the backbone reduce the birefringence of polyimides. Surprisingly, the pendant ether linkage is not a crucial factor in reducing the polyimide birefringence. Their birefringence is comparatively very low, compared with that of previous polyimides. © 2005 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 44: 1326–1342, 2006