In situ Study of Scanning Tunneling Microscopy On Passivation and Pit Corrosion of Stainless Steel

Traditional ways to investigate passivation and pitting is indirect electrochemical method.In this article, direct information for topography of ultrathin passivating film is obtained by employing in-situ ECSTM to stainless steel (Cr11Ni13 SS). Passivating potentials including 0V,0.2V, 0.5V and 0.8V (Vs.SCE) are applied to the sample in 0.5M H₂SO₄+0.02M NaCl respectively, while surface topography is recorded by STM on the same region, with dimension of 800×800 nanometers. ECSTM result provides a microscopic explanation of EIS. The result describes as fig. 1 and fig. 2.     

Study on the Corrosion Resistance of 304L Stainless Steel

304L is an austenitic stainless steel with very low carbon content, and is served as the application to the oxidizing media, however, its corrosion resistance is not satisfactory in reducing media. For example, the pitting corrosion occurred on 304L stainless steel tube, which had been mounted for one year, somewhere at the power station in die seashore of China. For this reason we have studied the corrosion behavior of 304L in some media and invented a novel surface treatment technique of stainless steel for extremely improving the corrosion resistance of 304L. The characteristics of the modified passive film on the steel were examined in this paper, and the corrosion resistance of treated 304L stainless steel was tested in our laboratory and the testing ground. The results are satisfactory.     

缓蚀剂对铜作用的激光扫描微区光电化学研究

采用激光扫描微区光电化学显微技术(PEM)对不同浓度下的苯并三氮唑(BTA)及其衍生物4-羧基苯并三唑甲酯与5-羧基苯并三唑甲酯的混合物(CBTME)在硼砂缓冲溶液(pH9.2)中对铜电极的缓蚀作用作了比较研究。研究发现当电位正向扫描至某一电位时,一定浓度的BTA或CBTME作用下,铜电极光响应由p-型转化为n-型,并可依此判断缓蚀剂的缓蚀性能,n-型光响应越大,缓蚀剂的缓蚀性能越好,与循环伏安光电流及交流阻抗测试的结果相一致;实验还发现,影响缓蚀剂对铜作用的过程不仅与缓蚀剂本身有关,还与电极电位有关。在一定的电位与一定的缓蚀剂浓度下可观察到铜电极表面共存着p-型和n-型区域及p转n的过程,因此可从微观上观察到缓蚀剂与铜表面作用的过程,为缓蚀剂的应用建立了良好的理论基础。     

多孔Ni在熔融碳酸盐中原位氧化/锂化时形变及溶解行为的研究

进一步研究在加载及无加载条件下多孔Ni电极在熔融盐中进行原位氧化/锂化时,电极厚度随时间的变化.应用SEM表征不同运行时间后多孔Ni样品的表面形态,用原子吸收光谱(AAS)测定熔盐中溶解的镍离子浓度.结果表明,负载条件下多孔镍在融盐中原位氧化/锂化时,镍离子溶出现象严重,即使无负载条件下,多孔镍在进行原位氧化/锂化过程中,仍有相当量的镍离子溶出并进入熔融碳酸盐电解质中.     

Equation of State of Spin-Polarized Neutron Metier

Within the spin-dependent Brueckner-Hatree-Fock framework, the equation of state of the spin-polarized neutron matter has been investigated by adopting the realistic nucleon-nucleon interaction AV₁₈ supplemented with a microscopic three-body force. The related physical quantities such as spin-symmetry energy, magnetic susceptibility and the Landau parameter G₀ in spin channel, have been extracted. The three-body force effects have been studied and discussed with a special attention. It is shown that in the whole range of spin-polarization, the energy per particle of spin-polarized neutron matter fulfills a quadratic relation versus the spin-polarization parameter δ= (p-p )/p . The predicted spin-symmetry energy is positive in the density region up to ρ = 0.8fm^-3 and increase monotonically as increasing density so that no any evidence is found for a spontaneous transition to a ferromagnetic state in neutron matter. The three-body force effect is to strongly increase the spin-symmetry energy and reduce the magnetic susceptibility at high densities, as a consequence , to make neutron matter become more stable against spin fluctuation. The obtained Landau parameter G₀ and its density dependence may serve as a constraint on the spin-spin parts of the phenomenological Skyrme and Skyrme-like interactions .     

不锈钢钝化膜耐蚀性与半导体特性的关联研究

通过极化曲线、交流阻抗谱和钝化膜半导体特性等电化学测量，研究了经电化学阳极氧化处理的不锈钢钝化膜在0.5 mol•L^-1 NaCl溶液中耐蚀性能与其半导体特性的关系，进一步探索电化学改性处理不锈钢钝化膜的耐蚀机理. 结果表明，不锈钢钝化膜在负于平带电位范围表现为p型半导体，在高于平带电位范围表现为n型半导体，这主要与组成钝化膜的Fe和Cr氧化物半导体性质有关. 与自然条件下形成的不锈钢钝化膜比较，发现经过电化学阳极氧化后不锈钢钝化膜具有较低的施主与受主浓度，平带电位负移，说明阴离子在钝化膜表面发生吸附. 低的施主与受主浓度及钝化膜表面负电荷的增强，可有效排斥侵蚀性Cl^－在钝化膜表面的特性吸附，有利于提高不锈钢的耐局部腐蚀性能.     

纳米TiO2混晶的形成及其对光催化性能的影响

用溶胶-凝胶法通过改变晶型调节剂2-甲基-2,4戊二醇的添加量制备了金红石相和锐钛矿相比例不同的纳米TiO2混晶.以膨胀珍珠岩为载体,制备珍珠岩负载纳米TiO2混晶催化剂,以X射线衍射(XRD)、紫外-可见吸收光谱(UV-visiblespectrum)、BET、Raman光谱等方法对纳米TiO2混晶和负载型纳米TiO2催化剂进行表征和性能测定,研究了催化剂的混晶效应对光催化降解甲基橙催化性能的影响.结果表明:晶型调节剂的含量及制备条件对混晶中金红石和锐钛矿相TiO2的比率有较大的影响.对于负载型纳米TiO2催化剂,混晶比影响催化剂的光催化降解效率,当混晶比为6.1时光催化效率最高,这一结果对光催化剂的制备和应用都具有重要的意义.     

CuO-ZnO-ZrO2催化甲醇水蒸汽重整反应机理和中间态

应用质谱在线技术,对CuO-ZnO-ZrO2催化甲醇水蒸汽重整（SRM）反应进行程序升温脱附（TPD）和程序升温表面反应（TPSR）研究.结果表明:在反应态催化剂表面,甲醇以分子吸附态形式存在,甲醇水蒸汽重整反应经历甲酸根中间物种.分别用CuO、CuO-ZnO、CuO-ZnO-ZrO2作催化剂,甲醇在气流中的摩尔分数分别高于5.4％、0.37％和0.17％时,甲酸根中间态的分解产物为CO2和H2;而甲醇在气流中的摩尔分数分别低于5.4％、0.37％和0.17％时,甲酸根中间态的分解产物为CO、CO2和H2.     

Al 2024-T3合金局部腐蚀的扫描微电极研究

应用扫描微电极技术和扫描电子显微镜技术研究Al 2024 T3合金在NaCl溶液中开路状态下的局部腐蚀发生的早期过程.实验表明,当Al合金浸入NaCl溶液,其表面即刻发生局部微点腐蚀,这些微点腐蚀与合金表面第二相颗粒密切相关,Al合金表面第二相Al2CuMg颗粒可表现为三种不同的腐蚀行为.     

覆铜板在NaCl溶液中的腐蚀电化学行为

应用线性极化、循环伏安(CV)及电化学阻抗谱(EIS)等电化学方法对覆铜板(CCL)和纯铜的腐蚀电化学行为进行了研究和比较. 结果表明, 覆铜板的耐蚀性弱于纯铜, 其阳极溶解过程与纯铜有所不同; 在较低电位下, CCL 以铜的氯化络合物的形式溶解, CuCl-2的扩散为该过程的控制步骤; 随着电位的升高, 腐蚀产物CuCl在电极表面形成疏松多孔的膜, Cl-在膜中的传输成为溶解过程的控制步骤. 电极表面CuCl 膜的消长过程是产生感抗弧的主要原因.